Anti-stain anti-corrosion antibacterial stainless steel plate and preparation method thereof
An antibacterial stainless steel and stainless steel plate technology, applied in antifouling/underwater coatings, electrolytic coatings, surface reaction electrolytic coatings, etc., can solve the problems of complex production process, high production cost, single performance, etc., and achieve high safety, Enhanced corrosion resistance and mild components
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0037] Example 1
[0038] An anti-fouling, anti-corrosion and antibacterial stainless steel plate.
[0039] (1) Mechanical polishing: polish the surface of the stainless steel plate with sandpaper;
[0040] (2) Alkaline washing: Put the mechanically polished stainless steel plate into Na 2 CO 3 Soak in the mixture of NaOH and NaOH for 15 minutes, take it out, and dry; 2 CO 3 The concentration of NaOH and NaOH are both 5g / mL;
[0041] (3) Pickling: Soak the alkali-washed stainless steel plate in hydrochloric acid for 10 minutes, take it out, and dry;
[0042] (4) Passivation: Put the acid-washed stainless steel plate into passivation solution, passivate it for 5min under the condition of anode voltage of 6 volts; the passivation solution consists of 2g / mL citric acid, 200mL / L glacial acetic acid, 2g / mL sodium chloride, 2mL / LH 2 O 2 And 1g / mL agar powder;
[0043] (5) Oxidation: Place the passivated stainless steel in a film-forming solution and treat it with alternating positive and neg...
Example Embodiment
[0059] Example 2
[0060] An anti-fouling, anti-corrosion and antibacterial stainless steel plate.
[0061] (1) Mechanical polishing: polish the surface of the stainless steel plate with sandpaper;
[0062] (2) Alkaline washing: Put the mechanically polished stainless steel plate into Na 2 CO 3 Soak in the mixed solution of NaOH and NaOH for 20 minutes, take it out, and dry; 2 CO 3 The concentration of NaOH and NaOH are both 3g / mL;
[0063] (3) Pickling: Soak the alkali-washed stainless steel plate in hydrochloric acid for 15 minutes, take it out, and dry;
[0064] (4) Passivation: Put the acid-washed stainless steel plate into passivation solution, passivate 8min under the condition of anode voltage of 4V; the passivation solution consists of 5g / mL citric acid, 300mL / L glacial acetic acid, 5g / mL sodium chloride, 5mL / LH 2 O 2 And 2g / mL agar powder;
[0065] (5) Oxidation: Place the passivated stainless steel in a film forming solution, and treat it with alternating positive and negativ...
Example Embodiment
[0081] Example 3
[0082] An anti-fouling, anti-corrosion and antibacterial stainless steel plate.
[0083] (1) Mechanical polishing: polish the surface of the stainless steel plate with sandpaper;
[0084] (2) Alkaline washing: Put the mechanically polished stainless steel plate into Na 2 CO 3 Soak in the mixed solution of NaOH and NaOH for 20 minutes, take it out, and dry; 2 CO 3 The concentration of is 5g / mL, and the concentration of NaOH is 3g / mL;
[0085] (3) Pickling: Soak the alkali-washed stainless steel plate in hydrochloric acid for 15 minutes, take it out, and dry;
[0086] (4) Passivation: Put the acid-washed stainless steel plate into passivation solution, passivate for 6min under the condition of anode voltage of 5V; the passivation solution consists of 4g / mL citric acid, 300mL / L glacial acetic acid, 3g / mL sodium chloride, 3mL / LH 2 O 2 And 1.5g / mL agar powder;
[0087] (5) Oxidation: The passivated stainless steel is placed in a film forming solution, and treated with alt...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap