Cable used for wind turbine generators

A technology for wind turbines and generators, applied in the field of cables, which can solve the problems of poor cable crack resistance, short service life, and low safety performance, and achieve significant smoke suppression effects, enhanced wear resistance and compression resistance, and use long life effect

Inactive Publication Date: 2017-08-15
安徽省无为县经纬电缆附件有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Wind power generation projects are carried out in the open air, and the service life of the cable sheath material is required to be very long. This requires extremely high thermal stability, aging resistance and mechanical properties of the cable material for wind turbine generators in extreme environments. Ordinary The cable has poor cracking resistance, low safety performance and short service life cycle

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A cable for a wind turbine generator proposed by the present invention includes: a cable core and a sheath layer coated on the outside of the cable core, and the raw materials of the sheath layer include by weight: 2 parts of antioxidant, isobutyl triethyl 5 parts of silicon oxide, 8 parts of plasticizer, 1.4 parts of hexamethylolmelamine hexamethyl ether, 0.4 parts of ethoxylated trimethylolpropane triacrylate, di-(tert-butyl peroxy) phthalo 3.6 parts of acid ester, 55 parts of EPDM rubber, 60 parts of polyvinyl chloride, 20 parts of polyurethane, 80 parts of composite filler, 1 part of calcium stearate, 1.6 parts of barium stearate, and 1 part of zinc naphthenate.

Embodiment 2

[0017] A cable for a wind turbine generator proposed by the present invention includes: a cable core and a sheath layer coated on the outside of the cable core, and the raw materials of the sheath layer include by weight: 4 parts of antioxidant, isobutyl triethyl 3 parts of silicon oxide, 12 parts of plasticizer, 0.8 part of hexamethylolmelamine hexamethyl ether, 1 part of ethoxylated trimethylolpropane triacrylate, di-(tert-butyl peroxy) phthalo 2 parts of ester, 65 parts of EPDM rubber, 40 parts of polyvinyl chloride, 30 parts of polyurethane, 60 parts of composite filler, 2 parts of calcium stearate, 1.2 parts of barium stearate, 3 parts of zinc naphthenate.

[0018] The composite filling is prepared by the following process: stir heavy calcium carbonate, calcined hydrotalcite, and water, then grind, add propylene glycol to mix evenly, spray dry, add ammonium polyphosphate, and stir with water, adjust the pH of the system to 5.8-6.4, and ultrasonically , heat up and stir, f...

Embodiment 3

[0020] A kind of cable for wind turbine generator proposed by the present invention comprises: a cable core and a sheath layer coated on the outside of the cable core, and the raw materials of the sheath layer include by weight: 2.5 parts of antioxidant, isobutyl triethyl 4.5 parts of silicon oxide, 9 parts of plasticizer, 1.2 parts of hexamethylol melamine hexamethyl ether, 0.6 parts of ethoxylated trimethylolpropane triacrylate, di-(tert-butyl peroxy) phthalo 3 parts of ester, 58 parts of EPDM rubber, 55 parts of polyvinyl chloride, 22 parts of polyurethane, 75 parts of composite filler, 1.2 parts of calcium stearate, 1.5 parts of barium stearate, and 1.2 parts of zinc naphthenate.

[0021] Antioxidants include by weight: 1.5 parts of tris(2,4-di-tert-butylphenyl) phosphite, 2.5 parts of styryl-N-phenylaniline, 3,5-di-tert-butyl tetramethylene 1 part of base-4-hydroxyhydrocinnamate; the plasticizer includes by weight: 5 parts of polyurethane hot melt adhesive, 2 parts of hyd...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a cable used for wind turbine generators. The cable comprises a cable core and a sheath layer used for coating the external side of the cable core; the sheath layer comprises, by weight, 2 to 4 parts of an anti-oxidant, 3 to 5 parts of isobutyltriethoxysilane, 8 to 12 parts of a plasticizer, 0.8 to 1.4 parts of hexakis(methoxymethyl)melamine, 0.4 to 1 part of ethoxylated trimethylolpropane triacrylate, 2 to 3.6 parts of di(tert-butylperoxy)phthalate, 55 to 65 parts of ethylene-propylene-diene monomer rubber, 40 to 60 parts of polyvinyl chloride, 20 to 30 parts of polyurethane, 60 to 80 parts of a composite filler, 1 to 2 parts of calcium stearate, 1.2 to 1.6 parts of barium stearate, and 1 to 3 parts of zinc naphthenate. The thermal stability of the cable is excellent; mechanical properties are excellent; aging resistance at extreme environment is extremely excellent; safety performance is high; and self life is long.

Description

technical field [0001] The invention relates to the technical field of cables, in particular to a cable for a wind turbine generator. Background technique [0002] Judging from the growth of global wind power generation in the past two years, wind turbine generators may grow at a rate of more than 50% in the next few years. These conditions show that there is a space for vigorous development and promotion of wind power generation, and it is matched with wind power projects. There is a huge market demand for special cable sheathing materials used. Wind power generation projects are carried out in the open air, and the service life of the cable sheath material is required to be very long. This requires extremely high thermal stability, aging resistance and mechanical properties of the cable material for wind turbine generators in extreme environments. Ordinary The cable has poor crack resistance, low safety performance and short service life cycle. Contents of the invention...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L23/16C08L75/04C08L83/06C08K13/06C08K9/02C08K9/04C08K3/26C08K5/5419C08K5/053H01B3/44
CPCC08L27/06C08K2201/014C08L23/16C08L2201/02C08L2201/08C08L2203/202C08L2205/025C08L2205/035H01B3/443C08L75/04C08L83/06C08K13/06C08K9/02C08K9/08C08K9/04C08K3/26C08K5/5419C08K5/053
Inventor 夏泽坤夏江涛李莉
Owner 安徽省无为县经纬电缆附件有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products