Manufacturing method of mold

A manufacturing method and mold technology, applied in the field of mold manufacturing, can solve problems such as increased production costs, corrosion of alloy molded products or parts, shortened service life of alloy molds, etc., to achieve extended service life, low manufacturing cost, and high humidity and heat resistance sexual effect

Inactive Publication Date: 2015-12-02
CHUZHOU DIMENGDE MOLD MFG
View PDF4 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Traditional mold materials are mostly metal alloy materials, but alloy molds are easily corroded by molded products or parts, which shortens the service life of the alloy mold, and often requires repair after the alloy mold has formed thousands of products or parts. touch, or even scrap
Moreover, the production cycle of alloy molds is long, and when products or parts need to be formed in large quantities, the alloy molds need to be frequently repaired or re-opened, resulting in an increase in the production cost of producing the products or parts, which is not conducive to improving the quality of products or parts. Parts market competitiveness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0027] This embodiment provides a method for manufacturing a mold, the material for manufacturing the mold includes silicon carbide

[0028] 4%-6%, graphite 5%-8%, curing agent 2%-3%, surfactant 3%-5%, silicon dioxide 4%-6%, epoxy resin 40%-50%, plasticizer The plasticizer is 3%-5%, the montmorillonite is 4%-6%, and the balance is water; the preferred plasticizer is aliphatic dibasic acid ester, and the curing agent is isocyanate. The surfactant is selected from ethylenediamine, diethylenetriamine, ammonium dodecylbenzenesulfonate or combinations thereof. The particle size of the silicon carbide is 600-800 mesh. The particle size of the graphite is 600-800 mesh.

[0029] The method for manufacturing a mold using the above-mentioned mold material comprises the following steps:

[0030] a. Weigh silicon carbide, graphite, and silicon dioxide, crush them, and put them into a dissolver;

[0031] b. Put the curing agent, organic dispersant, epoxy resin, plasticizer and montmori...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of machining, and particularly relates to a manufacturing method of a mold. The material for manufacturing the mold comprises 4-6% of silicon carbide, 5-8% of graphite, 2-3% of curing agent, 3-5% of surfactant, 4-6% of silicon dioxide, 40-50% of epoxy resin, 3-5% of plasticizer, 4-6% of montmorillonite and the balance of water. The method for manufacturing the mold comprises the following steps: pulverizing the material, forming a blank, turning the blank, carrying out high-temperature sintering, sanding, carrying out surface treatment, and carrying out spraying treatment to obtain the corrosion-resistant non-metal mold. The manufacturing method provided by the invention has the advantages of simple technique, resource saving, low manufacturing cost, abrasion resistance and corrosion resistance, and is suitable for mass production. The method enhances the toughness of the mold and prolongs the service life of the mold on the premise of keeping high damp heat resistance, chemical corrosion resistance and mechanical strength.

Description

technical field [0001] The invention belongs to the technical field of mechanical processing, and in particular relates to a method for manufacturing a mold. Background technique [0002] Mold, various molds and tools used in industrial production for injection molding, blow molding, extrusion, die-casting or forging forming, smelting, stamping and other methods to obtain the required products. In short, a mold is a tool used to shape an object. This tool is composed of various parts, and different molds are composed of different parts. It mainly realizes the processing of the shape of the article through the change of the physical state of the formed material. There are many types of molds, which can be divided into: ①Molds for processing metals according to the processing objects and processing technology. ②Processing non-metallic and powder metallurgy molds. Including plastic molds (such as injection molds, compression molds and extrusion molds, etc.), rubber molds and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08J7/04C08L63/00C08K13/02C08K3/34C08K3/04C08K3/36
Inventor 朱余宏胡丽亚
Owner CHUZHOU DIMENGDE MOLD MFG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap