A comprehensive recovery process of low-grade matte slag metal resources

A low-grade, matte technology, applied in the direction of photography technology, photography auxiliary technology, process efficiency improvement, etc., can solve the problems of no harmless resource recycling process, high cost of iron removal, high iron content, etc. , to achieve high environmental and economic benefits, reduce the cost of iron removal, and the scale can be large or small

Active Publication Date: 2017-12-22
GUANGZHOU ZHONGKE ZHENGCHUAN ENVIRONMENTAL PROTECTION TECH CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] As a dangerous solid waste, matte slag contains relatively low content of valuable metals and sulfur, and also contains a certain amount of As. If it is treated by conventional pyrometallurgical methods, it will waste resources and cannot avoid the formation of secondary pollution.
If wet treatment is used, because the iron content is too high, the cost of iron removal in the smelting process remains high, and it is difficult to realize in industrial production
At present, matte slag is used as ballast stone in shipyards or raw materials in cement plants, and there is no effective recovery and treatment process for harmless resources.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A comprehensive recovery process of low-grade matte slag metal resources

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A comprehensive recovery process for low-grade matte slag metal resources, comprising the following processing steps:

[0030] 1) The composition of matte slag produced by a certain factory: Cu 4.1%, Pb 5.44%, Fe 38.37%, Zn 1.41%, Ag 0.05%, CaO 3.3%, S 8.06%; this sample is crushed and ball milled to 95% of the sample particle size After <0.074mm, take a 500g sample, mix the slurry according to the proportion of solid content of 25%, and then use a permanent magnet semi-countercurrent magnetic separator for magnetic separation. The magnetic field strength is 800 gauss, and the iron concentrate yield is 13.3%. The obtained iron concentrate Grade up to 70.04%;

[0031] 2) Take 100g of magnetic separation tailings and add it to a beaker filled with 500ml of sulfuric acid solution with a concentration of 2mol / L. At the same time, add 1.1 times the theoretical amount of pyrolusite. Place the beaker in a water bath that has been heated to 95°C and stir for 2 hours. After fil...

Embodiment 2

[0039] A comprehensive recovery process for low-grade matte slag metal resources, comprising the following processing steps:

[0040] 1) The composition of matte slag produced by a certain factory: Cu 2.57%, Pb 5.18%, Zn 4.68%, Ag0.039%, Fe 50.74%, S 20.74%; the sample is crushed and ball milled until 100% of the sample particle size is <0.074mm Finally, take a 300g sample, mix the slurry according to the ratio of solid content of 30%, and then use a permanent magnet semi-countercurrent magnetic separator for magnetic separation. The magnetic field strength is 800 gauss, the iron concentrate yield is 13.6%, and the obtained iron concentrate grade reaches 67.7 %;

[0041] 2) Take 100g of magnetic separation tailings and add it to a beaker filled with 500ml of sulfuric acid solution with a concentration of 2mol / L. At the same time, add a theoretical amount of pyrolusite. Put the beaker in a water bath that has been heated to 90°C, stir for 3 hours, and then filter . The leachi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a comprehensive recovery process of low-grade matte slag metal resources. The process comprises the following steps: 1) matte slag performs the crushing and the wet ball milling to reach 100% of particle sizes less than 0.074 mm, and is magnetically separated by a permanent magnetic separator; and magnetically separated tailing is dehydrated for metal leaching and extraction; 2) the magnetically separated tailing performs the oxide leaching to comprehensively leach and extract valuable metal; leaching liquid is extracted to recover Cu; and strip liquor passes through electrodeposition cathode copper plate; 3) copper raffinate removes iron by using a goethite method; after Fe is removed, supernatant is extracted to recover Zn, and the strip liquor is concentrated and crystallized to prepare zinc sulfate; the obtained raffinate is extracted to recover manganese; and the strip liquor is concentrated and crystallized to prepare manganese sulfate; 4) after the raffinate is absorbed by activated carbon to reduce COD, heavy metal is treated by sulfide precipitation; and 5) after leaching slag performs the alkali washing, elemental sulfur and a lead-silver sulfide ore are recovered by flotation. The process solves the difficulty of incomplete recycling of low-grade matte slag, realizes comprehensive recovery of low-grade matte slag resources, and is higher in environmental benefit and economic benefit.

Description

technical field [0001] The invention relates to a comprehensive recovery process of low-grade matte slag metal resources, which belongs to the field of solid waste resource recovery. Background technique [0002] Matte slag is a by-product produced in the process of pyro-recovery of lead secondary resources, which contains valuable metals such as iron, lead, zinc, copper, and silver. 30%-50% of the iron in the matte slag exists in the form of elemental iron, and the rest of the iron exists in the form of FeS. The composition of matte slag is roughly as follows: Cu 2-5%, Pb 3-10%, Zn 3-10%, Ag 0.01-0.06%, Fe 35-60%, S 10-20%, most of the matte slag Both contain a certain amount of As. [0003] As a dangerous solid waste, matte slag contains relatively low content of valuable metals and sulfur, and also contains a certain amount of As. If it is treated by conventional pyrometallurgical methods, it will waste resources and cannot avoid the formation of secondary pollution. ....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22B7/00C22B19/20C22B19/30C22B47/00C25C1/12B03C1/02C01B17/06
CPCB03C1/02C01B17/06C22B7/007C22B19/22C22B19/30C22B47/00C25C1/12Y02P10/20
Inventor 晏波陈涛肖贤明
Owner GUANGZHOU ZHONGKE ZHENGCHUAN ENVIRONMENTAL PROTECTION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More