Preparation method of SAPO-34 molecular sieve
A technology of SAPO-34 and molecular sieve, which is applied in the direction of molecular sieve characteristic silicoaluminophosphate, molecular sieve and alkali-exchanged phosphate, etc., can solve the problems of increased production cost and narrow synthesis range, and achieve improved utilization rate, huge industrial application prospects, The effect of increasing usage
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0027] The invention discloses a preparation method of SAPO-34 molecular sieve. The molecular sieve is synthesized by solid-phase grinding. The molecular sieve is synthesized by solid-phase grinding. The molecular sieve includes the following steps: firstly grinding the reaction raw materials silicon source, aluminum source, template R1 and water for 10-20 minutes, and grind uniformly before loading The crystallization reaction is carried out in the reactor; after the crystallization is completed, it is cooled at room temperature, washed with deionized water to neutrality, and dried in the air at 80°C to obtain the original molecular sieve powder; the original molecular sieve powder is roasted in the air at 600°C for 4 hours, The final product is obtained; the addition amount of each reaction raw material should be such that the molar ratio of each component during the crystallization reaction is: Al 2 O 3 : SiO 2 : H 2 O: R1 is 0.5~1.5: 0.4~1.0: 1.2~3.6: 1.0~2.0, wherein the tem...
Example Embodiment
[0033] Example 1: 11.53 g of phosphoric acid was slowly dropped into 3.89 g of tetraethylenepentamine, 30 mL of ethanol was added, stirred for 3 hours, and the ethanol was refluxed at 80° C. to obtain a light yellow solid. Then wash with ether and ethanol 3 to 4 times, and finally dry.
Example Embodiment
[0034] Example 2: 11.53g phosphoric acid was slowly dropped into 5.44g tetraethylenepentamine, 30mL ethanol was added, stirred for 3 hours, and ethanol refluxed at 80°C to obtain a light yellow solid. Then wash with ether and ethanol 3 to 4 times, and finally dry.
[0035] Synthesis of Diethylene Triamine Phosphate DETA·H 3 PO 4 :
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap