Colored zirconia ceramic

A zirconia ceramic and phase zirconia technology, which is applied in the field of ceramic materials, can solve the problems of damage, light surface coating color, increased cost of preparation equipment, etc., and achieve the effects of enhancing interface bonding, improving interface performance, and avoiding adverse effects.

Active Publication Date: 2017-10-13
HANGZHOU ERRAN TECH
View PDF20 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese patent CN101020607A and patent application No. 01119222.4 respectively report the method for preparing silver-white and golden zirconia ceramics by surface treatment, and CN102512256A reports the method for dyeing zirconia ceramics by using thin film, but the surface coating obtained by the similar surface treatment method Light in color, easily damaged during use
Chinese patents CN1566021 and CN102659401A report the method of preparing black and gray zirconia ceramics under graphite reducing atmosphere, but similar coloring methods need to be carried out under reducing or vacuum conditions
The disadvantage of similar methods is that due to the diversity of color requirements, the cost of preparation equipment is greatly increased

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example

[0035] 1.1. Example of the hydrothermal hydrolysis method for manufacturing cubic zirconia slurry with solid solution of one or more rare earth metal ions

example 1

[0036] Example 1: Zirconium oxychloride (ZrOCl with a concentration of 0.5-1mol / L 2 ·8H 2 O≥99%) solution, yttrium nitrate (Y(NO 3 ) 3 ·6H 2 O≥99.9%) solution, erbium nitrate (Er(NO 3 ) 3 ·5H2O≥99.9%) solution is added into the reactor; wherein the total amount of yttrium oxide is 2-6 mol% of the amount of zirconia, and erbium oxide is 5-8 mol% of the amount of zirconia. Heat the reactor to 40-60°C and keep it warm for 2-3 hours. After the added yttrium nitrate is completely dissolved, add 0.5-1wt% polyvinyl alcohol according to the weight of the solution, then heat it to 200-250°C and keep it warm for 55- The hydrothermal-hydrolysis reaction was carried out for 65 hours. Keep the internal pressure at 2-3MPa to gradually hydrolyze and precipitate. Use a centrifuge to separate quickly, vacuum filter the precipitate, wash with distilled water and ethanol, and obtain cubic ZrO in solid solution of rare earth erbium metal ions 2 Precursor. According to cubic ZrO 2 The qu...

example 2

[0037] Example 2: Erbium nitrate (Er(NO3) 3.5H2O≥99.9%) solution is replaced with praseodymium nitrate (Pr(NO3) in example 1 3 ) 3 9H 2 O≥99.9%), neodymium nitrate (Nd(NO 3 ) 3 9H 2 O≥99.9%), holmium nitrate (Ho(NO 3 ) 3 ·5H 2 O≥99.9%), cerium nitrate (Ce(NO 3 ) 3 ·6H 2 O≥99.9%), europium nitrate (Eu(NO 3 ) 3 ·6H 2 O≥99.9%), samarium nitrate (Sm(NO 3 ) 3 ·5H 2 O≥99.9%), thulium nitrate (Tm(NO 3 ) 3 ·5H 2 O≥99.9%), terbium nitrate (Tb(NO 3 ) 3 ·6H 2 (0≥99.9%) solution, or when nitrate is replaced by one or more of sulfate, chloride, citrate, acetate, acetate, oxalate, yellow, Cubic zirconia slurry in purple, light yellow, light yellow, rose red, orange, light green, tan.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a colored zirconia ceramic, which is composed of tetragonal phase zirconia serving as the main crystalline phase and cubic phase zirconia serving as a minor crystalline phase, or is composed of tetragonal phase zirconia serving as the main crystalline phase, cubic phase zirconia serving as a minor crystalline phase, and a transition metal oxide. The colored zirconia ceramic realizes coloring through a rare earth metal that is in a solid solution state in cubic phase zirconia crystal grains, or achieves coloring through a rare earth metal that is in a solid solution state in cubic phase zirconia crystal grains, and is assisted by the transition metal oxide provided transition metal for toning. According to the invention, coloring rare earth metal ions are in a solid solution state in cubic zirconia lattices, and have no influence to the stability of tetragonal zirconia; solid solution rare earth metal ions in cubic zirconia are mainly adopted for coloring, then the consumption of other transition metal oxide coloring materials can be reduced or even the coloring materials can be not used, thus reducing the influence of transition metal oxide coloring materials concentrated at crystal boundaries to sintering densification, and avoiding the adverse effect on material strength.

Description

technical field [0001] The invention relates to the technical field of ceramic materials, in particular to a colored zirconia ceramic. Background technique [0002] At present, colored zirconia ceramics are usually prepared by three methods. [0003] One is to sinter the white zirconia part to 50-60% of the theoretical density, soak it in a salt solution containing one or more transition metals and rare earth metal oxides, and then dry it and further sinter it. Coloring solution and porous zirconia product as described in patent CN104918900A. The coloring solution generally contains the first transition metal elements, such as Fe, Mn, etc., which can easily lead to uneven coloring; the first transition metal elements generally can only exist in the grain boundary; the coloring ions exist in the grain boundary, which will reduce dental oxidation. The light transmission of zirconium products, if the content of coloring ions present in the grain boundaries is high, may also r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/48C04B35/626
Inventor 沈志坚熊焰张杰李廷凯
Owner HANGZHOU ERRAN TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap