Non-asbestos high-density temperature and wear resisting heat insulation plate and processing technology thereof

A high-density, asbestos-free technology, applied in the thermal insulation material treatment process and refractory field, can solve problems such as human harm, and achieve the effects of low slag ball content, good toughness and high density

Active Publication Date: 2015-11-25
JINGMEN KAIDI IND TECH CO LTD
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the high-density, high-strength, and heat-resistant boards used in China are mainly produced with asbestos as raw material. Because asbestos will cause great harm to the human body, the use and production of asbestos have been completely banned in Europe, America and developed countries, and other countries have also banned the use in different fields. , although my country has not completely banned it, it will gradually ban it

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] Raw material weight portion proportioning of the present invention is:

[0025] Kaolin 260 alumina powder 30 aluminum silicate refractory fiber 240

[0026] dry pulp 15 glass fiber 10 cationic starch 20

[0027] Polyvinyl alcohol 1.2 high elastic emulsion 1.5.

[0028] Kaolin particles 1-3um; aluminum silicate refractory fiber diameter 2-4um, length 5-10mm; alumina powder particles 1-3um; glass fiber diameter 7-13um, length 3-8mm.

[0029] The processing technology is:

[0030] A . Chopped: Chopped aluminum silicate ceramic fiber cotton, and then fully cleaned the fibers by elutriation to remove slag balls;

[0031] B .Ball milling: kaolin and alumina powder are ball milled by wet method;

[0032] C .Beating: put the dry pulp into the beating equipment, and add water to make a pulp to make a paper pulp;

[0033] D . Stirring: put the above-mentioned treated aluminum silicate ceramic fiber cotton, kaolin, alumina powder and paper slurry in a stirrer and add wa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
thermal resistanceaaaaaaaaaa
Login to View More

Abstract

The invention discloses a non-asbestos high-density temperature and wear resisting heat insulation plate. The heat insulation plate is characterized by comprising, by weight, 200-260 parts of kaolin, 15-40 parts of alumina powder, 200-260 parts of aluminum silicate refractory fiber, 10-20 parts of dry paper pulp, 5-15 parts of glass fiber, 10-20 parts of cationic starch, 1-1.5 parts of polyvinyl alcohol and 1-1.5 parts of high-elastic emulsion. The non-asbestos high-density temperature and wear resisting heat insulation plate completely has no asbestos, eliminates environment risks brought by asbestos fiber in the production, maintenance and cleaning processes, is environmentally friendly and has the advantages of resisting high temperature, high pressure, bending and wear, being high in density and good in tenacity and the like. The high temperature lower than or equal to 1200 DEG C can be resisted, and the density reaches up to 900-1100 kg / m<3>. The tenacity is good, and the compression ratio can reach 1:1.4. The shot content in the non-asbestos high-density temperature and wear resisting heat insulation plate is low, and it is ensured that products making contact with the heat insulation plate are not damaged in the using process.

Description

technical field [0001] The invention relates to the field of refractory and heat insulation material processing technology Background technique [0002] High-density, high-strength, temperature-resistant, wear-resistant insulation boards are mainly used for the transmission rollers of the steel belt conveying device of the cold acid treatment annealing furnace of the stainless steel production line, the driving roller of the flat glass conveying device of the float glass production line, and the continuous melting and continuous casting steel plate production line On the transmission roller of the steel belt conveying device and the high temperature resistant sealing gasket and other equipment and components. It has the advantages of high temperature resistance, high density, high pressure resistance, flexural resistance, and good product toughness. At present, the high-density, high-strength, and heat-resistant boards used in China are mainly produced with asbestos as ra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/04C04B14/10C04B14/38C04B18/24C04B14/42C04B14/30C04B24/38
CPCY02W30/91
Inventor 郭奉炎张敏
Owner JINGMEN KAIDI IND TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products