Repair mortar for concrete slab and preparation method

A technology for repairing mortar and concrete slabs, applied in the field of building materials, can solve problems such as poor compatibility of cement substrates, affecting the application of repair materials, and low bonding strength, and achieve good application value and prospects, good application value, and high The effect of bond strength

Inactive Publication Date: 2017-11-07
HEFEI GUANGMIN BUILDING MATERIAL CO LTD
View PDF5 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, polymer repair materials use various polymers as cementing materials, which have outstanding advantages such as high bonding strength, short curing time, and good durability, but have poor compatibility with cement substrates and high cost; polymer modification Repairing materials use polymers to modify cement-based materials. Although the compatibility between repairing materials and cement-based materials is improved to a certain extent, the cost is too high, which affects the application of this repairing material; the current inorganic repairing materials are generally Portland cement repair mortar has the advantages of high strength and good compatibility, but has the problems of high viscosity, poor workability, low bonding strength and poor aesthetics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] This embodiment relates to a repair mortar for concrete slabs and its preparation method;

[0028] The repair mortar for the concrete slab is prepared from the following components in parts by weight:

[0029] 75 parts of sulfoaluminate cement, 135 parts of quartz sand, 18 parts of heavy calcium powder, 22 parts of paste attapulgite clay, 15 parts of kaolin, 24 parts of polyacrylamide, 12 parts of polyvinyl alcohol, 1.6 parts of graphene, wood Sulfonate 1.3 parts, glass fiber 6 parts, defoamer 5 parts, early strength agent 0.3 parts.

[0030] Wherein, the paste-like attapulgite clay is a mixture obtained by adding water to the purified natural attapulgite clay, wherein the water content is 40% to 50%.

[0031] Among them, the accelerator includes calcium chloride, calcium nitrate, and calcium nitrite.

[0032] Among them, the defoamer is a high-carbon alcohol fatty acid ester compound.

[0033] The present invention prepares the method for concrete slab repair mortar...

Embodiment 2

[0041] This embodiment relates to a repair mortar for concrete slabs and its preparation method;

[0042] The repair mortar for the concrete slab is prepared from the following components in parts by weight:

[0043] 60 parts of sulfoaluminate cement, 100 parts of quartz sand, 10 parts of heavy calcium powder, 15 parts of paste-like attapulgite clay, 13 parts of kaolin, 22 parts of polyacrylamide, 5 parts of polyvinyl alcohol, 0.5 parts of graphene, wood Sulfonate 0.9 parts, glass fiber 5 parts, defoamer 3 parts, early strength agent 0.2 parts.

[0044] Among them, the paste-like attapulgite clay is a mixture obtained by adding water to the purified natural attapulgite clay, and the water content is 40%.

[0045] Among them, the accelerator includes calcium chloride, calcium nitrate, and calcium nitrite.

[0046] Wherein, the antifoaming agent is polyoxyethylene polyoxypropylene pentaerythritol ether.

[0047] The present invention prepares the method for concrete slab repa...

Embodiment 3

[0055] This embodiment relates to a repair mortar for concrete slabs and its preparation method;

[0056] The repair mortar for the concrete slab is prepared from the following components in parts by weight:

[0057] 88 parts of sulfoaluminate cement, 150 parts of quartz sand, 25 parts of heavy calcium powder, 30 parts of paste-like attapulgite clay, 18 parts of kaolin, 27 parts of polyacrylamide, 19 parts of polyvinyl alcohol, 2.6 parts of graphene, wood Sulfonate 2.2 parts, glass fiber 9 parts, defoamer 7 parts, early strength agent 0.4 parts.

[0058] Wherein, the paste-like attapulgite clay is a mixture obtained by adding water to the purified natural attapulgite clay, wherein the water content is 50%.

[0059] Among them, the accelerator includes calcium chloride, calcium nitrate, and calcium nitrite.

[0060] Wherein, the defoamer is a silicone powder defoamer.

[0061] The present invention prepares the method for concrete slab repair mortar, comprises the steps:

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
Login to View More

Abstract

The invention provides repair mortar for a concrete slab and a preparation method. The mortar is prepared from the following components: sulphate aluminium cement, quartz sand, heavy calcium powder, paste attapulgite, kaolin, polyacrylamide, polyvinyl alcohol, graphene, lignosulfonate, glass fiber, a defoaming agent and an early strength agent. The preparation method comprises the steps of firstly performing modification reaction on the polyacrylamide, the polyvinyl alcohol and the graphene, and then uniformly mixing a reaction product with the rest components in batches, thus obtaining the mortar. When the repair mortar provided by the invention is applied to the field of buildings, better compatibility to building concrete is realized, and mechanical properties of higher bonding strength and the like are also realized; furthermore, the repair mortar has the characteristics of construction easiness and good effect, and has better application value.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a repair mortar for concrete slabs and a preparation method thereof. Background technique [0002] Concrete and reinforced concrete are widely used in various fields as the main building materials. During the long-term use of concrete structures, they are affected by factors such as heavy loads, freeze-thaw cycles, chloride ion penetration, surface abrasion, and erosion of corrosive media. Many concrete structures have cracked, peeled, and hollowed out, which greatly affects the service life of the project. my country is one of the countries with frequent earthquakes. The earthquake has a very large damage to the existing concrete buildings, including civil buildings, concrete pavements, bridge decks, and concrete in industrial plants. The damage to mortar and concrete is naturally very serious. . For the concrete structures damaged in the earthquake, if the repair o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/06E04G23/02
CPCC04B28/06E04G23/0203C04B14/06C04B14/28C04B14/102C04B14/106C04B24/2652C04B24/2623C04B14/024C04B24/18C04B14/42C04B2103/50C04B22/124C04B22/085
Inventor 黄洋
Owner HEFEI GUANGMIN BUILDING MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products