A preparation method of vascular tissue engineering scaffold material loaded with pravastatin sodium
A technology of pravastatin sodium and scaffold material, which is applied in the field of preparation of vascular tissue engineering scaffold materials loaded with pravastatin sodium, can solve the problems of non-degradable, only 1 to 7 days, non-degradable, etc., and achieves prevention and treatment. Efficacy of recurrence, avoidance of acidic environment, and reduction of surgical complications
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0027] 1. Preparation of scaffold materials for vascular tissue engineering
[0028] (1) Preparation of pravastatin-loaded chitosan microspheres
[0029] (1.1) Mix Tween-80 and liquid paraffin according to the volume ratio of Tween-80: liquid paraffin = 2: 100, and mix evenly under electric stirring at a speed of 500 r / min to obtain an oil phase;
[0030] (1.2) join the chitosan that viscosity is lower than 200mPa.s in the acetic acid solution that volume concentration is 1%, magnetically stir 1h, be made into the chitosan solution that mass concentration is 1.5%; Dissolve pravastatin sodium in In the water, make the concentration of pravastatin sodium in water be 66.6g / L, obtain the pravastatin sodium aqueous solution; Then, mix the chitosan solution prepared with the pravastatin sodium aqueous solution, stir, and obtain the mass ratio Be the aqueous phase of pravastatin sodium: chitosan=1:1;
[0031] (1.3) Dissolving genipin in 30% ethanol aqueous solution, so that the con...
Embodiment 2
[0046] 1. Preparation of scaffold materials for vascular tissue engineering
[0047] (1) Preparation of pravastatin-loaded chitosan microspheres
[0048] (1.1) Mix span-80 and ethyl benzoate according to the volume ratio of span-80: ethyl benzoate = 8: 100, and mix evenly under electric stirring at a speed of 1000r / min to obtain an oil phase;
[0049] (1.2) Adding chitosan with a viscosity of 200 to 400mPa.s into an acetic acid solution with a volume concentration of 0.5%, magnetic stirring for 5h, and preparing a chitosan solution with a mass concentration of 3%; dissolving pravastatin sodium In water, make the concentration of pravastatin sodium in water be 16.6g / L, obtain pravastatin sodium aqueous solution; Then, mix the prepared chitosan solution and pravastatin sodium aqueous solution, stir well, make the Ratio is the aqueous phase of pravastatin sodium: chitosan=1:4;
[0050] (1.3) Genipin is dissolved in 40% aqueous ethanol, so that the concentration of genipin in 40...
Embodiment 3
[0062] 1. Preparation of scaffold materials for vascular tissue engineering
[0063] (1) Preparation of pravastatin-loaded chitosan microspheres
[0064] (1.1) Mix span-80 and liquid paraffin according to the volume ratio of span-80: liquid paraffin = 4: 100, and mix evenly under electric stirring at a speed of 850r / min to obtain an oil phase;
[0065] (1.2) Adding chitosan with a viscosity of 200 to 400mPa.s into an acetic acid solution with a volume concentration of 1%, magnetic stirring for 1h, and preparing a chitosan solution with a mass concentration of 1.5%; dissolving pravastatin sodium In water, make the concentration of pravastatin sodium in water be 33.3g / L, obtain pravastatin sodium aqueous solution; Ratio is the aqueous phase of pravastatin sodium: chitosan=1:2;
[0066] (1.3) Genipin is dissolved in 90% aqueous ethanol, so that the concentration of genipin in ethanol with a volume concentration of 90% is 13g / L to obtain a crosslinking agent solution;
[0067] ...
PUM
Property | Measurement | Unit |
---|---|---|
pore size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com