Environment-friendly adhesive and preparation method thereof

An adhesive and tackifier technology, which can be used in the preparation of adhesives, animal glue or gelatin, and the types of adhesives, etc. It can solve the problems of human toxicity, respiratory system and lung function damage, strong mutagenicity and carcinogenicity. , to achieve the effect of low curing temperature, excellent anti-corrosion protection and high bonding strength

Inactive Publication Date: 2015-12-30
林贤文
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are many types of adhesives currently used, but the existing general adhesives contain formaldehyde, benzene, toluene and other components that are poisonous to the human body.
These toxic components have caused serious pollution to people's environment and endangered health. These harmful components have certain damage to eyes, skin, respiratory system and lung function. Long-term inhalation of a small amount of formaldehyde can also cause chronic poisoning and cause strong mutagenesis. sex and carcinogenicity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] An environmentally friendly adhesive, including the following components and percentages: 8% starch, 16% soybean protein powder, 4% 10% ammonium persulfate solution, 5% talcum powder, 1% sodium benzoate, 5% hydroxymethyl cellulose , rosin modifier 3%, citric acid 2%, and the rest is water.

[0015] The preparation method of the adhesive comprises first mixing and stirring starch, soybean protein powder, 10% ammonium persulfate solution, tackifier and 60% water at 85°C, and then adding talcum powder, sodium benzoate, hydroxymethyl cellulose, and rosin The modifier, citric acid and the remaining water were stirred at 70°C for 2h.

Embodiment 2

[0017] An environmentally friendly adhesive, including the following components and percentages: 11% starch, 22% soybean protein powder, 5% 10% ammonium persulfate solution, 7% talcum powder, 1.5% calcium propionate, 6 hydroxymethyl cellulose %, rosin modifier 4%, citric acid 3%, and the balance is water.

[0018] The preparation method of the adhesive comprises first mixing and stirring starch, soybean protein powder, 10% ammonium persulfate solution, tackifier and 65% water at 90°C, and then adding talcum powder, calcium propionate, hydroxymethyl cellulose, The rosin modifier, citric acid and the remaining water were stirred at 70°C for 2h.

Embodiment 3

[0020] An environmentally friendly adhesive, including the following components and percentages: 10% starch, 18% soybean protein powder, 4.8% 10% ammonium persulfate solution, 6.5% talcum powder, 1.2% sodium benzoate, 5.5% hydroxymethyl cellulose , rosin modifier 3.7%, citric acid 2.5%, and the balance is water.

[0021] The preparation method of the adhesive includes first mixing starch and soybean protein powder, 10% ammonium persulfate solution, tackifier and 60% water at 85°C and stirring evenly, then adding talcum powder, sodium benzoate, hydroxymethyl cellulose, rosin The modifier, citric acid and the remaining water were stirred at 70°C for 2h.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an adhesive, particularly an environment-friendly adhesive and a preparation method thereof. The environment-friendly adhesive comprises 8-11% of starch, 16-22% of soybean protein powder, 4-5% of initiator, 5-7% of talcum powder, 1-1.5% of preservative, 5-6% of tackifier, 3-4% of rosin modifier, 2-3% of buffering agent and the balance of water. The preparation method comprises the following steps: uniformly mixing the starch, soybean protein powder, initiator, tackifier and partial water at 85-90 DEG C, adding the talcum powder, preservative, tackifier, rosin modifier, buffering agent and the rest water, and continuing stirring at 70 DEG C for 2 hours. The adhesive is green and environment-friendly, does not contain any environment-polluting component, can not injure the human health in the use process, has the characteristics of higher bonding strength, higher water resistance, higher heat resistance, lower curing temperature, excellent anticorrosion protective action and the like, and belongs to an environment-friendly adhesive.

Description

technical field [0001] The invention relates to the field of adhesives, in particular to an environmentally friendly adhesive and a preparation method thereof. Background technique [0002] At present, adhesives have been widely used in people's production and life, especially in industries such as furniture manufacturing, decoration and shoemaking. There are many types of adhesives used at present, but the existing general adhesives all contain formaldehyde, benzene, toluene and other components that are poisonous to the human body. These toxic components have caused serious pollution to people's environment and endangered health. These harmful components have certain damage to eyes, skin, respiratory system and lung function. Long-term inhalation of a small amount of formaldehyde can also cause chronic poisoning and cause strong mutagenesis. sex and carcinogenicity. It can be seen that the production of a green and environmentally friendly adhesive is the development tre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J189/00C09J103/02C09J11/08C09J11/06C09J11/04
Inventor 林贤文
Owner 林贤文
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap