Latex abrasive base paper and preparation method and application thereof

A technology of latex and sandpaper, applied in the direction of synthetic cellulose/non-cellulose material pulp/paper, paper, papermaking, etc. Lightweight, thermally stable, highly opaque effects

Inactive Publication Date: 2017-08-11
杭州特种纸业有限公司
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The latex sandpaper base paper currently on the market mainly has disadvantages such as poor wear resistance, poor flexibility, and low tensile strength, which seriously affect the quality and use effect of the finished paper.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Latex sandpaper base paper, including 30 parts by weight of corn stalk fiber, 10 parts of high-density cotton linter pulp, 5 parts of polypropylene fiber, 20 parts of alkali-free glass fiber chopped strands and 3 parts of ceramic fiber, used in the preparation of base paper 0.1 part of amphoteric polyacrylamide, 0.2 part of modified starch light calcium carbonate, 0.5 part of polyethylene oxide with a molecular weight of 2.5 million to 3 million and 5 parts of latex. The latex includes 60 parts by weight of natural latex 0.2 parts of zinc oxide, 1 part of solid paraffin, 6 parts of superfine ground calcium carbonate filler, 0.2 parts of dispersant sodium hexametaphosphate, 0.1 part of titanate coupling agent, 0.01 part of initiator ammonium persulfate, anti-aging 0.1 part of agent DBH, 0.05 part of hydrophobically modified alkali-swellable anionic associative thickener.

[0025] The preparation of the high-density cotton linter pulp is obtained by adding YY-02 penetrati...

Embodiment 2

[0038] Latex sandpaper base paper, including 50 parts by weight of corn stalk fiber, 30 parts of high-density cotton linter pulp, 12 parts of polypropylene fiber, 40 parts of alkali-free glass fiber chopped strands and 8 parts of ceramic fiber, used in the preparation of base paper 4 parts of amphoteric polyacrylamide, 0.8 part of modified starch light calcium carbonate, 5 parts of polyethylene oxide with molecular weight of 2.5 million to 3 million, 0.2 part of defoamer and 10 parts of latex. The count includes 80 parts of natural latex, 0.5 part of zinc oxide, 3 parts of solid paraffin, 8 parts of superfine ground calcium carbonate filler, 0.5 part of sodium hexametaphosphate as dispersant, 0.4 part of titanate coupling agent, and initiator 0.1 part of ammonium sulfate, 0.3 part of anti-aging agent DBH, 0.2 part of hydrophobically modified alkali-swellable anionic associative thickener.

[0039] As a preference, the high-density cotton linter pulp is prepared by adding YY-02...

Embodiment 3

[0052] Latex sandpaper base paper, including 45 parts by weight of corn stalk fiber, 15 parts of high-density cotton linter pulp, 7 parts of polypropylene fiber, 23 parts of alkali-free glass fiber chopped strands and 5 parts of ceramic fiber, used in the preparation of base paper 1.8 parts of amphoteric polyacrylamide, 0.4 part of modified starch light calcium carbonate, 4.1 parts of polyethylene oxide with a molecular weight of 2.5 million to 3 million, 0.1 part of defoamer and 6 parts of latex. The count includes 70 parts of natural latex, 0.4 parts of zinc oxide, 2 parts of solid paraffin, 7 parts of superfine ground calcium carbonate for filler, 0.3 part of sodium hexametaphosphate for dispersant, 0.3 part of titanate coupling agent, and 0.3 part of initiator hyperthermia. 0.08 parts of ammonium sulfate, 0.2 parts of anti-aging agent DBH, 0.15 parts of hydrophobically modified alkali-swellable anionic associative thickener.

[0053] As a preference, the high-density cotto...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to view more

Abstract

The invention provides latex abrasive base paper, which is prepared from the following raw materials in parts by weight: 30-50 parts of cornstalk fiber, 100 parts of high-density cotton linter pulp, 5-12 parts of polypropylene fiber, 20-40 parts of alkali-free glass fiber chopped strands and 3-8 parts of a ceramic fiber; the base paper is prepared from the following raw materials in parts by weight: 0.1-4 parts of amphoteric polyacrylamide, 0.2-0.8 part of modified starch light calcium carbonate, 0-0.2 part of polyoxyethylene with the molecular weight of 2500000 to 3000000, 0-0.2 part of an antifoaming agent and 5-10 parts of latex. The latex abrasive base paper has the characteristics of being good in abrasive resistance, good in flexibility and high in tensile strength.

Description

technical field [0001] The invention relates to the technical field of paper, in particular to a latex sandpaper base paper and a preparation method and application thereof. Background technique [0002] Sandpaper is a kind of paper used for grinding, and latex sandpaper base paper is one of the raw materials used to make high-quality grinding sandpaper. It has the advantages of high grinding finish, low friction temperature, and high durability. It is mainly used for grinding cars. , Mold, etc. The latex sandpaper base paper currently on the market mainly has disadvantages such as poor wear resistance, poor flexibility, and low tensile strength, which seriously affect the quality and use effect of the finished paper. Contents of the invention [0003] Aiming at the deficiencies of the prior art, the invention provides a latex sandpaper base paper with good abrasion resistance, good flexibility and high tensile strength; the invention also provides a preparation method of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21H11/12D21H13/14D21H13/40D21H13/36D21H15/12D21H17/37D21H17/28D21H17/67D21H17/46D21H25/04D21H21/16D21H21/10D21H21/14B24D11/02
CPCD21H11/12B24D11/02D21H13/14D21H13/36D21H13/40D21H15/12D21H17/28D21H17/37D21H17/46D21H17/675D21H21/10D21H21/14D21H21/16D21H25/04
Inventor 王建业吴琼华吴安波
Owner 杭州特种纸业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap