Preparation method of preserved plywood

A technology for plywood and anti-corrosion veneer, applied in the field of plywood, can solve the problems of environmental safety and personal health that affect environmental protection characteristics and other problems, and achieve the effects of excellent impregnation effect, good termites and decay bacteria, and improved corrosion resistance.

Inactive Publication Date: 2015-07-08
宁都鑫腾木业有限公司
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] There are many kinds of chemical agents for preservative treatment of plywood, but the use of various traditional wood preservatives (such as chromium-added copper

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0018] Example l

[0019] Wood section peeling, veneer drying, veneer cutting to obtain the veneer of the prepared plywood, and then the veneer is treated as follows:

[0020] (1) Prepare antiseptic solution: prepare antiseptic solution at a molar ratio of furfuryl alcohol and ammonium borate of 1:2;

[0021] (2) Anticorrosive solution treatment veneer: Put the veneer into a vacuum pressurizing tank, connect the vacuum equipment and pressurizing equipment (that is, turn off the pressure pump when starting the vacuum pump to vacuum; turn off the vacuum pump when turning on the pressure pump), and turn it on The vacuum pump performs vacuum processing to make the relative vacuum in the vacuum pressurized tank reach -0.08 MPa. After holding for 50 minutes, turn off the vacuum pump and introduce the configured anticorrosive solution until the relative vacuum in the vacuum pressurized tank is 1Mpa, open The pressure pump continues to feed the anticorrosive solution into the vacuum pressur...

Example Embodiment

[0025] Example 2

[0026] Wood section peeling, veneer drying, veneer cutting to obtain the veneer of the prepared plywood, and then the veneer is treated as follows:

[0027] (1) Configure antiseptic solution: mix furfuryl alcohol and ammonium borate at a molar ratio of 1:2.3 to configure antiseptic solution;

[0028] (2) Anticorrosive solution treatment veneer: Put the veneer into a vacuum pressurizing tank, connect the vacuum equipment and pressurizing equipment (that is, turn off the pressure pump when starting the vacuum pump to vacuum; turn off the vacuum pump when turning on the pressure pump), and turn it on The vacuum pump performs vacuum processing to make the relative vacuum in the vacuum pressurized tank reach -0.085MPa. After holding for 55 minutes, close the vacuum pump and introduce the configured anticorrosive solution until the relative vacuum in the vacuum pressurized tank is 1.5Mpa. Turn on the pressure pump, continue to pass the anticorrosive solution into the va...

Example Embodiment

[0032] Example 3

[0033] Wood section peeling, veneer drying, veneer cutting to obtain the veneer of the prepared plywood, and then the veneer is treated as follows:

[0034] (1) Configure antiseptic solution: mix furfuryl alcohol and ammonium borate at a molar ratio of 1:2.8 to configure antiseptic solution;

[0035] (2) Anticorrosive solution treatment veneer: Put the veneer into a vacuum pressurizing tank, connect the vacuum equipment and pressurizing equipment (that is, turn off the pressure pump when starting the vacuum pump to vacuum; turn off the vacuum pump when turning on the pressure pump), and turn it on The vacuum pump performs vacuum processing to make the relative vacuum in the vacuum pressurized tank reach -0.09MPa. After holding for 60 minutes, the vacuum pump is turned off, and the configured anticorrosive solution is introduced at the same time until the relative vacuum in the vacuum pressurized tank is 2.0Mpa. Turn on the pressure pump, continue to pass the antic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a preparation method of preserved plywood. The method is that a special mixed preserving solution is adopted to perform preserving soaking treatment for a single board in a vacuum state; the single board is processed by pressure reduction vacuum pumping treatment in order to fully absorb a preservative; then the single board is pressurized so that the preservative can fully permeate the board. The preserved plywood prepared by the method has the advantages that the loss rate of boron in the single board is small; the effects on resisting termite and rot fungi are improved; the preserving performance is greatly improved; the preserving effect is obviously increased; the service life of the preserved plywood is prolonged.

Description

technical field [0001] The invention relates to a plywood, in particular to a preparation method of an anti-corrosion plywood. Background technique [0002] my country's timber industry is in the process of transforming from using mainly natural forest timber to mainly utilizing plantation forest timber. Plantation forest fast-growing small timber will be the main timber raw material in my country in the future. However, fast-growing wood in artificial forests is prone to decay, insects, and mildew. Therefore, wood protection will play a role in prolonging the life of wood and reducing the waste caused by downgrading, downgrading, and discarding wood due to decay and insects. It plays the role of improving the quality of wood products and increasing the functions of wood products. Reduce the loss and waste of wood due to rot and other reasons, prolong the service life of wood products, reduce the demand for wood resources in related industries (including wood, furniture, co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B27D1/08B32B37/12B32B37/10B32B37/06C09J161/24C09J11/04C08G12/12
CPCB27D1/08B32B21/13B32B2307/7145B32B2307/752B32B2439/00B32B2479/00B32B2605/00B32B2605/12C08G12/12C08K3/38C08K2003/387C09J11/04C09J161/24
Inventor 蒙献芳马庆丘秋燕李珠肖彭鸿贰苏燕何晓荣苏文雪
Owner 宁都鑫腾木业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap