Mothproof non-woven cloth material for saline-alkali land and preparation method thereof

A non-woven, saline-alkali land technology, applied in the manufacture of fire-retardant and flame-retardant filaments, non-woven fabrics, rayon, etc. Anti-moth, improve anti-moth effect, enhance the effect of flexibility

Active Publication Date: 2016-12-21
SHANDONG SUNWAY LANDSCAPE TECH
View PDF10 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a moth-resistant non-woven fabric material for saline-alkali land, which has the advantages of good salt-alkali resistance and moth-proof, and solves the problems of poor salt-alkaline resistance and poor moth-proof effect of the existing non-woven fabrics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] A preparation method of mothproof non-woven fabric material for saline-alkali land, comprising the following steps:

[0058] S1. Preparation of the main liquid: firstly, 80 parts of polypropylene resin and 15 parts of ABS resin are heated and melted in a temperature environment of 165 degrees Celsius and a temperature environment of 220 degrees Celsius respectively. After melting, the 80 parts in the molten state are heated and melted. Mix 1 part polypropylene resin and 15 parts ABS resin and stir at a speed of 10 revolutions per second. After stirring for 10 minutes, add 5 parts ammonium polyphosphate, 8 parts antioxidant and 14 parts calcium oxide to the mixture. Stir 15 times per second, and after stirring for 8 minutes, keep it warm after mixing uniformly to obtain the main liquid;

[0059] S2. Prepare the first mixed liquid: add 8 parts of zinc borate, 1 part of jojoba oil and 1 part of sodium pentachlorophenate to the main material liquid, heat to 310 degrees Celsius, ...

Embodiment 2

[0064] A preparation method of mothproof non-woven fabric material for saline-alkali land, comprising the following steps:

[0065] S1. Preparation of the main material liquid: firstly, 90 parts of polypropylene resin and 17 parts of ABS resin are heated and melted in a temperature environment of 165 degrees Celsius and a temperature of 220 degrees Celsius respectively. After melting, the 90 parts in the molten state are heated and melted. Mix parts of polypropylene resin and 17 parts of ABS resin and stir at a speed of 10 revolutions per second. After stirring for 10 minutes, add 6 parts of ground ammonium polyphosphate, 10 parts of antioxidant and 17 parts of calcium oxide to the mixture. Stir 15 times per second, and after stirring for 8 minutes, keep it warm after mixing uniformly to obtain the main liquid;

[0066] S2. Prepare the first mixed liquid: add 9 parts of zinc borate, 1 part of jojoba oil and 1 part of sodium pentachlorophenate to the main material liquid, heat to 31...

Embodiment 3

[0071] A preparation method of mothproof non-woven fabric material for saline-alkali land, comprising the following steps:

[0072] S1. Preparation of the main liquid: firstly, 100 parts of polypropylene resin and 18 parts of ABS resin are heated and melted in a temperature environment of 165 degrees Celsius and a temperature environment of 220 degrees Celsius respectively. After melting, the 100 parts in the molten state are heated and melted. Mix parts of polypropylene resin and 18 parts of ABS resin and stir at a speed of 10 revolutions per second. After stirring for 10 minutes, add 7 parts of ground ammonium polyphosphate, 12 parts of antioxidants and 20 parts of calcium oxide to the mixture. Stir again at 15 cycles per second. After stirring for 8 minutes, keep it warm after mixing evenly to obtain the main liquid;

[0073] S2. Prepare the first mixed liquid: add 10 parts of zinc borate, 2 parts of jojoba oil and 2 parts of sodium pentachlorophenate to the main material liquid...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a mothproof non-woven cloth material for a saline-alkali land and a preparation method thereof. The mothproof non-woven cloth material for the saline-alkali land is prepared from the following components in parts by mass: 80 to 100 parts of polypropylene resin, 5 to 7 parts of ammonium polyphosphate, 15 to 18 parts of ABS (Acrylonitrile Butadiene Styrene) resin, 8 to 12 parts of an antioxidant, 14 to 20 parts of calcium oxide, 8 to 10 parts of zinc borate, 1 to 2 parts of jojoba oil, 6 to 9 parts of shaddock peel, 1 to 2 parts of sodium pentachlorophenate, 2 to 3 parts of cortex acanthopanacis, and 1 to 2 parts of wrinkled gianthyssop herb. The mothproof non-woven cloth material for the saline-alkali land has the advantages of high thermal stability, good flame retardance and good heat resistance and high strength; the calcium oxide is added into the formula, so that the saline-alkaline resistance of the material is improved; the mothproof effect of the material can be improved by adding the jojoba oil, the shaddock peel and the like; the strength and the corrosion resistance of the material can be improved by adding auxiliary agents into the material; the mothproof non-woven cloth is applicable to the places, such as the saline-alkali land, with high salinity and alkalinity, and good saline-alkaline resistance and a good mothproof effect are achieved.

Description

Technical field [0001] The invention relates to the technical field of moth-proof non-woven fabrics, in particular to a moth-proof non-woven fabric material for saline-alkali land and a preparation method thereof. Background technique [0002] Non-woven fabric, also known as non-woven fabric, is composed of oriented or random fibers. It is a new generation of environmentally friendly materials. It has many advantages such as moisture-proof, breathable, flexible, non-combustible, non-toxic, non-irritating, and recyclable. It is called cloth because of its appearance and certain properties. [0003] Non-woven fabrics do not have warp and weft threads, and are very convenient for cutting and sewing. They are deeply loved by craft lovers. However, the non-woven fabrics currently on the market generally have poor mothproofing effects. After a period of use, some insects will breed. Will decay non-woven fabrics, and when ordinary non-woven fabrics are used in some saline-alkali soils, t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D04H1/4382D01F6/46D01F1/10D01F1/07
CPCD01F1/07D01F1/10D01F1/103D01F6/46D04H1/4382
Inventor 王胜
Owner SHANDONG SUNWAY LANDSCAPE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com