Super dispersant surface activation treatment nanometer carbon black reinforced HDPE water supply pipe material

A technology of surface activation treatment and water supply pipes, which is applied in the field of building materials, can solve the problems of HDPE polymers that are difficult to disperse uniformly, affect the strength of pipes, oxidation induction time and hydrostatic strength, easy to agglomerate and absorb moisture, etc., and achieve the improvement of oxidation resistance , strong coloring ability, and the effect of improving hydrostatic strength

Inactive Publication Date: 2017-10-24
ANHUI JIELANTE NEW MATERIAL CO LTD
View PDF1 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the production process of conventional HDPE water supply pipes, HDPE resin and black masterbatch are generally used for extrusion production, but due to the non-polarity and hydrophilicity of the surface of carbon black, it is easy to agglomerate and absorb moisture during processing and storage, resulting in HDPE It is difficult to disperse uniformly in the polymer, which obviously affects the strength, oxidation induction time and hydrostatic strength of the pipe.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Super dispersant surface activation treatment nanometer carbon black reinforced HDPE water supply pipe material
  • Super dispersant surface activation treatment nanometer carbon black reinforced HDPE water supply pipe material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] High-gloss HDPE water supply pipe raw material ratio: HDPE resin 90% and high-gloss black masterbatch 10%; high-gloss black masterbatch raw material ratio is HDPE resin 48%, treated nano-carbon black 38%, lubricant 5%, processing aids 3%, antioxidant 2% and light stabilizer 4%; The raw material ratio of nano carbon black after treatment is nano carbon black 81%, polyolefin hyperdispersant 10%, graft copolymer hyperdispersant 6% and Surfactant 3%.

[0025] Among them, the polyolefin hyperdispersant is a terminal polyisobutylene dispersant; the graft copolymer hyperdispersant is a water-soluble polymer dispersant; the lubricant is a polyolefin oligomer; the processing aid is a silane cross-linked polymer. Ethylene copolymer; antioxidant is hindered phenolic antioxidant; light stabilizer is benzotriazole ultraviolet absorber.

Embodiment 2

[0027] High-gloss HDPE water supply pipe raw material ratio: HDPE resin 95% and high-gloss black masterbatch 5%; high-gloss black masterbatch raw material ratio is HDPE resin 50%, treated nano-carbon black 40%, lubricant 2%, processing aids 3%, antioxidant 2% and light stabilizer 3%; the raw material ratio of nano carbon black after treatment is nano carbon black 85%, polyolefin hyperdispersant 10%, graft copolymer hyperdispersant 2% and Surfactant 3%.

[0028] Among them, the polyolefin hyperdispersant is a methyl methacrylate dispersant; the graft copolymer hyperdispersant is an emulsion dispersant; the lubricant is a silane coupling agent; the processing aid is a polyethylene graft copolymer; The antioxidant is a hindered amine antioxidant; the light stabilizer is a benzotriazole ultraviolet absorber.

Embodiment 3

[0030] High-gloss HDPE water supply pipe raw material ratio: HDPE resin 94% and high-gloss black masterbatch 6%; high-gloss black masterbatch raw material ratio is HDPE resin 51%, treated nano-carbon black 39%, lubricant 2%, processing aids 3%, antioxidant 1% and light stabilizer 4%; The raw material ratio of nano carbon black after treatment is nano carbon black 81%, polyolefin hyperdispersant 10%, graft copolymer hyperdispersant 6% and Surfactant 3%.

[0031] Among them, the polyolefin hyperdispersant is a methyl methacrylate dispersant; the graft copolymer hyperdispersant is a water-soluble polymer dispersant; the lubricant is a titanate coupling agent; the processing aid is methyl Acrylic esters; the antioxidant is a phosphite antioxidant; the light stabilizer is a benzotriazole ultraviolet absorber.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
melt flow indexaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention discloses a super dispersant surface activation treatment nanometer carbon black reinforced HDPE water supply pipe material. According to the present invention, the prepared high brightness black masterbatch has advantages of large specific surface area of nanometer carbon black, strong coloring ability, good light stability, and significant enhancement effect; and the strength, the oxidation degree and the hydrostatic strength of the HDPE water supply and drain pipe material prepared from the high brightness black masterbatch are significantly improved.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a nano-carbon black reinforced HDPE water supply pipe material treated with hyperdispersant surface activation. Background technique [0002] In the production process of conventional HDPE water supply pipes, HDPE resin and black masterbatch are generally used for extrusion production, but due to the non-polarity and hydrophilicity of the surface of carbon black, it is easy to agglomerate and absorb moisture during processing and storage, resulting in HDPE It is difficult to disperse uniformly in the polymer, which obviously affects the strength, oxidation induction time and hydrostatic strength of the pipe. Contents of the invention [0003] In order to solve the above problems, the present invention proposes a hyperdispersant surface activation treatment nano-carbon black reinforced HDPE water supply pipe. [0004] In order to realize the purpose of the present in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08K13/06C08K9/04C08K3/04C08J3/22B29B7/00B29B7/28B29C47/92B29L23/00B29C48/92
CPCC08L23/06B29B7/005B29B7/28B29C48/09B29C48/92B29C2948/92704B29L2023/22C08J3/226C08J2323/06C08J2423/06C08K2201/011C08L2201/08C08L2203/18C08L2205/025C08L2205/03C08L2205/035C08L2207/062C08K13/06C08K9/08C08K3/04
Inventor 汪进南刘俊峰汪燕飞
Owner ANHUI JIELANTE NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap