Wear-resistant coating for metal pipe surface

A technology for wear-resistant coatings and metal pipes, applied in the direction of anti-corrosion coatings, fire-proof coatings, polyester coatings, etc., can solve the problems of adhesion, wear resistance and poor mechanical properties, and achieve good thermal stability, excellent mechanical properties, and mechanical properties With the effect of heat resistance enhancement

Inactive Publication Date: 2016-11-16
ANHUI ZHENGSHI NEW BUILDING MATERIAL
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the current rapid economic development, the surface protection of metal pipes has attracted more and more attention. Due to long-term harsh working environments, especially in some working environments that are outdoors for a long time and are prone to collisions, the adhesion of coatings on the surface of metal pipes , wear resistance and mechanical properties are getting higher and higher, but the adhesion, wear resistance and mechanical properties of conventional coatings are poor. With the development of science and technology in recent years, the surface coatings for metal pipes that meet the above requirements are increasingly unable to meet the needs and need to be solved urgently

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A wear-resistant coating for the surface of metal pipes, its raw materials include by weight: 20 parts of bisphenol A epoxy resin, 15 parts of alkyd resin, 5 parts of novolak epoxy resin, 18 parts of melamine, and 1 part of film-forming aid , 10 parts of modified corn gluten powder, 1 part of glass microspheres, 9 parts of zeolite powder, 2 parts of nano-calcium carbonate, 8 parts of graphene, 1 part of nano-titanium dioxide, 3 parts of vinyl triethoxysilane, 1 part of dispersant , 2 parts of antibacterial agent, 1 part of antifungal agent, 2 parts of wetting agent, 15 parts of benzyl alcohol, 30 parts of water.

Embodiment 2

[0016] A wear-resistant coating for the surface of metal pipes, its raw materials include by weight: 40 parts of bisphenol A epoxy resin, 5 parts of alkyd resin, 15 parts of novolac epoxy resin, 10 parts of melamine, and 2 parts of film-forming aids , 5 parts of modified corn gluten powder, 5 parts of glass microspheres, 5 parts of zeolite powder, 8 parts of nano-calcium carbonate, 2 parts of graphene, 5 parts of nano-titanium dioxide, 1 part of vinyl triethoxysilane, 2 parts of dispersant , 1 part of antibacterial agent, 2 parts of antifungal agent, 1 part of wetting agent, 30 parts of benzyl alcohol, and 15 parts of water.

[0017] The modified corn gluten powder is prepared by the following process: mix corn gluten powder, nano-titanium dioxide, and water, soak in microwave alkali, add trypsin to enzymolyze and inactivate, add castor protein, sodium polyphosphate, and urea to mix evenly, and use nano Titanium dioxide adjusts the pH value of the system to 7.2-8, stirs in a w...

Embodiment 3

[0019] A wear-resistant coating for the surface of metal pipes, its raw materials include by weight: 30 parts of bisphenol A epoxy resin, 12 parts of alkyd resin, 8 parts of novolac epoxy resin, 15 parts of melamine, and 1.2 parts of film-forming aid , 8 parts of modified corn gluten powder, 2 parts of glass microspheres, 8 parts of zeolite powder, 4 parts of nano-calcium carbonate, 7 parts of graphene, 2 parts of nano-titanium dioxide, 2.2 parts of vinyl triethoxysilane, 1.2 parts of dispersant , 1.6 parts of antibacterial agent, 1.2 parts of antifungal agent, 1.6 parts of wetting agent, 20 parts of benzyl alcohol, and 26 parts of water.

[0020] The modified corn gluten powder is prepared by the following process: mix 18 parts of corn gluten powder, 1 part of nano-titanium dioxide, and 50 parts of water in parts by weight, soak in microwave alkali for 5 minutes, microwave power is 500W, add trypsin for 15 minutes, and the enzymatic hydrolysis temperature 70°C, inactivate, ad...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a wear-resistant coating for the surface of metal pipes. The raw materials include: 20-40 parts of bisphenol A epoxy resin, 5-15 parts of alkyd resin, 5-15 parts of novolac epoxy resin, 10-18 parts of melamine, 1-2 parts of film-forming aid, 5-10 parts of modified corn gluten powder, 1-5 parts of glass microspheres, 5-9 parts of zeolite powder, 2-8 parts of nano-calcium carbonate, graphene 2‑8 parts, 1‑5 parts of nano titanium dioxide, 1‑3 parts of vinyl triethoxysilane, 1‑2 parts of dispersant, 1‑2 parts of antibacterial agent, 1‑2 parts of antifungal agent, 1 part of wetting agent ‑2 parts, 15‑30 parts of benzyl alcohol, 15‑30 parts of water. The invention has good mechanical properties, excellent bonding performance, and excellent wear resistance and smearing performance.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a wear-resistant coating for the surface of metal pipes. Background technique [0002] With the current rapid economic development, the surface protection of metal pipes has attracted more and more attention. Due to long-term harsh working environments, especially in some working environments that are outdoors for a long time and are prone to collisions, the adhesion of coatings on the surface of metal pipes , wear resistance and mechanical properties are getting higher and higher, but the adhesion, wear resistance and mechanical properties of conventional coatings are poor. With the development of science and technology in recent years, the surface coatings for metal pipes that meet the above requirements are increasingly unable to meet the needs and need to be solved urgently . Contents of the invention [0003] The invention provides a wear-resistant paint for the surface ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D163/00C09D167/08C09D163/04C09D189/00C09D5/08C09D7/12
CPCC09D163/00C08K2201/011C08L2201/08C08L2205/02C08L2205/035C09D5/08C09D5/18C09D7/61C09D7/63C09D7/70
Inventor 徐先锋胡正才
Owner ANHUI ZHENGSHI NEW BUILDING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products