Impact-resistant plastic electric power fitting composite material and making method thereof

A technology of electric power fittings and composite materials, applied in the field of composite materials, can solve the problems of reducing crystallization, creep performance, poor notched impact strength of dimensional stability, destroying the regularity of molecular structure, etc., to achieve improved water resistance and long anti-aging time , the effect of reducing internal defects

Inactive Publication Date: 2017-04-26
马鞍山市华能电力线路器材有限责任公司
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, due to the high crystallinity of nylon and the gap in grain size, there are many microscopic defects in the nylon structure, resulting in poor creep performance, dimensional stability and notched impact strength. These shortcomings limit the application of nylon. Therefore, it is necessary to modify nylon to destroy the regularity of its molecular structure and reduce crystallization, and because electric fittings have been used outdoors for a long time and the environment is harsh, in addition to requiring the material to be resistant to water and aging, its wear resistance, antistatic, and electric resistance Performance such as halo and lightning protection also needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] An impact-resistant plastic power fitting composite material, made of the following raw materials in parts by weight: waste nylon 66 plastic 100, o-cresol novolac epoxy resin 2.1, glass fiber 20, nano-magnesium oxide 1.1, carbon black 18, silane coupling agent KH550 6, chlorinated paraffin 3, polyurethane emulsion 6, wheat straw fiber powder 4.

[0015] A method for making an impact-resistant plastic power fitting composite material includes the following steps:

[0016] (1) Stir and grind nano-magnesium oxide and carbon black for 1-2 hours, calcinate at 800-900°C for 30-40 minutes, cool to 120-130°C, add polyurethane emulsion and ultrasonically grind for 10-15 minutes, and dry to obtain modification Nano magnesium oxide;

[0017] (2) Put the glass fiber into 20-30 times the mass of hydrogen peroxide solution with a mass concentration of 25%, stir and mix evenly, heat up to 105°C, reflux for 3-6 hours, filter and dry, add silane coupling agent KH550 and heat up to 80°C...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
impact strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an impact-resistant plastic electric power fitting composite material. The composite material is made from, by weight, 100 parts of waste nylon 66 plastic, 2.1-2.4 parts of o-cresol formaldehyde epoxy resin, 20-21 parts of glass fibers, 1.1-1.4 parts of nanometer magnesium oxide, 18-20 parts of carbon black, 6-8 parts of a silane coupling agent KH550, 3-5 parts of chlorinated paraffin, 6-8 parts of a polyurethane emulsion and 4-6 parts of wheat straw fiber micro-powder. Nylon is modified with the epoxy resin to form a matrix, modified glass fibers are adopted as a reinforcement material, the nanometer magnesium oxide grafted and modified with the polyurethane emulsion is added to a material, and other effective components are adopted to prepare the composite material, so the composite material has the advantages of solving of hysteresis loss and eddy current loss, no electric energy loss, high impact resistance, high mechanical strength and long ageing resistance.

Description

technical field [0001] The invention relates to the technical field of composite materials, in particular to an impact-resistant plastic power fitting composite material and a manufacturing method thereof. Background technique [0002] Power fittings are metal accessories that connect and combine various devices in the power system to transmit mechanical loads, electrical loads and some kind of protection. They are important components in the power transmission process. At present, non-magnetic aluminum alloys are mainly used. Although compared with the ferromagnetic materials used before, they play a certain role in energy saving and emission reduction of the power grid, but as metal conductors, eddy current losses still exist, and power loss is still unavoidable. Products must be obtained through high energy consumption and high pollution processes such as ore dressing, mining, electrolysis, and smelting. They are industries restricted by the state and cannot meet the econ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/06C08L63/04C08L91/06C08L97/02C08K13/06C08K9/04C08K9/00C08K3/22C08K3/04C08K9/06C08K9/02C08K7/14
CPCC08K2201/011C08L77/06C08L2201/08C08L2203/20C08L2205/035C08L2205/16C08L63/04C08L91/06C08L97/02C08K13/06C08K9/08C08K9/00C08K2003/222C08K3/04C08K9/06C08K9/02C08K7/14
Inventor 余炜于水马世虎
Owner 马鞍山市华能电力线路器材有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products