Waterborne anticorrosive coating and preparation method

A water-based technology for anti-corrosion coatings, applied in the direction of anti-corrosion coatings, epoxy resin coatings, coatings, etc., can solve the problems of weak use concept, secondary pollution, low occupancy rate, etc. Convenience, narrow distribution effect

Inactive Publication Date: 2015-12-23
ENG EQUIP CO LTD SUZHOU SAI SIDE
View PDF5 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] As we all know, coatings are widely used in all walks of life, and the solvent content in traditional solvent-based coatings is often more than 40%. These volatile organic compounds (VOC) enter the atmosphere, causing air pollution, and VOC will produce many Chemical reaction will form more toxic secondary pollution, while water-soluble coatings use water as a solvent, have extremely low VOC content, and have no pollution to the environment. Therefore, replacing solvent-based coatings with water-based coatings is the current development trend of the coatings industry; therefore, engaged in The research on water-based coatings can not only bring economic benefits, but also benefit the protection of the environment. At present, the market share of water-based coatings in my country is relatively low. Skeptical attitude, so there is a long way to go to develop and promote water-based coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] The present embodiment provides a kind of water-based anti-corrosion coating, it is characterized in that, this water-based anti-corrosion coating comprises the following components in parts by mass:

[0041] Water-based epoxy resin emulsion: 60 parts, pigments and fillers: 28 parts, film-forming aid ethylene glycol: 3 parts, leveling agent polyacrylic acid: 3 parts, defoamer tributyl phosphate: 3 parts, thickener hydroxyl Methyl cellulose: 1.1 parts, dispersant sodium hexametaphosphate: 1 part, water: 8 parts, curing agent diaminodiphenyl methyl sulfone DDS: 35 parts;

[0042] Among them: the pigment and filler are a mixture of iron oxide red and zinc phosphate, and the iron oxide red and zinc phosphate are mixed in a mass ratio of 1:1;

[0043] The preparation of aqueous epoxy resin emulsion is specifically as follows:

[0044] Pour E51 type epoxy resin into a 1000ml beaker, and heat it to 70°C in a water bath, then put it into an ultrasonic instrument, add emulsifie...

Embodiment 2

[0055] The present embodiment provides a kind of water-based anti-corrosion coating, it is characterized in that, this water-based anti-corrosion coating comprises the following components in parts by mass:

[0056]Water-based epoxy resin emulsion: 75 parts, pigments and fillers: 24 parts, film-forming aid ethylene glycol: 1 part, leveling agent hydroxymethyl cellulose: 4 parts, defoamer tributyl phosphate: 4 parts, increase Thickener hydroxymethyl cellulose: 0.5 parts, dispersant sodium hexametaphosphate: 2 parts, water: 10 parts, curing agent phenolic modified amine: 40 parts;

[0057] Among them: the pigment and filler are a mixture of iron oxide red and zinc phosphate, and the iron oxide red and zinc phosphate are mixed in a mass ratio of 1:1;

[0058] The preparation of aqueous epoxy resin emulsion is specifically as follows:

[0059] Pour E51 type epoxy resin into a 1000ml beaker, and heat it to 80°C in a water bath, then put it into an ultrasonic instrument, add emulsi...

Embodiment 3

[0070] The present embodiment provides a kind of water-based anti-corrosion coating, it is characterized in that, this water-based anti-corrosion coating comprises the following components in parts by mass:

[0071] Water-based epoxy resin emulsion: 68 parts, pigments and fillers: 20 parts, film-forming aid ethylene glycol: 2 parts, leveling agent polyacrylic acid: 2 parts, defoamer tributyl phosphate: 5 parts, thickener hydroxyl Methylcellulose: 1.5 parts, dispersant sodium hexametaphosphate: 3 parts, water: 5 parts, curing agent diethylenetriamine: 30 parts;

[0072] Among them: the pigment and filler are a mixture of iron oxide red and zinc phosphate, and the iron oxide red and zinc phosphate are mixed in a mass ratio of 1:1;

[0073] The preparation of aqueous epoxy resin emulsion is specifically as follows:

[0074] Pour E51 type epoxy resin into a 1000ml beaker, heat it in a water bath to 75°C, then put it into an ultrasonic instrument, add emulsifier OP-10 and polyoxye...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a waterborne anticorrosive coating. The waterborne anticorrosive coating comprises the following components: waterborne epoxy resin emulsion, a pigment filler, a film forming assistant, a leveling agent, a defoaming agent, a thickening agent, a dispersing agent, water and a curing agent, wherein the pigment filler is mixture of iron oxide red and zinc phosphate which are mixed according to a mass ratio of 1:1; the film forming assistant is glycol; the leveling agent is polyacrylic acid or hydroxymethyl cellulose; the defoaming agent is tributyl phosphate; the thickening agent is hydroxymethyl cellulose; the dispersing agent is sodium hexametaphosphate; the curing agent is one of diethylenetriamine, m-phenylenediamine, modified phenolic amine and diamino diphenyl sulfone (DDS). The invention further discloses a preparation method of the waterborne anticorrosive coating, the coating has good anticorrosive performance, the preparation method is simple and feasible and the cost is low.

Description

technical field [0001] The invention relates to a water-based anti-corrosion coating and a preparation method thereof, in particular to a water-based anti-corrosion coating and a preparation method thereof. Background technique [0002] As we all know, coatings are widely used in all walks of life, and the solvent content in traditional solvent-based coatings is often more than 40%. These volatile organic compounds (VOC) enter the atmosphere, causing air pollution, and VOC will produce many Chemical reaction will form more toxic secondary pollution, while water-soluble coatings use water as a solvent, have extremely low VOC content, and have no pollution to the environment. Therefore, replacing solvent-based coatings with water-based coatings is the current development trend of the coatings industry; therefore, engaged in The research on water-based coatings can not only bring economic benefits, but also benefit the protection of the environment. At present, the market sha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D5/08C09D7/12C09D7/00C09D7/06C09D7/47
Inventor 陈平顾建强钱燕华
Owner ENG EQUIP CO LTD SUZHOU SAI SIDE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap