Heat insulation coating for building and preparation method of heat insulation coating

A technology for thermal insulation coatings and buildings, applied in fire-resistant coatings, reflective/signal coatings, antifouling/underwater coatings, etc., can solve the problems of complex construction process, poor thermal insulation performance, high price, etc., to solve environmental pollution problems, Low moisture absorption and low bulk density

Inactive Publication Date: 2017-09-08
HEFEI YAKELI NEW BUILDING MATERIAL CO LTD
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the external wall insulation materials currently on the market have their own shortcomings, such as easy cracking, relatively poor thermal insulation performance, complicated construction technology and high prices.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A building thermal insulation coating, comprising the following raw materials:

[0029] 90 parts of styrene-acrylic emulsion;

[0030] 55 parts of glass wool;

[0031] 45 parts of short fiber;

[0032] 40 parts of thermoplastic expanded hollow microspheres;

[0033] 25 parts of nano aluminum silicate;

[0034] 20 parts of nano calcium carbonate;

[0035] 10 parts of nano titanium dioxide;

[0036] 10 parts of filler;

[0037] 10 auxiliaries;

[0038] 150 parts of water;

[0039] The auxiliary agent includes the following raw materials: 2 parts of antifreeze, 1 part of defoaming agent, 1 part of dispersant, 0.2 part of film-forming auxiliary, 0.2 part of leveling agent, 0.2 part of flame retardant and 0.2 part of coupling agent share.

[0040] Wherein, the solid content of the styrene-acrylic emulsion is 40%, and the minimum film-forming temperature is 1°C.

[0041] Wherein, the short fibers are zirconia crystal fibers.

[0042] Wherein, the thermoplastic expa...

Embodiment 2

[0052] A building thermal insulation coating, comprising the following raw materials:

[0053] 100 parts of styrene-acrylic emulsion;

[0054] 65 parts of glass wool;

[0055] 55 parts of short fiber;

[0056] 45 parts of thermoplastic expanded hollow microspheres;

[0057] 30 parts of nano aluminum silicate;

[0058] 25 parts of nano calcium carbonate;

[0059] 20 parts of nano titanium dioxide;

[0060] 20 parts of filler;

[0061] 15 parts of adjuvant;

[0062] 180 parts of water;

[0063] The auxiliary agent includes the following raw materials: 4 parts of antifreeze, 3 parts of defoaming agent, 2 parts of dispersant, 1.2 parts of film-forming auxiliary, 0.8 part of leveling agent, 0.6 part of flame retardant and 0.4 part of coupling agent share.

[0064] Wherein, the solid content of the styrene-acrylic emulsion is 60%, and the minimum film-forming temperature is 10°C.

[0065] Wherein, the short fibers are alumina crystal fibers.

[0066] Wherein, the thermoplas...

Embodiment 3

[0076] A building thermal insulation coating, comprising the following raw materials:

[0077] 95 parts of styrene-acrylic emulsion;

[0078] 60 pieces of glass wool;

[0079] 50 parts of short fiber;

[0080] 42 parts of thermoplastic expanded hollow microspheres;

[0081] 27 parts of nano aluminum silicate;

[0082] 23 parts of nano calcium carbonate;

[0083] 15 parts of nano titanium dioxide;

[0084] 15 parts of filler;

[0085] 12 parts of adjuvant;

[0086] 165 parts of water;

[0087] The auxiliary agent includes the following raw materials: 3 parts of antifreeze, 2 parts of defoaming agent, 1.5 parts of dispersant, 0.7 part of film-forming auxiliary, 0.5 part of leveling agent, 0.4 part of flame retardant and 0.3 part of coupling agent share.

[0088] Wherein, the solid content of the styrene-acrylic emulsion is 50%, and the minimum film-forming temperature is 6°C.

[0089] Wherein, the short fibers are mullite crystal fibers.

[0090] Wherein, the thermopl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
minimum film forming temperatureaaaaaaaaaa
Login to View More

Abstract

The invention discloses a heat insulation coating for a building and a preparation method of the heat insulation coating, and relates to the field of building materials. The heat insulation coating is prepared from the following raw materials in parts: 90 to 100 parts of styrene-acrylic emulsion, 55 to 65 parts of glass wool, 45 to 55 parts of short fiber, 40 to 45 parts of thermoplastic expanded hollow microspheres, 25 to 30 parts of nano aluminium silicate, 20 to 25 parts of nano calcium carbonate, 10 to 20 parts of nano titanium dioxide, 10 to 20 parts of a filler, 10 to 15 parts of an auxiliary and 150 to 180 parts of water. A coating film formed by the coating is good in heat insulation and preservation effect, high in bonding strength, difficult to crack and high in abrasion resistance; furthermore, the preparation method is scientific and simple; the energy consumption is greatly reduced; meanwhile, the heat insulation coating is free of pollution to the environment.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a building thermal insulation coating and a preparation method thereof. Background technique [0002] With the improvement of human's awareness of environmental protection, architectural coatings are developing from the past performance of protecting walls and decoration to multi-functional and green development. Building energy conservation has been paid more and more attention by the country in recent years. Thermal insulation coating is a very popular solution for building exterior wall thermal insulation in recent years. However, most of the exterior wall insulation materials currently on the market have their own shortcomings, such as easy cracking, relatively poor thermal insulation performance, complicated construction process and high price. SUMMARY OF THE INVENTION [0003] The purpose of the present invention is to provide a kind of building thermal insula...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D125/14C09D5/14C09D5/33C09D5/16C09D7/12C09D5/18
CPCC09D125/14C08K2003/2241C08K2003/265C08K2201/011C08L2201/02C08L2205/03C09D5/004C09D5/14C09D5/1662C09D5/1687C09D5/18C08L83/04C08K13/04C08K7/14C08K3/34C08K3/26C08K3/22C08K5/54C08K5/521
Inventor 王磊
Owner HEFEI YAKELI NEW BUILDING MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com