Anti-aging superfine fully vulcanizated powdered rubber polyvinyl chloride composite water pipe and preparing method thereof

A powder rubber and polyvinyl chloride technology is applied in the field of anti-aging ultra-fine fully vulcanized powder rubber and polyvinyl chloride composite water pipes and their preparation fields, which can solve the problems of poor heat resistance, easy corrosion and aging of rubber, affecting the service life of water pipes, etc. The effect of improving aging resistance, improving heat resistance and aging resistance, improving contact area and bonding strength

Inactive Publication Date: 2016-08-10
蚌埠市燕南塑料制品厂
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The water pipe obtained through this research has good strength and toughness, but the rubber is easy to corrode and age, and its heat resistance is poor, which affects the service life of the water pipe and needs to be improved. In addition, the water pipe also needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] An anti-aging ultrafine fully vulcanized powder rubber polyvinyl chloride composite water pipe, made of the following raw materials in parts by weight (kg): ultrafine fully vulcanized powder rubber 29, PVCSG, zinc oxide nanowires 2, cerium nitrate 3, deionized Water 70, butyl acrylate 1.6, ammonium persulfate 0.2, expanded graphite 2, maleic anhydride 0.8, lithium chloride sol 0.8, nanocellulose 0.5, dodecafluoroheptylpropyltrimethoxysilane 2.6, ethanol 60, ammonia water 15.

[0014] The preparation method of the anti-aging superfine fully vulcanized powder rubber polyvinyl chloride composite water pipe comprises the following steps:

[0015] (1) Mix cerium nitrate and deionized water, stir to obtain a solution, then add ultrafine fully vulcanized powder rubber, then slowly add ammonia water to the above mixture while stirring, stir and react at 30°C for 3 hours, filter and dry, get powder;

[0016] (2) Mix butyl acrylate and dodecafluoroheptylpropyltrimethoxysilane, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
impact strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses an anti-aging superfine fully vulcanizated powdered rubber polyvinyl chloride composite water pipe. The composite water pipe is prepared from, by weight, 29-30 parts of superfine fully vulcanizated powdered rubber, 68-70 parts of PVCSG-3, 2-2.3 parts of zinc oxide nanowire, 3-3.2 parts of cerous nitrate, 70-80 parts of deionized water, 1.6-1.8 parts of butyl acrylate, 0.2-0.3 part of ammonium persulfate, 2-3 parts of expanded graphite, 0.8-1 part of maleic anhydride, 0.8-1 part of lithium chloride sol, 0.5-0.6 part of nano-crystalline cellulose, 2.6-2.8 parts of dodecafluoroheptyl-propyl-trimethoxysilane, 60-70 parts of ethyl alcohol and 15-16 parts of ammonium hydroxide. By mixing expanded graphite, maleic anhydride and lithium chloride sol, the elasticity of expanded graphite is improved. By adding nano-crystalline cellulose, cohesiveness between expanded graphite and PVC is improved. Modified expanded graphite has high thermal conductivity, and the strength, tenacity and aging resistance of the water pipe are improved.

Description

technical field [0001] The invention relates to the technical field of PVC water pipes, in particular to an anti-aging superfine fully vulcanized powder rubber polyvinyl chloride composite water pipe and a preparation method thereof. Background technique [0002] Plastic pipes for pressure water supply should have both high strength and high toughness. Rigid polyvinyl chloride (PVC-U) water supply pipes have insufficient toughness and are easy to burst under the action of external conditions. Improving the mechanical properties of PVC-U materials is an effective way to increase the service life of products. The article "Research on the Modification of Rigid Polyvinyl Chloride by Ultra-fine Fully Vulcanized Powder Rubber" aims at this practical problem, starting from the basic idea of ​​toughening and enhancing the performance of PVC-U materials, for the first time using high-type resin to extrude PVC-U water supply For the pipe material, fully vulcanized ultrafine powder ru...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L51/04C08L1/02C08K13/06C08K9/04C08K9/02C08K7/24C08K7/08C08K3/22
CPCC08K2201/011C08L27/06C08L2201/08C08L2203/18C08L2205/03C08L51/04C08L1/02C08K13/06C08K9/04C08K9/02C08K7/24C08K2003/2213C08K7/08
Inventor 王志军宋秀风
Owner 蚌埠市燕南塑料制品厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com