Polytrimethylene terephthalate enhanced composition

A technology of polytrimethylene terephthalate and a composition, which is applied in the field of polytrimethylene terephthalate reinforced composition, can solve the problems of easy aging, poor heat resistance, low strength, etc., and achieves good practical value and Promote the prospect, improve the application effect and the effect of the application field

Inactive Publication Date: 2015-08-26
QINGDAO XINZHAN PLASTIC
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Polytrimethylene terephthalate (PTT), as a new type of polyester polymer material with excellent comprehensive properties, has been widely used in the fields of fibers, films, engineering plastics, etc. Problems such as poor thermal performance and easy aging limit its application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A poly(trimethylene terephthalate) reinforced composition, the components of which are proportioned by mass percentage: PTT 70%, inorganic filler 20%, acrylate core-shell copolymer 8%, benzotriazole ultraviolet absorber 0.5%, nucleating agent 0.1%, aluminum-titanium composite coupling agent 0.5%, antioxidant 0.2%, pentaerythritol stearate 0.7%, the PTT is polyethylene terephthalic acid with an intrinsic viscosity of 0.7-1.2dL / g Propylene glycol ester, the inorganic filler is wollastonite with an average length of 10-500 μm, an average diameter of 3-30 μm, and an aspect ratio of 3-100, and the nucleating agent is nano-talcum powder and benzene with a mass ratio of 8:1:1 A compound of sodium formate and polyethylene glycol, the antioxidant is a compound of hindered phenolic antioxidant 1010 and phosphite antioxidant 168 at a mass ratio of 1:1.

[0022] Preparation method: (1), put PTT in a forced air circulation oven, dry at 110°C-120°C for about 6-8 hours, and wait for u...

Embodiment 2

[0024] A poly(trimethylene terephthalate) reinforced composition, the components of which are proportioned by mass percentage: PTT 81%, inorganic filler 10%, acrylate core-shell copolymer 6%, benzophenone ultraviolet absorber 2%, nucleating agent 0.2%, aluminum-titanium composite coupling agent 0.2%, antioxidant 0.1%, pentaerythritol stearate 0.5%, the PTT is polyethylene terephthalic acid with an intrinsic viscosity of 0.7-1.2dL / g Propylene glycol ester, the inorganic filler is wollastonite with an average length of 10-500 μm, an average diameter of 3-30 μm, and an aspect ratio of 3-100, and the nucleating agent is nano-talcum powder and benzene with a mass ratio of 8:1:1 A compound of sodium formate and polyethylene glycol, the antioxidant is a compound of hindered phenolic antioxidant 1076 and phosphite antioxidant 168 at a mass ratio of 1:1.

[0025] Preparation method: (1), put PTT in a forced air circulation oven, dry at 110°C-120°C for about 6-8 hours, and wait for use;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
aspect ratioaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polytrimethylene terephthalate enhanced composition. The enhanced composition comprises the following ingredients, by weight, 70%-90% of PTT, 5%-20% of inorganic filling material, 3%-8% of flexibilizers, 0.5%-2% of ultraviolet ray stabilizing agents, 0.1%-0.5% of nucleating agents, 0.1%-0.5% of coupling agents, 0.1%-0.5% of anti-oxidants and 0.1%-1% of lubricants. The inorganic filling material is wollastonite with an average length of 10-500 micrometers, with an average diameter of 3-30 micrometers and with a length / diameter of 3-100. The beneficial effects are that the composition has excellent enhancement, toughening and aging resistant effects, application effects of polytrimethylene terephthalate are raised, application fields of of polytrimethylene terephthalate are widened, and therefore the enhanced composition has good practical values and popularization prospects.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a reinforced poly(trimethylene terephthalate) composition. Background technique [0002] Polytrimethylene terephthalate (PTT), as a new type of polyester polymer material with excellent comprehensive properties, has been widely used in the fields of fibers, films, engineering plastics, etc. Problems such as poor thermal performance and easy aging limit its application. Contents of the invention [0003] The purpose of the present invention is to provide a poly(trimethylene terephthalate) reinforced composition with good mechanical properties, strong aging resistance and good molding. [0004] The technical solution adopted by the present invention to solve the technical problem is: poly(trimethylene terephthalate) reinforced composition, and its components are proportioned by mass percentage: PTT 70%-90%, inorganic filler 5%-20%, Toughening agent 3%~8%, UV stabilize...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08K13/06C08K9/00C08K7/10C08K3/34C08K5/098B29B9/06B29C47/92B29C48/92
Inventor 不公告发明人
Owner QINGDAO XINZHAN PLASTIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com