Cable material, and preparation method and application thereof

A cable material and raw material technology, applied in the direction of insulated cables, cables, circuits, etc., can solve the problem that the flexibility of the cable material does not meet the requirements

Active Publication Date: 2017-02-08
JIANGSU DASHENG POLYMER
View PDF7 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide a cable material and its preparation method and application, so a

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cable material, and preparation method and application thereof
  • Cable material, and preparation method and application thereof
  • Cable material, and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0080] In this embodiment, the cable material is prepared from the following raw materials in parts by weight:

[0081]

[0082] Among them, the polyethylene is linear low-density polyethylene, the molecular weight is 100,000, and the melt index is 2g / 10min; the silicone rubber is methyl vinyl silicone rubber; the grafting rate of maleic anhydride grafted EVA is 1.5%, and the The mass percentage is 30%; the molecular weight of the EPDM rubber is 50,000, the Mooney viscosity is 30, and the Shore A hardness is 20; the inorganic flame-retardant filler is aluminum hydroxide.

[0083] The preparation method is as follows:

[0084] (1) Add the above-mentioned raw materials into the internal mixer for internal mixing. After the temperature of the internal mixer reaches 125°C, turn over the materials. Before the internal mixing stops, clean the silo and the feeding port. The time is 25 minutes, and the dough is obtained;

[0085] (2) Extrude and granulate the dough obtained in st...

Embodiment 2

[0089] In this embodiment, the cable material is prepared from the following raw materials in parts by weight:

[0090]

[0091] Among them, polyethylene is high-density polyethylene with a melt index of 3g / 10min; the silicone rubber is a mixture of methyl vinyl silicone rubber and methyl phenyl vinyl silicone rubber; the grafting rate of maleic anhydride grafted EVA is 1 %, the mass percentage of VA is 32%; the molecular weight of EPDM rubber is 100,000, the Mooney viscosity is 40, and the Shore A hardness is 30; the inorganic flame retardant filler is magnesium hydroxide.

[0092] The preparation method is as follows:

[0093] (1) Add the above-mentioned raw materials into the internal mixer for internal mixing. After the temperature of the internal mixer reaches 128°C, turn over the materials. Before the internal mixing stops, clean the silo and the feeding port. The time is 23 minutes, and the dough is obtained;

[0094] (2) The dough obtained in step (1) is extruded ...

Embodiment 3

[0098] In this embodiment, the cable material is prepared from the following raw materials in parts by weight:

[0099]

[0100]

[0101]Among them, the polyethylene is linear low-density polyethylene, the molecular weight is 110,000, and the melt index is 3g / 10min; the silicone rubber is methyl vinyl silicone rubber; the grafting rate of maleic anhydride grafted EVA is 2%, and the The mass percent content is 35%; the molecular weight of EPDM rubber is 150,000, the Mooney viscosity is 70, and the Shore A hardness is 50; the inorganic flame-retardant filler is aluminum hydroxide treated with surface activation; the heat stabilizer is Zinc stearate; antioxidant tetrakis[β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate] pentaerythritol ester.

[0102] The preparation method is as follows:

[0103] (1) Add the above-mentioned raw materials into the internal mixer for internal mixing. After the temperature of the internal mixer reaches 130°C, turn over the materials. Before ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Melt indexaaaaaaaaaa
Melt indexaaaaaaaaaa
Melt indexaaaaaaaaaa
Login to view more

Abstract

The invention provides a cable material, and a preparation method and application thereof. The cable material is prepared from the following raw materials in parts by weight: 10-30 parts of polyethylene, 5-20 parts of silicone rubber, 5-15 parts of maleic anhydride graft EVA (ethylene-vinyl acetate), 0.5-10 parts of ethylene propylene diene monomer rubber, 40-65 parts of flame retardant, 2-5 parts of red phosphorus, 0.1-2 parts of silane coupling agent and 0.1-2 parts of triallyl isocyanurate. The preparation method comprises the following steps: banburying, extrusion and irradiation crosslinking. The cable material provided by the invention has the advantages of high flexibility, favorable insulativity, favorable flame retardancy, favorable oil resistance and favorable cold resistance, and is applicable to automobile wire insulating materials.

Description

technical field [0001] The invention belongs to the field of insulating materials, in particular to a cable material and a preparation method and application thereof. Background technique [0002] Wires and cables are one of the important parts of automobiles, and their reliability is crucial to driving safety. Due to various complex environments such as vibration, friction, ozone, oil pollution, high heat, cold and electromagnetic radiation inside the car, it is required that the car wires have various functions such as heat resistance, cold resistance, wear resistance, oil resistance and anti-interference. And as the functions of the car continue to change, the requirements for the car's wires are also increasing. [0003] The power system, control system and safety system of electric vehicles are all driven by electricity, and the internal cables will carry higher voltage and current than traditional automotive cables. The high current passing through the internal cable...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L83/07C08L23/08C08L23/16C08L51/06C08K13/02C08K3/22C08K3/02C08K5/3492C08K13/06C08K5/098B29C47/92H01B7/02B29C48/92
CPCB29C48/92B29C2948/92704C08K2201/014C08L23/06C08L23/0815C08L83/04C08L2201/02C08L2201/08C08L2203/202C08L2205/025C08L2205/035C08L2207/062C08L2312/06H01B7/02C08L23/16C08L51/06C08K13/02C08K2003/2227C08K2003/026C08K5/34924C08K2003/2224C08K13/06C08K5/098
Inventor 潘卫东范魏魏罗顺
Owner JIANGSU DASHENG POLYMER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap