Anticorrosive moistureproof bamboo wood processing adhesive

An adhesive and anti-corrosion technology, applied in the direction of adhesive types, starch-derived adhesives, polymer adhesive additives, etc., can solve the problems of poor water resistance and corrosion resistance, low bonding strength, etc. Cost savings, enhanced bond strength, enhanced bond strength

Inactive Publication Date: 2016-03-02
广德县永彬竹木工艺品厂
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the prior art, the present invention provides an anti-corrosion and moisture-proof adhesive for bamboo and wood processing, which solves the shortcomings of traditional adhesives for bamboo and wood processing such as low bonding strength, poor water resistance and corrosion resistance. Corrosion and moisture-proof bamboo and wood processing adhesives have wide sources of raw materials, simple production process, environmental protection and no pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The anti-corrosion and moisture-proof bamboo wood processing adhesive of this embodiment is made of the following raw materials in weight percentage: starch: 25%, potassium permanganate (5% solution): 6%, sodium hydroxide (10% solution): 6%, nano zinc oxide (ZnO): 1%, nano zirconia (ZrO 2 ): 1%, tackifier (rosin): 2%, preservative (borax): 0.2%, moisture-proof agent swelling (bentonite): 0.1%, fatty acid glyceride: 0.01%, urea: 0.02%, ammonia water: 5% , and the balance is deionized water.

[0027] The preparation method comprises the following steps:

[0028] (1) Raw material preparation: take each component by weight percentage and stand-by;

[0029] (2) Preparation of oxidized starch: put the starch in a reaction kettle, add deionized water, stir to make a starch emulsion, add 5% potassium permanganate, stir for 15 minutes to mix it with the starch emulsion, and then add 10% hydrogen Sodium oxide was reacted for 20 minutes under sufficient stirring conditions to p...

Embodiment 2

[0033] The anti-corrosion and moisture-proof bamboo wood processing adhesive of this embodiment is made of the following raw materials in weight percentage: starch: 32%, potassium permanganate (5% solution): 9%, sodium hydroxide (10% solution): 8%, nano zinc oxide (ZnO): 3%, nano zirconia (ZrO 2 ): 3%, tackifier (rosin): 3%, preservative (borax): 0.4%, moisture-proof agent (bentonite): 0.2%, fatty acid glyceride: 0.02%, urea: 0.04%, ammonia water 6%, remaining The volume is deionized water.

[0034] The preparation method comprises the steps of:

[0035] (1) Raw material preparation: take each component by weight percentage and stand-by;

[0036] (2) Preparation of oxidized starch: put the starch in a reaction kettle, add deionized water, stir to make a starch emulsion, add 5% potassium permanganate, stir for 15 minutes to mix it with the starch emulsion, and then add 10% hydrogen Sodium oxide was reacted for 25 minutes under sufficient stirring conditions to prepare oxidiz...

Embodiment 3

[0040] The anti-corrosion and moisture-proof bamboo wood processing adhesive of the present embodiment is made of the raw materials of following percentage by weight: starch: 40%, potassium permanganate (5% solution): 12%, sodium hydroxide (10% solution): 10%, nano zinc oxide (ZnO): 5%, nano zirconia (ZrO 2 ): 5%, tackifier (rosin): 4%, preservative (borax): 0.6%, moisture-proof agent (bentonite): 0.4%, fatty acid glyceride: 0.03%, urea: 0.05%, ammonia water: 7%, The balance is deionized water.

[0041] The preparation method comprises the steps of:

[0042] (1) Raw material preparation: take each component by weight percentage and stand-by;

[0043] (2) Preparation of oxidized starch: put the starch in a reaction kettle, add deionized water, stir to make a starch emulsion, add 5% potassium permanganate, stir for 15 minutes to mix it with the starch emulsion, and then add 10% hydrogen Sodium oxide was reacted for 30 minutes under sufficient stirring conditions to prepare oxid...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses an anticorrosive moistureproof bamboo wood processing adhesive and relates to the technical field of adhesives, the anticorrosive moistureproof bamboo wood processing adhesive is prepared from the following materials: starch, potassium permanganate (5% solution), sodium hydroxide (10% solution), nano zinc oxide ZnO, nano zirconia (ZrO2), a tackifier, a preservative, a moistureproof agent, fatty acid glycerides, urea, deionized water and ammonia, the anticorrosive moistureproof bamboo wood processing adhesive solves the shortcomings of low bonding strength, poor water resistance and poor corrosion resistance of the traditional bamboo wood processing adhesive, and is wide in source of the raw materials, simple in production process, environmental-friendly, and non-pollution.

Description

technical field [0001] The invention relates to the technical field of adhesives, in particular to an anti-corrosion and moisture-proof adhesive for bamboo and wood processing. Background technique [0002] A new type of adhesive based on synthetic polymers—synthetic polymer adhesives. The most widely used and most representative formaldehyde-based adhesives include urea-formaldehyde resin adhesives, phenolic resin adhesives, and melamine. Among them, urea-formaldehyde resin is used in the largest amount, accounting for about 80% of the amount of formaldehyde-based adhesives and 60% of the total consumption of bamboo and wood adhesives. This type of adhesive has developed rapidly due to its small molecular weight, good wettability, and high bonding strength, and soon replaced natural adhesives and occupied the wood adhesive market. Compared with phenolic resin and melamine resin, the water resistance of urea-formaldehyde resin is poor, mainly because after curing, urea-form...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J103/10C09J11/04C09J11/06C09J11/08C08B31/18
Inventor 陈永彬
Owner 广德县永彬竹木工艺品厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com