Polyethylene/nylon composite material and preparing method thereof

A nylon composite material and polyethylene technology, applied in the field of polyethylene/nylon composite materials, can solve the problems of unfavorable environmental protection, harmful to human body, high toxicity of maleic anhydride, etc., and achieve improved mechanical properties and physical properties, good water resistance, Good dimensional stability

Inactive Publication Date: 2015-10-28
SUZHOU HONGHENG CHEM
View PDF7 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method can effectively improve the wear resistance of nylon, but maleic anhydride is highly toxic and harmful to the human body, which is not conducive to environmental protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A polyethylene / nylon composite material, in parts by weight, comprises the following components:

[0041] 10-20 parts of polyethylene, 30-60 parts of nylon 6,

[0042] 2-8 parts of nano silicon oxide, 1-5 parts of dibutyl maleate,

[0043] 2-6 parts of zinc maleate, 5-8 parts of glass fiber,

[0044] 1-3 parts of silane coupling agent, 6-10 parts of white oil,

[0045] 1-5 parts of octadecyltrimethylammonium chloride,

[0046] 0.1-0.3 parts of dicumyl peroxide,

[0047] Antioxidant 0.8-2.5 parts, other additives 1-3 parts.

[0048] Its preparation method comprises the following steps:

[0049] (1) Mix polyethylene, nano silicon oxide, silane coupling agent, dibutyl maleate, zinc maleate, dicumyl peroxide and polyethylene wax evenly, add them to the autoclave, and React at 180°C for 2-5 hours, cool to room temperature, and dry in vacuum to obtain modified polyethylene;

[0050] (2) the modified polyethylene that step (1) obtains and nylon, white oil, glass fiber, ...

Embodiment 2

[0053] A polyethylene / nylon composite material, in parts by weight, comprises the following components:

[0054] 10-20 parts of polyethylene, 30-60 parts of nylon 6,

[0055] 2-8 parts of nano silicon oxide, 1-5 parts of dibutyl maleate,

[0056] 2-6 parts of zinc maleate, 5-8 parts of glass fiber,

[0057] 1-3 parts of silane coupling agent, 6-10 parts of white oil,

[0058] 1-5 parts of octadecyltrimethylammonium chloride,

[0059] 0.1-0.3 parts of dicumyl peroxide,

[0060] Antioxidant 0.8-2.5 parts, other additives 1-3 parts.

[0061] Its preparation method comprises the following steps:

[0062] (1) Mix polyethylene, nano silicon oxide, silane coupling agent, dibutyl maleate, zinc maleate, dicumyl peroxide and polyethylene wax evenly, add them to the autoclave, and React at 180°C for 2-5 hours, cool to room temperature, and dry in vacuum to obtain modified polyethylene;

[0063] (2) the modified polyethylene that step (1) obtains and nylon, white oil, glass fiber, ...

Embodiment 3

[0066] A polyethylene / nylon composite material, in parts by weight, comprises the following components:

[0067] 10-20 parts of polyethylene, 30-60 parts of nylon 6,

[0068] 2-8 parts of nano silicon oxide, 1-5 parts of dibutyl maleate,

[0069] 2-6 parts of zinc maleate, 5-8 parts of glass fiber,

[0070] 1-3 parts of silane coupling agent, 6-10 parts of white oil,

[0071] 1-5 parts of octadecyltrimethylammonium chloride,

[0072] 0.1-0.3 parts of dicumyl peroxide,

[0073] Antioxidant 0.8-2.5 parts, other additives 1-3 parts.

[0074] Its preparation method comprises the following steps:

[0075] (1) Mix polyethylene, nano silicon oxide, silane coupling agent, dibutyl maleate, zinc maleate, dicumyl peroxide and polyethylene wax evenly, add them to the autoclave, and React at 180°C for 2-5 hours, cool to room temperature, and dry in vacuum to obtain modified polyethylene;

[0076] (2) the modified polyethylene that step (1) obtains and nylon, white oil, glass fiber, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a polyethylene / nylon composite material. The polyethylene / nylon composite material comprises, by weight, 10-20 parts of polyethylene, 30-60 parts of nylon 6, 2-8 parts of nano silicon dioxide, 1-5 parts of dibutyl maleate, 2-6 parts of zinc maleate, 5-8 parts of glass fibers, 1-3 parts of silane coupling agent, 6-10 parts of white oil, 1-5 parts of octadecyl trimethyl ammonium chloride, 0.1-0.3 part of dicumyl peroxide, 0.8-2.5 parts of antioxygen and 1-3 parts of other auxiliaries. The invention further discloses a preparing method of the polyethylene / nylon composite material. The polyethylene / nylon composite material is good in heat resistance and high temperature resistance, excellent in low temperature impact resistance, good in waterproof performance, and high in dimensional stability; in addition, the raw materials are nontoxic, and environmental protection is facilitated.

Description

Technical field: [0001] The invention relates to the field of polymer modification, in particular to a polyethylene / nylon composite material. Background technique: [0002] Nylon, the scientific name of polyamide, is the first of the five general-purpose engineering plastics. Since the invention by W.H.Carothers of DuPont in the 1930s, the production capacity and output of nylon have ranked first in engineering plastics. Nylon has high mechanical strength, high melting point, wear resistance, oil resistance and general solvent resistance, and resistance to plastics. Excellent thermal properties. However, due to the formation of hydrogen bonds between the amide groups of nylon and water molecules, compared with hydrophobic polymers such as polyolefins, it has greater water absorption, resulting in poor dimensional stability of the product, low impact strength in dry state or low temperature, Opaque, poor solubility and other shortcomings. With the continuous advancement of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/02C08L51/06C08L91/06C08K13/04C08K7/14C08K3/36C08K5/098C08K5/19B29C47/92B29C45/78B29C48/92
CPCC08L77/02B29C45/78B29C48/92B29C2945/76531B29C2948/92704C08K2201/003C08K2201/011C08L2201/08C08L2205/03C08L2207/062C08L51/06C08L91/06C08K13/04C08K7/14C08K3/36C08K5/098C08K5/19
Inventor 矫磊
Owner SUZHOU HONGHENG CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap