Preparation method of high-solid-content low-viscosity pressure-sensitive adhesive

A high-solid content, low-viscosity technology, used in adhesives, adhesive types, ester copolymer adhesives, etc. It can reduce the viscosity of the pressure-sensitive adhesive, increase the initial tack and tack, and reduce the viscosity.

Inactive Publication Date: 2017-01-25
JIANGSU GUOJIAO CHEM TECH
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But there are still the following disadvantages: 1. There are many types of polymerized monomers, which have a large impact on the polymerization stability and viscosity of the pressure-sensitive adhesive, which makes the viscosity of the pressure-sensitive adhesive not low enough; 2. The emulsifiers and The amount of initiator is relatively small, and the amount of buffer is relatively large, so that the polymerization gel rate of the pressure-sensitive adhesive is reduced, and the viscosity is relatively increased, thereby reducing the initial adhesion and holding force of the pressure-sensitive adhesive.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] The preparation method of the high-solid-content low-viscosity pressure-sensitive adhesive of this embodiment, the specific steps of the preparation method are as follows:

[0015] (1) Preparation of raw materials: 40 parts of butyl acrylate, 15 parts of hydroxyethyl acrylate or hydroxypropyl acrylate or a mixture of the two, 10 parts of acrylic acid or methacrylic acid or a mixture of the two, ammonium bicarbonate or sodium bicarbonate or 0.1 parts of the mixture of the two, 3 parts of sodium dodecylbenzenesulfonate, 3 parts of ammonium persulfate or potassium persulfate or a mixture of the two, 1.5 parts of defoamer WBA, 40 parts of deionized water, tert-butyl persulfate 1 part of hydrogen peroxide, 1 part of sodium formaldehyde sulfoxylate or ascorbic acid or a mixture of both and 10 parts of ammonia water;

[0016] (2) Preparation of pre-emulsion: Start the agitator of reaction vessel A, control the speed at 40-60r / min, then add 30% deionized water of the total amou...

Embodiment 2

[0019] The preparation method of the high-solid-content low-viscosity pressure-sensitive adhesive of this embodiment, the specific steps of the preparation method are as follows:

[0020] (1) Preparation of raw materials: 70 parts of butyl acrylate, 5 parts of hydroxyethyl acrylate or hydroxypropyl acrylate or a mixture of the two, 0.5 parts of acrylic acid or methacrylic acid or a mixture of the two, ammonium bicarbonate or sodium bicarbonate or 0.01 parts of the mixture of the two, 0.7 parts of sodium dodecylbenzenesulfonate, 0.3 parts of ammonium persulfate or potassium persulfate or a mixture of the two, 0.5 parts of defoamer WBA, 20 parts of deionized water, tert-butyl persulfate 0.1 part of hydrogen oxide, 0.1 part of sodium formaldehyde sulfoxylate or ascorbic acid or a mixture of the two and 0.5 part of ammonia water;

[0021] (2) Preparation of pre-emulsion: Start the agitator of reaction vessel A, control the speed at 40-60r / min, then add 30% deionized water of the t...

Embodiment 3

[0024] The preparation method of the high-solid-content low-viscosity pressure-sensitive adhesive of this embodiment, the specific steps of the preparation method are as follows:

[0025] (1) Raw material preparation: 53 parts of butyl acrylate, 12 parts of hydroxyethyl acrylate or hydroxypropyl acrylate or a mixture of the two, 5.5 parts of acrylic acid or methacrylic acid or a mixture of the two, ammonium bicarbonate or sodium bicarbonate or 0.06 parts of the mixture of the two, 1.9 parts of sodium dodecylbenzenesulfonate, 1.7 parts of ammonium persulfate or potassium persulfate or a mixture of the two, 1.1 parts of defoamer WBA, 35 parts of deionized water, tert-butyl persulfate 0.6 parts of hydrogen peroxide, 0.6 parts of sodium formaldehyde sulfoxylate or ascorbic acid or a mixture of the two and 5.5 parts of ammonia water;

[0026](2) Preparation of pre-emulsion: Start the agitator of reaction vessel A, control the speed at 40-60r / min, then add 30% deionized water of the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of a high-solid-content low-viscosity pressure-sensitive adhesive. The preparation method specifically includes the steps of 1), preparation of raw materials; 2), preparation of pre-emulsion; 3), preparation of the high-solid-content low-viscosity pressure-sensitive adhesive; the raw materials include, by weight, 40-70 parts of butyl acrylate, 5-15 parts of acrylate esters, 0.5-10 parts of carboxyl containing functional monomers, 0.01-0.1 part of a buffering agent, 0.7-3 parts of an emulsifying agent, 0.3-3 parts of an initiating agent, 0.5-1.5 parts of a defoaming agent WBA, 20-40 parts of deionized water, 0.1-1 part of an oxidizing agent, 0.1-1 part of a reducing agent and 0.5-10 parts of a pH controlling agent. The preparation method has the advantages that the raw materials and use amount of the same are changed, the type of the monomers is reduced, the polymers capable of promoting stability of the pressure-sensitive adhesive and reducing viscosity of the adhesive are selected, high solid content of the pressure-sensitive adhesive is guaranteed, and viscosity of the pressure-sensitive adhesive is lowered.

Description

technical field [0001] The invention belongs to the field of adhesive manufacturing, in particular to a pressure-sensitive adhesive with high solid content and low viscosity [0002] Glue preparation method. Background technique [0003] The current biaxially oriented polypropylene films are mostly coated with ordinary pressure-sensitive adhesives with low solid content. Although the price of this type of glue is low, the technology is mature and coating is relatively convenient. However, when drying to the same degree, the heat required for glue with low solid content is much higher than that required for glue with high solid content, and the transportation cost per unit of dry glue is correspondingly higher. [0004] In view of the above phenomenon, patent CN 101676347 A discloses a 60% high solid content pressure sensitive adhesive and its preparation method. The 60% high solid content pressure sensitive adhesive is as follows by weight percentage: butyl acrylate 48-54%,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J133/08C08F220/18C08F220/28C08F220/06C08F2/44
CPCC08F2/44C08F220/18C08F220/1804C09J133/08C09J2301/302C08F220/281C08F220/06
Inventor 张孝俤王翠冈俞健钧
Owner JIANGSU GUOJIAO CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products