Alginate fiber anti-bacteria facial mask base cloth

A technology of seaweed fiber and copper alginate fiber, which is applied in the direction of non-woven fabrics, alginate artificial filaments, cosmetics, etc., can solve the problems of low tensile strength of the base fabric, easy damage, high cost of the mask, and achieve a long shelf life , High antibacterial rate, good safety effect

Inactive Publication Date: 2015-10-07
厦门百美特生物材料科技有限公司
View PDF7 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the single fiber breaking strength of silver-containing seaweed fiber is low (less than 1.6CN / dtex), and the effect of implementation will lead to low tensile strength of the base fabric. After soaking in liquid, it is easy to be damaged and cannot be used normally.
At the same time, the mask prepared by silver ion alginate fiber and copper alginate fiber is expensive, the market is difficult to accept, and it is difficult to apply in practice

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Embodiment 1: the preparation of seaweed fiber antibacterial mask base cloth

[0029] Using sodium alginate as raw material and 4 mass fraction % copper chloride aqueous solution as coagulation liquid, copper alginate fibers were prepared by wet spinning process.

[0030] 1% by weight of alginate copper fiber and 99% by weight of cupro ammonia fiber are evenly mixed, and the facial mask base cloth is prepared through a known spunlace non-woven fabric process.

[0031] The facial mask base fabric prepared in this embodiment is tested against Escherichia coli, Staphylococcus aureus, Pseudomonas aeruginosa and fungi Candida albicans according to the national standard GB / T20944.2-2007. The antibacterial rate of the bacteria was greater than 70%, which had antibacterial effect.

Embodiment 2

[0032] Embodiment 2: the preparation of seaweed fiber antibacterial mask base cloth

[0033] Using sodium alginate as raw material and 4 mass fraction % copper chloride aqueous solution as coagulation liquid, copper alginate fibers were prepared by wet spinning process.

[0034] 10% by weight of copper alginate fiber and 90% by weight of tencel are uniformly mixed, and a mask base cloth is prepared through a known spunlace non-woven fabric process.

[0035] The facial mask base fabric prepared in this embodiment is tested against Escherichia coli, Staphylococcus aureus, Pseudomonas aeruginosa and fungi Candida albicans according to the national standard GB / T20944.2-2007. The antibacterial rate of bacteria is greater than 99.999%, which has a good antibacterial effect.

Embodiment 3

[0036] Embodiment 3: the preparation of seaweed fiber antibacterial mask base cloth

[0037] Using sodium alginate as raw material and 4 mass fraction % copper sulfate aqueous solution as coagulation liquid, copper alginate fiber was prepared by wet spinning process.

[0038] 5% by weight of copper alginate fiber is evenly mixed with 49.5% by weight of cupro ammonia fiber and 49.5% by weight of tencel, and the facial mask base cloth is prepared through a known spunlace non-woven fabric process.

[0039] The facial mask base fabric prepared in this embodiment is tested against Escherichia coli, Staphylococcus aureus, Pseudomonas aeruginosa and fungi Candida albicans according to the national standard GB / T20944.2-2007. The average antibacterial rate of the bacteria is greater than 99.0%, which has a good antibacterial effect.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Freezing temperatureaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an alginate fiber anti-bacteria facial mask base cloth. The alginate fiber anti-bacteria facial mask base cloth is prepared by the steps that, by weight, 90-99 percent of regenerated cellulose fiber and, by weight, 1-10 percent of alginic acid copper fiber are uniformly mixed, and the cloth is obtained through a spunlace nonwoven technology. The alginate fiber anti-bacteria facial mask base cloth can be used for sticking-type facial masks. When essence fluid is added on the alginate fiber anti-bacteria facial mask base cloth, no preservative is needed, and the quality guarantee period is three years. In the quality guarantee period, it can be guaranteed that the colony count of a product is controlled within the national standard prescribed range. According to the alginate fiber anti-bacteria facial mask base cloth, no preservative is needed to be adopted, in addition, production, logistics, storage and use have no difference with those of current products with the addition of preservatives, the quality guarantee period is long, the antibacterial rate is high, and good news is brought to consumers.

Description

technical field [0001] The invention relates to the fields of textiles and beauty products, in particular to a seaweed fiber antibacterial facial mask base cloth. Background technique [0002] Beauty makeup stick-on masks are becoming more and more popular among consumers. Stick-on masks are mainly composed of mask base fabric soaked in essence. The general requirements for the mask base fabric are soft and comfortable, good fit, light and transparent, and strong moisture retention. Therefore, the mainstream mask base fabric is made of regenerated cellulose fibers such as cupro ammonia fiber, Tencel and other spunlace non-woven fabrics. Process preparation, the base fabric of the mask plays the role of the carrier of the essence; the essence used is usually composed of water, glycerin, hyaluronic acid, xanthan gum and other active ingredients. In order to control the reproduction of bacteria, one or more This preservative is an inevitable choice for most facial mask product...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D04H1/4258D04H1/4209D04H1/4382D04H1/492D01D5/06D01F9/04A61K8/02A61K8/73A61Q19/00
Inventor 刘松林林丽雯刘澄胜邱东黄福龙
Owner 厦门百美特生物材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com