High breaking resistant glass ceramic disc and preparation method thereof

A glass-ceramic, drop-resistant technology, applied in the field of ceramic materials, can solve problems such as poor burst resistance, poor temperature resistance, and failure to meet market demand, and achieve the effect of improved mechanical properties and strong drop resistance

Inactive Publication Date: 2015-10-07
安徽省德邦瓷业有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the rapid development of science and technology and the continuous improvement of living standards, people's requirements for the quality and performance of glass ceramic pla

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] A glass-ceramic dish with high drop resistance, made of the following raw materials in weight (kg): cullet 34, Fushan stone 20, ka-nepheline 23, chromium slag 12, basalt 24, straw ash 5, titanium pyroxene 12, dolomite Stone 10, Sky Blue Stone 14, Magnesium Zirconate 8, Sodium Carbonate 4.5, Cobalt Oxide 2.5, Lithium Silicate 4, Additive 6;

[0015] The auxiliary agent is mixed with the following raw materials by weight (kg): saltpeter powder 3, coke powder 2, potassium hydrogen tartrate 3, animal ashes 5, waste brick powder 2.5, lanthanum carbonate 1, yttrium oxalate 0.6, magnesium nitride 4. Fused calcium aluminate 5;

[0016] A method for preparing a high-shatter-resistant glass-ceramic disc, comprising the following steps:

[0017] (1) get fushan stone, ka-nepheline, chromium slag, basalt, titanite, dolomite, cerulean and mix uniformly, pulverize, cross 100 mesh sieves, add an appropriate amount of water beating to make a slurry with a concentration of 55%, then Ad...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high breaking resistant glass ceramic disc and a preparation method thereof. The high breaking resistant glass ceramic disc is prepared from the following raw materials by weight part: 27-38 of broken glass, 15-25 of vesuvianite, 14-26 of kaliophilite, 10-15 of chromium slag, 17-29 of basalt, 4-6 of straw ash, 10-15 of titanaugite, 8-16 of dolomite, 9-18 of lazulite, 5-10 of magnesium zirconate, 3-6 of sodium carbonate, 2-3 of cobalt oxide, 3-5 of lithium silicate, and of 5-7 of an assistant. The glass ceramic disc prepared by the invention is prepared by compounding of vesuvianite, kaliophilite, chromium slag, basalt, straw ash, titanaugite, lazulite, magnesium zirconate, lithium silicate and other raw materials, has greatly enhanced mechanical properties, especially the breaking strength and fracture toughness, so that the glass ceramic disc has strong breaking resistance and durability, and is worthy of wide popularization and application.

Description

technical field [0001] The invention relates to a high-shatter-resistant glass-ceramic disc and a preparation method thereof, belonging to the field of ceramic materials. Background technique [0002] Ceramic glass, also known as glass-ceramic, is a kind of composite material combined with crystal phase and glass made through high-temperature melting, molding, and heat treatment. A new type of silicate material, which is a dense, non-porous and uniform mixture composed of crystal phase and residual glass phase. Usually the size of crystals can be from nanometer to micrometer, and the number of crystals can reach 50% to 90%. It has high mechanical strength, low electrical conductivity, high dielectric constant, good machining performance, thermal stability, etc., and is widely used in daily utensils. With the rapid development of science and technology and the continuous improvement of living standards, people's requirements for the quality and performance of glass ceramic ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C10/04A47G19/02
Inventor 姚永祥
Owner 安徽省德邦瓷业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap