Preparation method of non-smooth surface anti-drag liquid material
A non-smooth surface, liquid material technology, applied in biocide-containing paints, anti-fouling/underwater coatings, coatings, etc., can solve the problems of low drag reduction performance of materials, inability to fully present molds, and difficulty in demoulding , to achieve the effect of reducing mechanical operating costs, reducing energy consumption, and reducing resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
example 1
[0017] Dissect 10 artificially cultured earthworms with a length of 15 cm, remove the earthworm epidermis, wash 3 times with clean water after manual removal of impurities, transfer the earthworm epidermis to a tissue grinder, crush it into 0.2×0.2 cm epidermis fragments, and collect the obtained epidermis Fragments, put it in a fermenter filled with 30mL deionized water, seal and ferment for 6 days, filter, collect the filtrate, and set aside, collect the filter residue and soak it in formalin for 6h, set aside; weigh 10g of micron silica powder, Add it to the filtrate obtained above, set the stirring speed to 300r / min, stir and react for 2 hours, evaporate and crystallize the obtained mixed solution, and grind the obtained crystal with a mortar to obtain a composite powder; mix xylene and acetic acid at a volume ratio of 6:3:1 Butyl ester and methyl isobutyl ketone solution, then successively weigh 5g of white carbon black, 5g of fluorocarbon resin and 3g of the above-mention...
example 2
[0020] Dissect 15 artificially cultured earthworms with a length of 16 cm, remove the earthworm epidermis, wash 4 times with clean water after manual removal of impurities, transfer the earthworm epidermis to a tissue grinder, crush it into epidermal fragments of 0.3 × 0.3 cm, and collect the obtained epidermis Fragments, put it in a fermenter filled with 40mL deionized water, seal and ferment for 7 days, filter, collect the filtrate, and set aside, collect the filter residue and soak it in formalin for 7h, set aside; weigh 15g of micron silica powder, Add it to the filtrate obtained above, set the stirring speed to 400r / min, stir and react for 3h, evaporate and crystallize the obtained mixed solution, and grind the obtained crystal with a mortar to obtain a composite powder; mix xylene and acetic acid at a volume ratio of 6:3:1 Butyl ester and methyl isobutyl ketone solution, then successively weigh 7g of white carbon black, 6g of fluorocarbon resin and 4g of the above-mention...
example 3
[0023] Dissect 20 artificially cultured earthworms with a length of 18 cm, remove the earthworm epidermis, wash 5 times with clean water after manual removal of impurities, transfer the earthworm epidermis to a tissue grinder, crush it into epidermal fragments of 0.4 × 0.4 cm, and collect the obtained epidermis Fragments, put it in a fermenter filled with 50mL deionized water, seal and ferment for 8 days, filter, collect the filtrate, and set aside, collect the filter residue and soak it in formalin for 8h, set aside; weigh 20g of micron silica powder, Add it to the filtrate obtained above, set the stirring speed to 500r / min, stir and react for 4h, evaporate and crystallize the obtained mixed solution, and grind the obtained crystal with a mortar to obtain a composite powder; mix xylene and acetic acid at a volume ratio of 6:3:1 Butyl ester and methyl isobutyl ketone solution, then weigh 8g of white carbon black, 8g of fluorocarbon resin and 5g of the above-mentioned composite ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap