Multi-component copolymer and its preparation method and use

A multi-component copolymer and copolymerization technology, applied in chemical instruments and methods, descaling and water softening, water/sludge/sewage treatment, etc., can solve the problem of anti-scaling and dispersing effects that are not as good as synthetic polymers and natural polymers are unstable , easy to decompose at high temperature and other problems, to achieve the effect of improving scale inhibition and dispersing performance, narrow molecular weight distribution and high conversion rate

Active Publication Date: 2018-01-23
CHENGDU QIDA WATER TREATMENT ENG
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Organic phosphine compounds, such as ATMP, HEDP, PBTCA, etc., although they have good chemical stability, temperature resistance, synergy and chelating Ca 2+ , Mg 2+ , Zn 2+ , Fe 2+ and other metal ions and strong ability to inhibit calcium carbonate scale, but because organic phosphine can make water eutrophication, it is not conducive to environmental protection
Natural polymers, such as lignin, tannin, sodium humate, etc., have a negative effect on Ca 2+ , Mg 2+ Such salt scale crystal growth has a certain inhibitory effect, but natural polymers have the disadvantages of instability, easy decomposition, large input amount, high impurity content, high temperature and easy decomposition, and the anti-scaling and dispersion effects are not as good as synthetic polymers. less direct use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multi-component copolymer and its preparation method and use
  • Multi-component copolymer and its preparation method and use
  • Multi-component copolymer and its preparation method and use

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0037] Component A: 2 parts of hydrogen peroxide (hydrogen peroxide with a content of about 27%), 2 parts of ammonium persulfate, prepared as a 40% aqueous solution;

[0038] Component B: 15 parts of acrylic acid, 5 parts of aconitic acid, 2 parts of methyl methacrylate, 2 parts of hydroxyethyl acrylate, 2 parts of hydroxypropyl acrylate, prepared as a 59% aqueous solution;

[0039] Component C: 0.5 parts of vitamin C, 0.5 parts of sodium bisulfite, 2 parts of isopropanol, 2 parts of thioglycolic acid, 0.025 parts of ferric ammonium sulfate, 0.025 parts of copper sulfate, 3 parts of sodium vinyl sulfonate, allyl sulfonate 2 parts of sodium methacrylate, 2 parts of sodium methacrylate, 34 parts of deionized water;

[0040] According to the above-mentioned C component batching method, in the reactor equipped with a reflux condenser and a stirring device, turn on the stirring device, prepare C component, and pass steam to raise the temperature after preparation. When the temperatu...

example 2

[0042] Component A: 2 parts of hydrogen peroxide (about 27% hydrogen peroxide), 2 parts of potassium persulfate, prepared as a 40% aqueous solution;

[0043] Component B: 15 parts of acrylic acid, 5 parts of itaconic acid, 5 parts of aconitic acid, 1 part of methyl acrylate, 1 part of vinyl acetate, 2 parts of hydroxypropyl methacrylate, prepared as a 54% aqueous solution;

[0044] Component C: 0.5 parts of ferrous sulfate, 0.5 parts of sodium hypophosphite, 2 parts of n-propanol, 2 parts of thioglycolic acid, 2 parts of mercaptopropanol, 0.05 parts of iron sulfate, 0.05 parts of copper sulfate, 2 parts of sodium allyl sulfonate 2 parts, 2 parts of 2-acrylamide-2-methylpropanesulfonic acid, 25 parts of deionized water;

[0045] According to the above-mentioned C component batching method, in the reactor equipped with a reflux condenser and a stirring device, turn on the stirring device, prepare C component, and pass steam to raise the temperature after preparation. When the t...

example 3

[0047] Component A: 2 parts of potassium persulfate, 2 parts of ammonium persulfate, prepared as a 50% aqueous solution;

[0048] Component B: 5 parts of acrylic acid, 15 parts of methacrylic acid, 5 parts of aconitic acid, 5 parts of itaconic acid, 1 part of methyl methacrylate, 1 part of hydroxyethyl acrylate, prepared as a 50% aqueous solution;

[0049] Component C: 0.5 parts of sodium thiosulfate, 0.5 parts of diethylamine, 2 parts of n-propanol, 2 parts of thioglycolic acid, 2 parts of mercaptopropanol, 2 parts of mercaptoethanol, 0.05 parts of ferric ammonium sulfate, 0.05 parts of iron citrate , 0.05 parts of copper sulfate, 1 part of sodium methacrylate, 1 part of 2-acrylamide-2-methylpropanesulfonic acid, 1 part of styrenesulfonic acid, 16 parts of deionized water;

[0050] According to the above-mentioned C component batching method, in the reactor equipped with a reflux condenser and a stirring device, turn on the stirring device, prepare C component, and pass steam...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
corrosion rateaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of water treatment, and relates to a multi-component copolymer used for industrial circulating water and its preparation method and application, specifically as a scale and corrosion inhibitor, especially as a low-phosphorus, environment-friendly, corrosion and scale inhibitor. The multiple copolymer of the present invention is obtained by copolymerizing unsaturated organic monomers containing carboxyl groups, unsaturated organic monomers containing ester groups and unsaturated organic monomers containing sulfonic acid groups, and the limiting viscosity number of the multiple copolymers is 0.035~0.055dL / g. The multi-component copolymer of the present invention has properties such as scale inhibition, dispersion, corrosion inhibition, and temperature resistance, and can be used as a scale and dispersant agent; especially, it can be used as a low-phosphorus environmental protection corrosion and scale inhibitor, and can be used in circulating cooling water systems and oilfield water injection systems, seawater desalination and other fields.

Description

technical field [0001] The invention belongs to the technical field of water treatment, and relates to a multi-component copolymer used for industrial circulating water and its preparation method and application, specifically as a scale and corrosion inhibitor, especially as a low-phosphorus, environment-friendly, corrosion and scale inhibitor. Background technique [0002] The development of industrialization requires more and more water, especially in thermal power, chemical, energy and other enterprises with huge water consumption. In order to achieve the purpose of saving energy, reducing emissions, and reducing energy consumption, these industrial enterprises generally adopt circulating cooling water systems; however, after the water has been recycled for many times, the salts and other substances in the water will be concentrated, resulting in scaling and corrosion . In order to inhibit scaling and reduce corrosion, and maintain stable operation of production, it is n...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08F220/06C08F222/02C08F222/06C08F220/14C08F220/28C08F228/02C08F220/58C08F212/14C08F218/08C08F2/10C08F2/38C08F4/40C02F5/10C02F5/12C02F5/14C02F103/02C02F103/08C02F103/10
CPCC02F5/10C02F5/12C02F5/145C08F220/06C08F222/06C02F2103/023C02F2103/10C02F2103/08C08F222/02C08F220/14C08F218/08C08F220/281C08F228/02C08F220/585C08F212/14
Inventor 李雪波林坤华
Owner CHENGDU QIDA WATER TREATMENT ENG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap