Composite silane modified automobile leaf spring paint and preparation method thereof

Abstract

The invention discloses composite silane modified automobile leaf spring paint. The composite silane modified automobile leaf spring paint is prepared from, by weight, 0.7-1 part of tetrahydro-1,3,4,6-tetrakis(methoxymethyl)imidazo[4,5-d]imidazole-2,5(1H,3H)-dione, 0.4-1 part of triphenylphosphine, 0.1-0.2 part of dodecafluoroheptyl-propyl-trimethoxysilane, 1-2 parts of aluminum ammonium sulfate, 7-9 parts of hydroxyethyl methylacrylate, 0.8-1 part of phosphorus pentoxide, 2-3 parts of p-methoxyphenol, 0.6-2 parts of tetrabutylammonium bromide, 17-20 parts of acrylic acid, 6-8 parts of methyl methacrylate, 140-150 parts of epoxy resin E-51, 0.07-0.1 part of ammonium persulfate, 2-3 parts of sodium bicarbonate, 0.6-1 part of sodium dodecyl benzene sulfonate, 0.2-0.4 part of hexamethyl cyclotrisiloxane, 1-2 parts of sodium diacetate, 6-9 parts of kaolin and 1-2 parts of alkenyl succinic anhydride. The paint is low in cost, and the problems that at the present stage, an automobile leaf spring coating is large in falling amount, not environmentally friendly and poor in anti-rust capability are solved.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a composite silane-modified automobile leaf spring coating and a preparation method thereof. Background technique [0002] Acrylic monomers are often used in the polymerization process of water-based acrylic resins. Due to the presence of hydrophilic carboxyl groups on acrylic acid, the stability of polymer emulsions is enhanced. Under dry film conditions, carboxyl groups can closely adhere to the substrate Together, the adhesion between the coatings is greatly improved; but in a humid environment, because the carboxyl group on the acrylic acid is hydrophilic, the association with water is very strong, and the water molecules are easily absorbed into the coating and the metal through the capillary. In the interface, the force between the carboxyl group and the surface of the metal substrate is greatly reduced, the adhesion in the wet state is poor, and the water resistance is re...

AI Technical Summary

Problems solved by technology

If the coating is too thin, the general coating has poor antirust performance and is not enough to protect the automobile leaf spring, which requires the new coating to have the highest possible antirust performance under the condition of a thinner coating

At present, the coatings of automobile leaf springs at home and abroad are relatively thick, and there are more or less damages caused by too thick extrusion during the coating assembly process. These damages will further become corrosion spots, which seriously affect the coating quality of automobile leaf springs. Quality, improving the rust resistance of the coating per unit thickness as much as possible is gradually becoming a problem that needs to be solved urgently