Novel antibacterial and mildew-proof coating as well as preparation and application methods thereof

An antibacterial and antifungal and coating technology, applied in antifouling/underwater coatings, coatings, paints containing biocides, etc. The effect of simple and easy process

Inactive Publication Date: 2016-11-16
SUZHOU TIANJIANHENG ELECTRONICS INFORMATION TECH CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, antibacterial and antifungal treatment must be carried out, and it is difficult for general-purpose epoxy coatings to be effectively applied under such conditions, and its antibacterial and antifungal effects a

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] A novel antibacterial and antifungal coating, by weight component, comprises the following components:

[0050] Ethyl acrylate-styrene copolymer 30 parts

[0051] 1 part silicon dioxide

[0052] Barium sulfate 2 parts

[0053] Calcium carbonate 8 parts

[0054] Casein 5 parts

[0055] Magnesium chloride 0.5 parts

[0056] 3 parts magnesium hydroxide

[0057] Copper pyrithione sulfate 0.8 parts

[0058] Dimethylbenzyl dodecyl ammonium bromide 0.05 parts

[0059] Titanium dioxide 12 parts

[0060] Carbon black 0.2 parts

[0061] Talcum powder 6 parts

[0062] 20 parts of purified water.

[0063] The preparation method of above-mentioned novel antibacterial antifungal paint, comprises the steps:

[0064] (1) Dissolve dimethyl benzyl dodecyl ammonium bromide in water, stir and dissolve at a stirring speed of 2500r / min and set aside;

[0065] (2) Mix ethyl acrylate-styrene copolymer, silicon dioxide, barium sulfate, calcium carbonate, casein, magnesium chloride, ...

Embodiment 2

[0070] A novel antibacterial and antifungal coating, by weight component, comprises the following components:

[0071] Ethyl acrylate-styrene copolymer 55 parts

[0072] Silicon dioxide 8 parts

[0073] Barium sulfate 12 parts

[0074] Calcium carbonate 22 parts

[0075] Casein 16 servings

[0076] Magnesium chloride 2 parts

[0077] Magnesium hydroxide 8 parts

[0078] Copper pyrithione sulfate 5 parts

[0079] Dimethylbenzyl dodecyl ammonium bromide 0.2 parts

[0080] Titanium dioxide 20 parts

[0081] Carbon black 0.5 parts

[0082] Talcum powder 15 parts

[0083] 50 parts of deionized water.

[0084] The preparation method of above-mentioned novel antibacterial antifungal paint, comprises the steps:

[0085] (1) Dissolve dimethyl benzyl dodecyl ammonium bromide in water, stir and dissolve at a stirring speed of 2800r / min and set aside;

[0086] (2) Mix ethyl acrylate-styrene copolymer, silicon dioxide, barium sulfate, calcium carbonate, casein, magnesium chloride...

Embodiment 3

[0091] A novel antibacterial and antifungal coating, by weight component, comprises the following components:

[0092] Ethyl acrylate-styrene copolymer 40 parts

[0093] 3 parts silicon dioxide

[0094] Barium sulfate 5 parts

[0095] Calcium carbonate 15 parts

[0096] Casein 8 servings

[0097] Magnesium chloride 1 part

[0098] Magnesium hydroxide 5 parts

[0099] Copper pyrithione sulfate 3 parts

[0100] Dimethylbenzyl dodecyl ammonium bromide 0.1 parts

[0101] Titanium dioxide 16 parts

[0102] Carbon black 0.3 parts

[0103] 9 parts talcum powder

[0104] 30 parts of deionized water.

[0105] The preparation method of above-mentioned novel antibacterial antifungal paint, comprises the steps:

[0106] (1) Dissolve dimethyl benzyl dodecyl ammonium bromide in water, stir and dissolve at a stirring speed of 2700r / min, and set aside;

[0107] (2) Mix ethyl acrylate-styrene copolymer, silicon dioxide, barium sulfate, calcium carbonate, casein, magnesium chloride,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a novel antibacterial and mildew-proof coating as well as preparation and application methods of the novel antibacterial and mildew-proof coating. The novel antibacterial and mildew-proof coating comprises ethyl acrylate-styrene copolymers, silicon dioxide, barium sulfate, calcium carbonate, casein, magnesium chloride, magnesium hydroxide, pyridine ketone copper sulfate, dimethyl benzyl dodecyl ammonium bromide, titanium dioxide, carbon black, talcum powder and water. The novel antibacterial and mildew-proof coating is reasonable in components, high in stability and excellent in effect, is extremely antibacterial and mildew-proof, and is capable of isolating damp and retaining warmth. The preparation method of the novel antibacterial and mildew-proof coating is simple and practicable in process, high in production efficiency, low in application cost, simple to operate and easy to implement; the produced novel antibacterial and mildew-proof coating is stable in quality, convenient to use and high in compatibility, and has high popularization and application values.

Description

technical field [0001] The invention belongs to the field of paint production, and in particular relates to a novel antibacterial and antimildew paint, and a preparation method and an application method of the novel antibacterial and antimildew paint. Background technique [0002] Generally speaking, paints and coatings are materials that can be coated on the surface of the object to be coated and form a continuous thin film that adheres firmly, whether it is a traditional coating product that uses natural substances as raw materials or a synthetic chemical product that is currently developing. The coating products of raw materials are all organic chemical polymer materials, and the formed coating film belongs to the type of polymer compound. According to the classification of modern chemical products, coatings belong to fine chemical products, and modern coatings are gradually becoming a class of multifunctional Engineering materials are an important industry in the chemica...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D133/08C09D5/14C09D7/12
CPCC09D5/14C09D133/08C09D7/61C09D7/63C08L89/00C08K13/02C08K2003/265C08K2003/166C08K3/36C08K3/34C08K5/3432
Inventor 叶晓龙
Owner SUZHOU TIANJIANHENG ELECTRONICS INFORMATION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap