High-tear-resistance rubber cable material

A rubber cable, high resistance technology, applied in the direction of rubber insulators, organic insulators, etc., can solve the problems of wear-resistant collision, temperature resistance, medium resistance, aging resistance and flame retardant performance not meeting the requirements, frequent electrical accidents, cable outer protection The sleeve is easy to break and other problems, to achieve the effect of less cable short circuit, improve chemical stability, and improve processing plasticity

Inactive Publication Date: 2016-10-05
JING FENG GRP
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the continuous and rapid development of China's economy, cables have been widely used in various industries, and it is the second largest industry in China after the automobile industry. , leading to the damage or loss of the original performance of the cable rubber surface, especially when used in an environment with long-term high temperature and complex geological conditions, its wear-resistant collision, temperature resistance, medium resistance, aging resistance, and flame retardancy cannot meet the requirements. Frequent electrical accidents, and with the further improvement of the country's electrical safety requirements, the quality of cables will be higher and higher
Cable is the carrier of power transmission, and its use scenarios are very broad, which also makes the requirements for cable performance different in different application scenarios, especially in some low-temperature environments, the existing cables face many problems during use , for example, in the process of dragging and bending, the cable is easily damaged, and in the low temperature environment, the outer sheath of the cable is easily broken and damaged, which needs to be solved urgently

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] A rubber cable material with high tear resistance, made of the following raw materials in parts by weight (kg): barium fluoride 11, magnesium carbonate 5, peat soil 7, nitrile rubber 60, neoprene 55, eucalyptus essential oil 3. Copper naphthenate 1, natural rubber 55, zinc oxide 2, hollow glass microspheres 30, white clay 2, calcium hydroxide 2, silane coupling agent kh5501, epoxy resin E4412, diethylenetriamine 0.06, accelerator DA0.1, silane coupling agent kh5702.6, appropriate amount of distilled water.

[0014] The rubber cable material with high tear resistance is prepared by the following specific steps:

[0015] (1) Dry the hollow glass microspheres at 120°C for 2 hours, make a solution with absolute ethanol and distilled water at a mass ratio of 9:1, then add silane coupling agent KH550 to dissolve to make a 3% solution, and then add glass Sonicate the microbeads at 60°C for 60min, dry at 120°C for 3h after the end, cool down and set aside;

[0016] (2) Dilute...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-tear-resistance rubber cable material which is prepared from the following raw materials in parts by weight: 11-13 parts of barium fluoride, 5-7 parts of magnesium carbonate, 7-9 parts of peat soil, 60-66 parts of nitrile-butadiene rubber, 55-60 parts of chloroprene rubber, 3-4 parts of eucalyptus essential oil, 1-1.4 parts of copper naphthenate, 55-70 parts of natural rubber, 2-3 parts of zinc oxide, 30-40 parts of hollow glass microsphere, 2-2.4 parts of argil, 2-3 parts of calcium hydroxide, 1-1.3 parts of silane coupling agent kh550, 12-16 parts of epoxy resin E44, 0.06-0.1 part of diethylenetriamine, 0.1-0.2 part of accelerator DA, 2.6-3 parts of silane coupling agent kh570 and a right amount of distilled water. The high-tear-resistance rubber cable material can effectively prevent the cable from cracking, has the advantages of fewer cable short circuits and moisture resistance and prolongs the service life of the cable.

Description

technical field [0001] The invention relates to the technical field of cable materials, in particular to a rubber cable material with high tear resistance. Background technique [0002] As the name implies, hollow glass microspheres are hollow glass microspheres with different hollowness and density. In most cases, adding hollow glass microspheres to polymers can significantly reduce material costs, improve the processing flow properties of high-viscosity materials, endow products with better appearance, and improve the stiffness and even strength of materials. Under certain conditions, it can also improve the wear resistance and impact resistance of the material to a certain extent, and can also give the product good heat insulation, sound insulation and other properties. With the continuous and rapid development of China's economy, cables have been widely used in various industries, and it is the second largest industry in China after the automobile industry. , leading t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L9/02C08L11/00C08L7/00C08L63/02C08K13/06C08K9/06C08K7/28C08K5/544C08K5/5419C08K3/34C08K3/22C08K3/16C08K3/26H01B3/28
CPCC08L9/02C08L2201/02C08L2201/08C08L2203/202C08L2205/035H01B3/28C08L11/00C08L7/00C08L63/00C08K13/06C08K9/06C08K7/28C08K5/544C08K5/5419C08K3/346C08K2003/2296C08K2003/2206C08K3/16C08K2003/267
Inventor 许义彬
Owner JING FENG GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products