Non-poisonous fireproof moistureproof insulating cable

A moisture-proof insulation and cable technology, applied in the direction of insulated cables, insulated conductors, organic insulators, etc., can solve problems such as cable skin damage, unreasonable cable structure design, and corporate losses.

Inactive Publication Date: 2016-02-17
STATE GRID SHANDONG ELECTRIC POWER +2
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, with the development of society and economy, the amount of wire and cable is increasing rapidly, and the quality requirements for cables are also constantly improving, such as cables used in industries, electric power and coal mines, etc. The requirements are very high. In some special fields, the requirements for cables are very high. However, due to the unreasonable structural design of the existing cables, in practical applications, some cables are not suitable for work in some harsh environments. The cable skin is damaged by use, which not only distorts the signal transmission, but also brings a lot of inconvenience to the maintenance personnel and causes great losses to the enterprise.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A non-toxic fire-resistant and moisture-proof insulated cable, which is prepared by wrapping an aluminum alloy conductor with an insulating outer layer, and the insulating outer layer is prepared from the following raw materials in parts by weight:

[0022] 1 part of aluminum hydroxide, 1 part of graphite, 2 parts of silicon carbide, 2 parts of triphenyl phosphate, 2 parts of oleic acid amide, 3 parts of magnesium hydroxide, 3 parts of glass fiber, 3 parts of borax, 3 parts of palygorskite, hard 3 parts of fatty acid, 4 parts of aluminum nitride, 5 parts of egg shell, 6 parts of triallyl cyanurate, 10 parts of polypropylene resin, 30 parts of EPDM rubber, 30 parts of polyethylene, hydrogenated nitrile rubber 50 servings.

[0023] Among them, the particle size of aluminum hydroxide, graphite, silicon carbide, magnesium hydroxide and aluminum nitride is controlled at 100 mesh; the diameter of glass fiber is 10um, and the length is 30um.

[0024] The preparation method of...

Embodiment 2

[0030] A non-toxic, fire-resistant and moisture-proof insulated cable, which is prepared by wrapping an aluminum-copper alloy conductor with an insulating outer layer,

[0031] The insulating outer layer is prepared from the following raw materials in parts by weight:

[0032] 2 parts of aluminum hydroxide, 2 parts of graphite, 3 parts of silicon carbide, 3 parts of triphenyl phosphate, 3 parts of oleic acid amide, 4 parts of magnesium hydroxide, 4 parts of glass fiber, 4 parts of borax, 4 parts of palygorskite, hard 4 parts of fatty acid, 5 parts of aluminum nitride, 7 parts of egg shell, 8 parts of triallyl cyanurate, 12 parts of polypropylene resin, 40 parts of EPDM rubber, 40 parts of polyethylene, hydrogenated nitrile rubber 60 servings.

[0033] Among them, the particle size of aluminum hydroxide, graphite, silicon carbide, magnesium hydroxide and aluminum nitride is controlled at 100 mesh; the diameter of glass fiber is 20um, and the length is 50um.

[0034] The prepa...

Embodiment 3

[0040] The performance test of the cable prepared by the present invention:

[0041] 1. The fire-resistant and moisture-proof properties and the mechanical properties of the insulating outer layer prepared in embodiment 1 and embodiment 2, the specific test results can be seen in Table 1, wherein the thickness of the insulating outer layer is 2mm:

[0042] Table 1

[0043] group Tensile strength (N / mm 2 ) Elongation at break (%) Thermal stability time at 200°C (min) Volume resistivity×10 -15 (Ω·cm) fire-resistant level Example 1 17.2 467 >200 2.43 UL94V-0 Example 2 17.6 459 >200 2.47 UL94V-0

[0044] 2. Moisture-proof and moisture-proof performance test: put the test material under the condition of 100% humidity and 60°C for 200 days, and measure the main performance parameters, see Table 2:

[0045] Table 2

[0046] group Volume resistivity retention (%) Tensile Strength Retention Rate (%) Elongation at break (%)...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Particle sizeaaaaaaaaaa
Diameteraaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of cables, and discloses a non-poisonous fireproof moistureproof insulating cable. The cable is prepared in a manner that an insulating outer layer wraps a conductor, and the insulating outer layer is made of the following materials: aluminium hydroxide, graphite, silicon carbide, triphenyl phosphate, oleamide, magnesium hydroxide, glass fibers, borax, palygorskite, stearic acid, aluminium nitride, egg shells, triallyl cyanurate, polypropylene resin, EPDM, polyethylene, and hydrogenated butadiene-acrylonitrile rubber. The conductor is an aluminium alloy conductor or an aluminium copper alloy lead. The cable is better in fireproof, moistureproof and waterproof performances and mechanical performances.

Description

technical field [0001] The invention belongs to the field of cables, in particular to a non-toxic, fire-resistant and moisture-proof insulated cable. Background technique [0002] The high temperature and moisture resistance of the cable is particularly important, which is the guarantee for the normal transportation of electricity. At present, with the development of society and economy, the amount of wire and cable is increasing rapidly, and the quality requirements for cables are also constantly improving, such as cables used in industries, electric power and coal mines, etc. The requirements are very high. In some special fields, the requirements for cables are very high. However, due to the unreasonable structural design of the existing cables, in practical applications, some cables are not suitable for work in some harsh environments. The cable skin is damaged by use, which not only distorts the signal transmission, but also brings a lot of inconvenience to the mainten...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01B3/30H01B7/02H01B7/28H01B7/18H01B7/29C08L15/00C08L23/06C08L23/12C08L23/16C08K13/04C08K5/20C08K7/14C08K3/22C08K3/04C08K3/34C08K5/09C08K3/26C08K3/28
Inventor 王贤宗孙永波武传寿赵永贵张明李志鹏
Owner STATE GRID SHANDONG ELECTRIC POWER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products