A licking brick preventing sheep urinary calculi

A technology of urinary calculus and brick licking, which is applied in the field of brick licking to prevent sheep urinary calculi, can solve the problems of economic income loss of sheep farmers, affect the growth speed of sheep, and affect the reproductive performance of sheep, so as to prevent sheep urinary calculus and improve Immunity of the body, the effect of reducing damage

Pending Publication Date: 2016-08-10
TANGSHAN NORMAL UNIV
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In recent years, the sheep breeding industry has developed rapidly, and the breeding mode has gradually changed from the original grazing to barn feeding. The main feed materials are straw, gramineous pasture, corn, cottonseed cake, wheat straw, etc., because of the transformation of feeding methods, And the reason of feed raw material causes the lamb of fattening sheep, breeding ram, fattening sheep ram etc. to appear urinary calculus in breeding process, not only influences the growth rate of sheep, and affects the reproductive performance of sheep, causes death when serious, to raising sheep loss of economic income of households

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] This embodiment is a licking brick for preventing urinary calculi in sheep. The raw materials for preparing the licking brick are mainly ammonium chloride, table salt, stone powder, grass powder, compound trace elements, compound vitamins, cement and bentonite. The preparation method is as follows:

[0017] Composite trace elements are composed of potassium iodide, cobalt chloride, zinc sulfate heptahydrate, yeast selenium and stone powder.

[0018] The multivitamin is composed of vitamin A, vitamin D, vitamin E and corncob powder.

[0019] 1. Preparation of composite trace elements Mix potassium iodide, cobalt chloride, zinc sulfate heptahydrate, yeast selenium, and stone powder in a mass ratio of 1:0.5:3:0.5:5 to obtain composite trace elements;

[0020] 2. Preparation of multivitamins: mix vitamin A, vitamin D, vitamin E, and corncob powder evenly in a mass ratio of 0.2:0.1:1:6 to form multivitamins;

[0021] 3. Preparation of grass powder: Grinding impurity-free fo...

Embodiment 2

[0026] The raw materials for preparing the licking brick are mainly ammonium chloride, table salt, stone powder, grass powder, compound trace elements, compound vitamins, cement and bentonite. The preparation method is as follows:

[0027] Composite trace elements are composed of potassium iodide, cobalt chloride, zinc sulfate heptahydrate, yeast selenium and stone powder.

[0028] The multivitamin is composed of vitamin A, vitamin D, vitamin E and corncob powder.

[0029] 1. Preparation of composite trace elements Mix potassium iodide, cobalt chloride, zinc sulfate heptahydrate, yeast selenium, and stone powder evenly in a mass ratio of 1:0.7:4:0.7:5 to obtain composite trace elements;

[0030] 2. Preparation of multivitamins: mix vitamin A, vitamin D, vitamin E, and corncob powder evenly in a mass ratio of 0.4:0.2:2:6, which is the multivitamin;

[0031] 3. Preparation of grass powder: Grinding impurity-free forage grass and straw, and the crushing particle size is such tha...

Embodiment 3

[0036] The raw materials for preparing the licking brick are mainly ammonium chloride, table salt, stone powder, grass powder, compound trace elements, compound vitamins, cement and bentonite. The preparation method is as follows:

[0037] Composite trace elements are composed of potassium iodide, cobalt chloride, zinc sulfate heptahydrate, yeast selenium and stone powder.

[0038] The multivitamin is composed of vitamin A, vitamin D, vitamin E and corncob powder.

[0039] 1. Preparation of composite trace elements Mix potassium iodide, cobalt chloride, zinc sulfate heptahydrate, yeast selenium, and stone powder in a mass ratio of 1.0:1.0:5.0:1.0:5.0 to obtain composite trace elements;

[0040] 2. Prepare multivitamins: mix vitamin A, vitamin D, vitamin E, and corncob powder evenly in a mass ratio of 0.5:0.3:2.5:6, which is the multivitamin;

[0041] 3. Preparation of grass powder: Grinding impurity-free forage grass and straw, and the crushing particle size is such that all ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A licking brick preventing sheep urinary calculi is disclosed. Raw materials for manufacturing the licking brick mainly comprise ammonium chloride, table salt, shone flour, grass meal, composite trace elements, composite vitamins, cement and bentonite. A manufacturing method includes fully mixing potassium iodide, cobaltous chloride, zinc sulfate heptahydrate, selenium yeast and stone flour according to a ratio to obtain the composite trace elements, fully mixing vitamin A, vitamin D, vitamin E and corn cob powder according to a ratio to obtain the composite vitamins, smashing impurity-free forage grass and straw with all of the smashed product passing through a standard sieve having a size of 10 meshes to obtain the grass meal, fully mixing the ammonium chloride, the table salt, the shone flour, the grass meal, the composite trace elements, the composite vitamins, the cement and the bentonite according to a ratio to obtain a mixture, fully mixing the mixture with water according to a mass ratio to obtain a slurry mixture, adding the slurry mixture into a mold, and curing for 1-3 days to obtain a final product. The licking brick reduces harm of peroxides in a body, effectively boosts body immunity, and prevents the sheep urinary calculi from a plurality of angles and by a plurality of manners.

Description

technical field [0001] The invention relates to a licking brick for sheep raising industry, in particular to a production technology of the licking brick for preventing sheep urinary calculus. Background technique [0002] In recent years, the sheep breeding industry has developed rapidly, and the breeding mode has gradually changed from the original grazing to barn feeding. The main feed materials are straw, gramineous pasture, corn, cottonseed cake, wheat straw, etc., because of the transformation of feeding methods, And the reason of feed raw material causes the lamb of fattening sheep, breeding ram, fattening sheep ram etc. to appear urinary calculus in breeding process, not only influences the growth rate of sheep, and affects the reproductive performance of sheep, causes death when serious, to raising sheep loss of economic income of households. For this reason, how to reduce the incidence of sheep urinary stones and improve the cure rate through technical means such ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A23K50/15A23K10/40A23K20/24A23K20/20A23K20/174
Inventor 李成会蔡玉梅
Owner TANGSHAN NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products