Polymer green luminescence material containing Zn-Tb mixed metal and preparation method of polymer green luminescence material

A technology of mixing metals and luminescent materials, applied in 3/13 groups of organic compounds without C-metal bonds, luminescent materials, chemical instruments and methods, etc., can solve the problems of decreased fluorescence intensity, poor stability of doping materials, and high cost , to achieve the effect of simple preparation process equipment, excellent luminous performance and low cost of raw materials

Inactive Publication Date: 2016-06-22
LUOYANG NORMAL UNIV
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the preparation process of doped devices is complex and costly, and the phase separation phenomenon often occurs in host-guest devices, which reduces the device efficiency, and the wavelength of the material is almost limited, so it is difficult to modify according to needs
The commonly used method is to disperse the rare earth compound as a dopant into the transition metal coordination polymer and physically mix it. Due to the poor dispersion of the rare earth complex in the polymer matrix, it is easy to separate from the matrix and other shortcomings, resulting in doping The stability of the material is poor, the concentration quenching occurs between the fluorescent molecules, and the fluorescence intensity decreases

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polymer green luminescence material containing Zn-Tb mixed metal and preparation method of polymer green luminescence material
  • Polymer green luminescence material containing Zn-Tb mixed metal and preparation method of polymer green luminescence material
  • Polymer green luminescence material containing Zn-Tb mixed metal and preparation method of polymer green luminescence material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A kind of polymer green luminescent material of Zn-Tb mixed metal, the chemical formula of this coordination polymer is: {[Tb 3 (HMIDC) 7 ·6H 2 O][Zn 6 (bipy) 2 ·3H 2 O]·6H 2 O} n , wherein, n is greater than 1, the material can be excited by near-ultraviolet light, and emit strong green fluorescence; the Zn-Tb mixed metal polymer green light-emitting material, the specific steps are as follows:

[0031] (1), take the organic ligand H 3 MIDC (0.1mmol) was dissolved in NoOH solution with a concentration of 1mol / L, and then dispersed in a mixed organic solvent (10ml) to obtain solution A;

[0032] (2), take Zn(ClO 4 ) 2 ·6H 2 O (0.1 mmol) and Tb 4 o 7 Add (0.1mmol) (10ml) a mixed solution of water and organic solvent (the organic solvent is methanol, and the volume ratio of water to methanol is 0.5:1), stir and mix to obtain solution B;

[0033] (3) Take solution B (10ml) and add solution A (10ml), stir to obtain cloudy solution C, then add 4,4-bipy (0.2mmol)...

Embodiment 2

[0046] A kind of preparation method of the polymer green luminescent material of Zn-Tb mixed metal, concrete steps are as follows:

[0047] (1), take the organic ligand H 3 MIDC (1mmol) was dissolved in NoOH solution with a concentration of 1mol / L, and then dispersed in a mixed organic solvent (100ml) to obtain solution A;

[0048] (2), take Zn(ClO 4 ) 2 ·6H 2 O (1mmol) and Tb 4 o 7 Add (1mmol) (100ml) a mixed solution of water and organic solvent (the organic solvent is methanol, and the volume ratio of water to methanol is 1:1), stir and mix to obtain solution B;

[0049] (3) Take solution B (50ml) and add solution A (10ml), stir to get cloudy solution C, then add 4,4'-biby (0.2mmol), and adjust the pH to 4.5 with dilute nitric acid, after stirring, get Mixture D;

[0050] (4) Stir the mixed solution D with a magnetic stirrer at normal temperature and pressure to obtain the precursor solution E;

[0051] (5) Transfer the precursor solution E to a hydrothermal reactio...

Embodiment 3

[0053] A kind of preparation method of the polymer green luminescent material of Zn-Tb mixed metal, concrete steps are as follows:

[0054] (1), take the organic ligand H 3 MIDC (1mmol) was dissolved in NoOH solution with a concentration of 1mol / L, and then dispersed in a mixed organic solvent (100ml) to obtain solution A;

[0055] (2), take Zn(ClO 4 ) 2 ·6H 2 O (1mmol) and Tb 4 o 7 Add (1mmol) (100ml) a mixed solution of water and organic solvent (the organic solvent is methanol, and the volume ratio of water to methanol is 1:1), stir and mix to obtain solution B;

[0056] (3) Take solution B (20ml) and add solution A (10ml), stir to obtain cloudy liquid C, then add 4,4-biby (0.2mmol), and adjust the pH to 4 with dilute nitric acid, after stirring, a mixed Liquid D;

[0057] (4) Stir the mixed solution D with a magnetic stirrer at normal temperature and pressure to obtain the precursor solution E;

[0058] (5) Transfer the precursor solution E to a hydrothermal reacti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a polymer green luminescence material containing Zn-Tb mixed metal and a preparation method of the polymer green luminescence material. The chemical formula of the coordination polymer is {[Tb3(HMIDC)7.6H2O][Zn6(bipy)2.3H2O].6H2O}n, wherein n is larger than 1. The material can be excited by near ultraviolet and emit strong green fluorescence. The prepared polymer green luminescence material containing Zn-Tb mixed metal is good in crystal crystallinity, free of toxicity and pollution, high in heat stability, good in luminescence property and low in raw material cost. Equipment used in the preparation process is simple, the method is easy and convenient to implement and suitable for mass production, and the material can meet requirements of the application fields of display, information and illumination in the electronic industry, public places, household appliances and the like. The material has broad application in the aspects of rare-earth three-base-color fluorescent lamps, display of large-screen high-definition color television sets, rare-earth phosphor luminescence materials and the like.

Description

technical field [0001] The invention relates to the technical field of luminescent materials, in particular to a Zn-Tb mixed metal polymer green luminescent material and a preparation method thereof. Background technique [0002] The unique spectroscopic characteristics of rare earth ions make them play an important role in life science research. In recent years, rare earth luminescent materials with stable physical and chemical properties and no pollution have become a new direction for the research and development of new luminescent materials. Metal-organic frameworks (MOFs) is a new scientific research topic involving inorganic chemistry, organic chemistry and coordination chemistry, which has attracted worldwide attention. Based on rare-earth metal-organic frameworks, it can be combined with some life-necessary Metal ions such as Ca 2+ , Mg 2+ ,Al 3+ Binding proteins such as, for example, excess Al 3+ It will damage the tissues and cells of the human body, leading t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C07F19/00C09K11/06C08G83/00
CPCC07F5/003C08G83/00C09K11/06C09K2211/182C09K2211/188
Inventor 冯勋冯玉全李荣芳张甜白若飞刘献明
Owner LUOYANG NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap