A kind of anti-fog film material and preparation method thereof

A thin-film material and anti-fog technology, applied in the direction of coating, etc., can solve the problems affecting the light transmittance of the film, danger, fogging, etc., and achieve the effects of simple preparation method, good film-forming property, and convenient material acquisition

Active Publication Date: 2017-10-31
YANCHENG FENGYING PLASTIC PROD CO LTD
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, during driving, due to the difference between the specific heat of the glass and the specific heat of the air, fogging often occurs, which seriously affects the sight of the driver and passengers.
At the same time, the existing car defogging is mainly through blowing and heating. After the fog appears, it needs to be dealt with in time, otherwise it will affect the driver's sight and bring potential danger.
[0004] In Chinese patent CN200920243860.2, an electric heating screen is placed in the middle of the film interlayer to achieve the anti-fog effect of the anti-fog glass film. The anti-fog effect of the anti-fog glass film is obvious, but it will affect the light transmission of the film and cause accidents. happened

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anti-fog film material and preparation method thereof
  • A kind of anti-fog film material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] (1) 68kg of ethyl acetate, 8kg of cellulose acetate butyrate, 0.5kg of benzoyl peroxide, 0.5kg of copper sulfate pentahydrate, 0.1kg of sodium zirconate, and 0.02kg of cobalt oxide were stirred evenly;

[0023] (2) Add in a high-pressure homogenizer with a pressure of 11Mpa and a temperature of 75°C, mix for 12 minutes, add 0.02kg of boron trifluoride-dimethylaniline, stir for 10 minutes at 75°C under nitrogen, degas, pour In a flat mold, dry in an oven at 60° C. for 4 hours, and demold to obtain an anti-fog film material.

Embodiment 2

[0025] (1) 68kg of ethyl acetate, 11kg of cellulose acetate butyrate, 0.5kg of benzoyl peroxide, 0.5kg of copper sulfate pentahydrate, 0.1kg of sodium zirconate, and 0.02kg of cobalt oxide were stirred evenly;

[0026] (2) Add in a high-pressure homogenizer with a pressure of 11Mpa and a temperature of 75°C, mix for 12 minutes, add 0.02kg of boron trifluoride-dimethylaniline, stir for 10 minutes at 75°C under nitrogen, degas, pour In a flat mold, dry in an oven at 60° C. for 4 hours, and demold to obtain an anti-fog film material.

Embodiment 3

[0028] (1) 85kg of ethyl acetate, 11kg of cellulose acetate butyrate, 2kg of benzoyl peroxide, 1.5kg of copper sulfate pentahydrate, 0.4kg of sodium zirconate, and 0.5kg of cobalt oxide were stirred evenly;

[0029] (2) Add to a high pressure homogenizer with a pressure of 15Mpa and a temperature of 95°C, mix for 18 minutes, add 0.04kg of tetraethylenepentamine, 0.6kg of octamethylcyclotetrasiloxane and bis-(phenyldimethylsiloxane) 1.2kg of alkane)methylsilanol, 0.02kg of boron trifluoride-dimethylaniline, stirred at 90°C for 15 minutes under nitrogen, degassed, poured into a flat mold, and dried in an oven at 65°C for 6 hour, demoulding to obtain the anti-fog film material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an anti-fog film material and a preparation method thereof. The above-mentioned anti-fog film material is made of the following components by weight: 68-85 parts of ethyl acetate, 8-11 parts of cellulose acetate butyrate, 0.5-2 parts of benzoyl oxide, 0.5-1.5 parts of copper sulfate pentahydrate, 0.1-0.4 parts of sodium zirconate, 0.02-0.8 parts of boron trifluoride-dimethylaniline, and 0.02-0.5 parts of cobalt oxide. The invention also provides a preparation method of the above-mentioned anti-fog film material.

Description

technical field [0001] The invention belongs to the field of film materials, in particular to an anti-fog film material and a preparation method thereof. Background technique [0002] A film is a thin, flexible, transparent sheet, usually made of plastic, adhesive, rubber, or other materials. Commonly used film materials mainly include optical film, composite film, superconducting film, polyester film, nylon film, plastic film, etc. [0003] Automobiles have become more and more important means of transportation in people's lives. The glass used on automobiles is generally ordinary glass. Although ordinary glass has good light transmittance, it is convenient to observe the situation outside the car. However, during driving, due to the difference between the specific heat of the glass and the specific heat of the air, fogging often occurs, which seriously affects the sight of the driver and passengers. At the same time, the existing automobile defogging is mainly through bl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D101/14C09D7/12
Inventor 陈昌春
Owner YANCHENG FENGYING PLASTIC PROD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap