Ceiling material and preparation method thereof

A technology of ceiling and polymer materials, applied in the field of building materials, to achieve the effect of purifying air, high tensile strength, and hard texture

Inactive Publication Date: 2017-09-08
肥西县碧涛建材有限公司
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the problems that existing ceiling materials still have many deficiencies in air purification, compression resistance, tensile resistance, thermal insulation and fire prevention, the purpose of the present invention is to provide a ceiling material and a preparation method thereof. The prepared ceiling material has Can purify air, high compressive strength, high tensile strength, good thermal insulation effect and good fireproof effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceiling material and preparation method thereof
  • Ceiling material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] A ceiling material, comprising the following raw materials in parts by weight: 65 parts of polyurethane polymer material, 12 parts of fly ash, 12 parts of ethyl stearate, 9 parts of palmitic acid, 3 parts of nano silicon dioxide, 3 parts of nano calcium carbonate , 12 parts of nano titanium dioxide, 8 parts of bamboo charcoal, 17 parts of zirconia, 15 parts of boron carbide, 6 parts of glass fiber, 7 parts of attapulgite, 16 parts of glass wool, 18 parts of aluminum silicate, 0.6 parts of heat stabilizer, light stabilizer 0.7 parts of agent, 0.5 parts of coupling agent, 0.4 parts of antioxidant and 0.6 parts of foaming agent.

[0047] Fly ash is added to the raw materials, and the fly ash is used as a filler of the ceiling material, which can improve the strength of the prepared ceiling material.

[0048] Nano-scale titanium dioxide is added to the raw material. Nano-scale titanium dioxide has the characteristics of sterilization, anti-fouling, deodorization, non-toxic ...

Embodiment 2

[0068] A ceiling material, comprising the following raw materials in parts by weight: 60 parts of polyurethane polymer material, 9 parts of fly ash, 10 parts of ethyl stearate, 5 parts of palmitic acid, 2 parts of nano silicon dioxide, 2 parts of nano calcium carbonate , 10 parts of nano titanium dioxide, 6 parts of bamboo charcoal, 15 parts of zirconia, 12 parts of boron carbide, 4 parts of glass fiber, 6 parts of attapulgite, 13 parts of glass wool, 12 parts of aluminum silicate, 0.3 parts of heat stabilizer, light stabilizer 0.5 parts of agent, 0.3 parts of coupling agent, 0.2 parts of antioxidant and 0.4 parts of foaming agent.

[0069] Fly ash is added to the raw materials, and the fly ash is used as a filler of the ceiling material, which can improve the strength of the prepared ceiling material.

[0070] Nano-scale titanium dioxide is added to the raw material. Nano-scale titanium dioxide has the characteristics of sterilization, anti-fouling, deodorization, non-toxic a...

Embodiment 3

[0090] A ceiling material, comprising the following raw materials in parts by weight: 70 parts of polyurethane polymer material, 15 parts of fly ash, 14 parts of ethyl stearate, 13 parts of palmitic acid, 4 parts of nano silicon dioxide, 4 parts of nano calcium carbonate , 14 parts of nano titanium dioxide, 10 parts of bamboo charcoal, 19 parts of zirconia, 18 parts of boron carbide, 8 parts of glass fiber, 8 parts of attapulgite, 19 parts of glass wool, 24 parts of aluminum silicate, 0.9 parts of heat stabilizer, light stabilizer 0.9 parts of agent, 0.7 parts of coupling agent, 0.6 parts of antioxidant and 0.8 parts of foaming agent.

[0091] Fly ash is added to the raw materials, and the fly ash is used as a filler of the ceiling material, which can improve the strength of the prepared ceiling material.

[0092] Nano-scale titanium dioxide is added to the raw material. Nano-scale titanium dioxide has the characteristics of sterilization, anti-fouling, deodorization, non-toxi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Relating to the field of building materials, the invention provides a ceiling material and a preparation method thereof. The ceiling material comprises the following raw materials by weight: a polyurethane polymer material, fly ash, ethyl stearate, palmitic acid, nano silica, nano calcium carbonate, nano titanium oxide, bamboo charcoal, zirconium oxide, boron carbide, glass fiber, attapulgite, glass wool, aluminum silicate, a heat stabilizer, a light stabilizer, a coupling agent, an antioxidant, and a foaming agent. The preparation method comprises the steps of: (1) weighing the raw materials, (2) preparing a mixture a, (3) preparing a mixture b, (4) preparing a mixture c, and (5) conducting molding in a die. The ceiling material prepared by the method provided by the invention has the advantages of air purification, high compressive strength, high tensile strength, good heat insulation effect and good fire prevention effect.

Description

technical field [0001] The invention belongs to the field of building materials, and in particular relates to a ceiling material and a preparation method thereof. Background technique [0002] Ceilings are used as interior roof decoration materials. In the past, straw mats, reed mats, and wooden boards were used as the main materials in traditional houses. With the advancement of technology, more building materials have been applied. [0003] In the process of interior decoration, toxic and harmful gases such as formaldehyde will be emitted, which cannot be removed in a short time and seriously endanger human health. [0004] However, the existing ceiling materials are not effective in purifying toxic and harmful gases such as formaldehyde, and in addition to the above-mentioned air purification performance, the ceiling materials also have many deficiencies in their basic fire prevention, heat preservation, compression resistance, and tensile properties. , also needs to be ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/02C04B26/16
CPCC04B26/16C04B2111/00025C04B2111/00603C04B2111/28C04B2111/40C04B2201/32C04B2201/50C04B18/08C04B24/045C04B24/04C04B14/062C04B14/28C04B14/305C04B14/022C04B14/306C04B14/323C04B14/42C04B14/102C04B14/041C04B22/10C04B24/42C04B38/02
Inventor 俞克波
Owner 肥西县碧涛建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com