Breathable wearing-resistant fabric material and preparation method thereof

A technology of textile materials and raw materials, which is applied in the field of breathable and wear-resistant textile materials and their preparation, can solve problems such as sagging, lack of elasticity, and easy deformation, and achieve the effects of strong friction resistance, strong practicability, and cheap raw materials

Inactive Publication Date: 2017-06-23
马志明
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But at the same time, there are also defects such as lack of elasticity, easy deformation, wrinkling and sagging.
[0010] Therefore, from the perspective of the development of material science, pure chemical fibers or natural fibers cannot meet the growing requirements of modern society for the performance of preventive materials. It is particularly necessary to prepare a composite textile material that is superior to ordinary fiber materials by combining the chemical composition and the corresponding production process.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] (1) Take by weight 50 parts of apocynum fiber, 40 parts of viscose fiber, 35 parts of polylactic acid, 30 parts of trimethyl metasilicate, 20 parts of dilauryl thiodipropionate, dodecylbenzene 18 parts of sodium sulfonate, 12 parts of phosphatidylethanolamine, 8 parts of potassium metabisulfite, 6 parts of cetyltrimethylammonium bromide, 6 parts of hydroxypropyl starch, 4 parts of nano silicon dioxide, cetyl alcohol sulfuric acid 4 parts of ester sodium salt, 3 parts of linoleic acid, 2 parts of silane coupling agent KH-590, 2 parts of sulfenamide, 160 parts of deionized water;

[0030] (2) Polylactic acid, trimethyl metasilicate, dilauryl thiodipropionate, sodium dodecylbenzenesulfonate, phosphatidylethanolamine, potassium metabisulfite, cetyl trimethyl bromide Mix ammonium, hydroxypropyl starch and deionized water, place on a magnetic stirrer and stir at a speed of 650r / min for 35min, then heat up to 80°C, and bathe in water for 15min to obtain a preliminary mixture; ...

Embodiment 2

[0036] (1) Take by weight 53 parts of apocynum fiber, 45 parts of viscose fiber, 40 parts of polylactic acid, 35 parts of trimethyl metasilicate, 23 parts of dilauryl thiodipropionate, dodecylbenzene 20 parts of sodium sulfonate, 14 parts of phosphatidylethanolamine, 10 parts of potassium metabisulfite, 7 parts of cetyltrimethylammonium bromide, 7 parts of hydroxypropyl starch, 5 parts of nano silicon dioxide, cetyl alcohol sulfate 5 parts of ester sodium salt, 4 parts of linoleic acid, 3 parts of silane coupling agent KH-550, 3 parts of epoxy resin, 160 parts of deionized water;

[0037] (2) Polylactic acid, trimethyl metasilicate, dilauryl thiodipropionate, sodium dodecylbenzenesulfonate, phosphatidylethanolamine, potassium metabisulfite, cetyl trimethyl bromide Mix ammonium, hydroxypropyl starch and deionized water, place on a magnetic stirrer and stir at a speed of 700r / min for 40min, then heat up to 85°C, and bathe in water for 20min to obtain a preliminary mixture;

[0...

Embodiment 3

[0043] (1) Take by weight 55 parts of apocynum fiber, 50 parts of viscose fiber, 45 parts of polylactic acid, 40 parts of trimethyl metasilicate, 26 parts of dilauryl thiodipropionate, dodecylbenzene 22 parts of sodium sulfonate, 16 parts of phosphatidylethanolamine, 12 parts of potassium metabisulfite, 8 parts of cetyltrimethylammonium bromide, 8 parts of hydroxypropyl starch, 6 parts of nano silicon dioxide, cetyl alcohol sulfate 6 parts of ester sodium salt, 5 parts of linoleic acid, 4 parts of silane coupling agent KH-560, 4 parts of polyvinyl alcohol, 160 parts of deionized water;

[0044] (2) Polylactic acid, trimethyl metasilicate, dilauryl thiodipropionate, sodium dodecylbenzenesulfonate, phosphatidylethanolamine, potassium metabisulfite, cetyl trimethyl bromide Mix ammonium, hydroxypropyl starch and deionized water, place on a magnetic stirrer and stir at a speed of 750r / min for 45min, then heat up to 90°C, and bathe in water for 25min to obtain a preliminary mixture;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a breathable wearing-resistant fabric material and a preparation method thereof. The preparation method comprises the following steps: by taking apocynum fiber, viscose, polylactic acid and trimethyl metasilicate as main components, adding dilauryl thiodipropionate, sodium dodecyl benzene sulfonate, phosphatidyl ethanolamine, potassium metabisulfite, cetyl trimethyl ammonium bromide, hydroxypropyl starch, nanosilicon dioxide, sodium cetyl sulfate, linoleic acid, a silane coupling agent, an adhesive and deionized water, and performing magnetic stirring, heating water bath, ball milling treatment, high-pressure homogenization, screw rod extrusion and the like, thereby obtaining the breathable wearing-resistant fabric material. The breathable wearing-resistant fabric material is good in breathability, good in fraction property, capable of meeting industrial requirements and has relatively good application prospects.

Description

technical field [0001] The invention relates to the technical field of textile materials, in particular to a breathable and wear-resistant textile material and a preparation method thereof. Background technique [0002] Textile materials refer to fibers and fiber products, specifically fibers, yarns, fabrics and their composites. In modern textiles, the research and development of new textile materials, especially the development and use of nanofibers, has broken through the traditional concept of textile materials. Textile materials have become an important part of soft materials, and one of the basic characteristics of textile materials is to take "shape" and its composite form as the research subject. [0003] Traditional textile materials mainly refer to fibers, which are the basic unit of textile materials. The source, composition, preparation, shape, and performance of fibers are extremely rich and complex. In simple terms, fibers are divided into two categories: na...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L1/02C08L67/04C08L3/08C08L63/00C08L29/04C08K13/02C08K5/372C08K5/19C08K5/42C08K5/09C08K3/36C08K5/544C08K5/44B29B9/06
CPCC08L1/02B29B9/06C08K2201/011C08L2205/025C08L2205/03C08L2205/035C08L2205/16C08L67/04C08L3/08C08K13/02C08K5/372C08K5/19C08K5/42C08K5/09C08K3/36C08K5/544C08K5/44C08L63/00C08L29/04
Inventor 马志明
Owner 马志明
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap