Novel material of abrasion-resistant tire and preparation method thereof

A new material and tire technology, applied in special tires, tire parts, chemical instruments and methods, etc., can solve problems such as poor wear resistance, reduce modulus and tensile strength, avoid large energy consumption, and reduce interface tension effect

Inactive Publication Date: 2017-09-19
河南颇文商贸有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The Chinese patent application number 201410145691.4 discloses a tire tread rubber composition and a preparation method thereof, including N234 carbon black, octyl soap salt and natural rubber, wherein the mass ratio of N234 carbon black: octyl soap salt: natural rubber is 40~60:1~5:100, the rubber compound has high strength and tear resistance, but poor wear resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A new wear-resistant tire material provided in this embodiment, the wear-resistant tire includes the following raw materials in parts by weight:

[0035] 85 parts of natural rubber, 12 parts of chlorohydrin rubber, 12 parts of alkali-free glass fiber, 8 parts of silicon dioxide, 21 parts of carbon black, 1 part of stearic acid, 18 parts of octyl oleate, 1 part of magnesium salt whisker, N- 12 parts of tert-butyl-2-benzothiazole sulfonamide, 0.08 parts of silane coupling agent, 3 parts of protective wax, 0.1 part of leveling agent,

[0036] The whisker diameter of the magnesium salt whisker is less than 1 μm, the alkali-free glass fiber is chopped fiber,

[0037] The leveling agent includes the following raw materials in parts by weight: 40 parts of sodium urealate polymer, 12 parts of hexamethylenetetramine, and 2.5 parts of sodium chloride.

[0038] Described magnesium salt whisker synthetic method is as follows:

[0039] Magnesium sulfate and magnesium hydroxide are...

Embodiment 2

[0049] A new wear-resistant tire material provided in this embodiment, the wear-resistant tire includes the following raw materials in parts by weight:

[0050] 50 parts of natural rubber, 28 parts of chlorohydrin rubber, 8 parts of alkali-free glass fiber, 23 parts of silicon dioxide, 7 parts of carbon black, 8 parts of stearic acid, 2 parts of octyl oleate, 9 parts of magnesium salt whiskers, N- 2 parts of tert-butyl-2-benzothiazole sulfonamide, 0.23 parts of silane coupling agent, 1 part of protective wax, 1.9 parts of leveling agent,

[0051] The whisker diameter of the magnesium salt whisker is less than 1 μm, the alkali-free glass fiber is chopped fiber,

[0052] The leveling agent includes the following raw materials in parts by weight: 30 parts of sodium urealate polymer, 15 parts of hexamethylenetetramine, and 1.8 parts of sodium chloride.

[0053] Described magnesium salt whisker synthesis method is as follows:

[0054] Magnesium sulfate and magnesium hydroxide are...

Embodiment 3

[0064] A new wear-resistant tire material provided in this embodiment, the wear-resistant tire includes the following raw materials in parts by weight:

[0065] 65 parts of natural rubber, 12 parts of chlorohydrin rubber, 11 parts of alkali-free glass fiber, 8 parts of silicon dioxide, 11 parts of carbon black, 5 parts of stearic acid, 18 parts of octyl oleate, 1 part of magnesium salt whisker, N- 12 parts of tert-butyl-2-benzothiazole sulfonamide, 0.08 parts of silane coupling agent, 2 parts of protective wax, 0.1 part of leveling agent,

[0066] The whisker diameter of the magnesium salt whisker is less than 1 μm, and the alkali-free glass fiber is chopped fiber,

[0067] The leveling agent includes the following raw materials in parts by weight: 30 parts of sodium urealate polymer, 14 parts of hexamethylenetetramine, and 1.8 parts of sodium chloride.

[0068] Described magnesium salt whisker synthesis method is as follows:

[0069] Magnesium sulfate and magnesium hydroxid...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of new materials, and provides a new wear-resistant tire material and a preparation method thereof. The wear-resistant tire comprises the following raw materials in parts by weight: 50-85 parts of natural rubber, 12-28 parts of chlorohydrin rubber, 8-12 parts of alkali-free glass fiber, 8-23 parts of silicon dioxide, 7-21 parts of carbon black, 1-8 parts of stearic acid, 2-18 parts of octyl oleate, 1-9 parts of magnesium salt whisker, N 2-12 parts of tert-butyl-2-benzothiazole sulfonamide, 0.08-0.23 parts of silane coupling agent, 1-3 parts of protective wax, 0.1-1.9 parts of leveling agent, the crystals of the magnesium salt whiskers The whisker diameter is less than 1 μm, the alkali-free glass fiber is chopped fiber, and the leveling agent includes the following raw materials in parts by weight: 30-40 parts of sodium urealate polymer, 12-15 parts of hexamethylenetetramine, Sodium chloride 1.8-2.5 parts. The above-mentioned raw materials are kneaded and heated to form new tire materials, and the Acron wear is between 0.18-0.24cm3, achieving the effect of improving wear resistance.

Description

technical field [0001] The invention belongs to the technical field of new materials, and in particular relates to a new material for wear-resistant tires and a preparation method thereof. Background technique [0002] The outermost layer of the tire is in contact with the road surface and has a pattern printed on the surface. It can make the tire have traction, buffer the impact and swing when driving, and prevent the cord layer from being cut and pierced. It is required to have high wear resistance, fatigue resistance, good aging resistance, high tensile strength, elasticity and toughness, and low heat generation during driving. [0003] The Chinese patent application number 201410145691.4 discloses a tire tread rubber composition and a preparation method thereof, including N234 carbon black, octyl soap salt and natural rubber, wherein the mass ratio of N234 carbon black: octyl soap salt: natural rubber is 40~60:1~5:100, the resulting rubber has high strength and tear ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L71/03C08L91/00C08K13/04C08K7/08C08K7/14C08K3/36C08K3/04C08K5/09C08K5/1515C08K3/16C08K5/05B60C1/00C01F5/00
CPCC08L7/00B60C1/0016C01F5/00C08L2205/035
Inventor 向晓霞
Owner 河南颇文商贸有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap