Graphene-MBI compound pre-dispersion rubber masterbatch and preparation method thereof

A technology of pre-dispersed masterbatch and graphene, applied in the field of graphene-MBI composite pre-dispersed masterbatch and its preparation, can solve problems such as affecting workers' health, uneven dispersion, flying, etc. The effect of improving dispersibility and solving dust pollution

Inactive Publication Date: 2017-10-17
NINGBO ACTMIX POLYMER
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When MBI is used in rubber production, there are dust flying and pollution problems. After inhalatio

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Graphene-MBI compound pre-dispersion rubber masterbatch and preparation method thereof
  • Graphene-MBI compound pre-dispersion rubber masterbatch and preparation method thereof
  • Graphene-MBI compound pre-dispersion rubber masterbatch and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The Graphene-MBI composite pre-dispersed masterbatch of embodiment one, its weight percentage is composed of: graphene 55%, 2-mercaptobenzimidazole 22%, vinyltriethoxysilane 3%, dioctyl adipate 2% ester, 1% triphenyl phosphate, 2% zinc stearate, 8% rubber matrix, 7% industrial white oil, the sum of the weight percentages of the above components is 100%; the rubber matrix is ​​composed of main rubber and processing aids , the main rubber is EPDM rubber, the processing aids are paraffin wax and pentaerythritol stearate, and the weight ratio of the main rubber, paraffin wax and pentaerythritol stearate is 4:1:1.

Embodiment 2

[0025] The Graphene-MBI composite pre-dispersed master batch of embodiment two, its percentage by weight consists of: graphene 57%, 2-mercaptobenzimidazole 24%, vinyltriethoxysilane 1%, dioctyl adipate 1% ester, 1% triphenyl phosphate, 1% zinc stearate, 7% rubber matrix, 8% industrial white oil; the rubber matrix is ​​composed of main rubber and processing aids, the main rubber is EPDM rubber and acrylic acid Ester rubber, processing aids are paraffin and pentaerythritol stearate.

Embodiment 3

[0026] The Graphene-MBI composite pre-dispersed masterbatch of embodiment three, its percentage by weight is composed of: graphene 60%, 2-mercaptobenzimidazole 15%, vinyltriethoxysilane 1%, dioctyl adipate 1% ester, 1% triphenyl phosphate, 3% zinc stearate, 10% rubber matrix, 9% industrial white oil; the rubber matrix is ​​composed of main rubber and processing aids, the main rubber is acrylate rubber and chlorohydrin rubber , The processing aids are paraffin wax and pentaerythritol stearate.

[0027] The preparation method of the listed Graphene-MBI composite pre-dispersed master batch of above-mentioned embodiment comprises the following steps:

[0028] (1) Accurately weigh each raw material required for preparing the masterbatch according to the proportioning ratio;

[0029] (2) Divide the processing aid into three parts; then put the main rubber into the internal mixer and knead for 2 minutes; then add 1 / 3 of the processing aid to the internal mixer and knead for 2 minute...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses graphene-MBI compound pre-dispersion rubber masterbatch which is composed of, by weight, 55-60% of graphene, 15-35% of 2-mercaptobenzimidazole, 1-4% of vinyl triethoxysilane, 1-2% of dioctyl adipate, 1-2% of triphenyl phosphate, 1-5% of zinc stearate, 7-15% of rubber matrix and 6-14% of industrial white oil, the weight percentage sum of components is 100%, the rubber matrix is composed of main rubber and a processing aid, the main rubber is at least one of EPDM rubber, styrene butadiene rubber, nitrile butadiene rubber, acrylate rubber and chlorohydrine rubber, and the processing aid is paraffin and pentaerythritol stearate. The rubber masterbatch contains two active ingredients including graphene and MBI, the problems of dispersity and dust pollution of graphene and MBI in rubber products can be solved effectively, the rubber masterbatch can promote rubber vulcanization and improve mechanical performance and aging performance when being used for producing vulcanized rubber subsequently.

Description

technical field [0001] The invention relates to the technical field of pre-dispersion and granulation of processing aids, in particular to a graphene-MBI composite pre-dispersion masterbatch and a preparation method thereof. Background technique [0002] Graphene is a new type of carbon material in which carbon atoms are closely packed in a two-dimensional plane to form a two-dimensional honeycomb lattice. Graphene is currently the thinnest but hardest nanomaterial in the world. It is almost completely transparent and only absorbs 2.3% of light; its thermal conductivity is 5300W / m K, much higher than that of diamond and carbon nanotubes; at room temperature, Its electron mobility reaches 15000cm 2 / V·s, much higher than that of carbon nanotubes and silicon crystals; its resistivity is about 10 -6 Ω·cm, excellent electrical conductivity, equivalent to some metals; it has a high specific surface area, the limit value can reach 2630m 2 / g. Due to the unique characteristics ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/16C08L33/04C08L91/06C08K13/02C08K3/04C08K5/37C08K5/5425C08K5/11C08K5/523C08K5/098C08J3/22C08L9/06
CPCC08L91/06C08J3/226C08J2309/06C08J2491/06C08L9/06C08L2205/025C08L2205/03C08L2205/035C08L23/16C08K13/02C08K3/04C08K5/378C08K5/5425C08K5/11C08K5/523C08K5/098C08L33/04C08L71/03
Inventor 连千荣谷建鹏赵永青
Owner NINGBO ACTMIX POLYMER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products