Method for preparing graphene/ferric oxide composite material

A composite material and graphene technology, applied in chemical instruments and methods, alkali metal compounds, alkali metal oxides/hydroxides, etc., can solve problems such as harmfulness and water pollution, and achieve avoidance of agglomeration, good stability, and excellent Effect of photocatalytic degradation activity

Inactive Publication Date: 2017-12-29
张家港市思杰五金工具有限公司
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Organic dyes cause water pollution, so the remediation of the water environment has become an important issue in recent years. Organic dyes are widely used because of their wide range of uses, but most organic dyes are harmful to the human body. Therefore, it is urgent to develop an effective, Simple and environmentally friendly technology to purify water resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Preparation method of graphene / iron oxide composite material

[0019] (1), adding graphene oxide into a mixed solution of deionized water and ethanolamine, and ultrasonically dispersing at 25° C. for 2 hours, wherein the volume ratio of deionized water and ethanolamine is 4:1;

[0020] (2), PEG-10000, ferrous ammonium sulfate and hexamethylenetetramine are dissolved in mixed solution, wherein, graphene oxide: PEG-10000: ferrous ammonium sulfate: hexamethylenetetramine=100: 2:4:3;

[0021] (3), the mixed solution is placed in a sealed environment, and kept at 180°C for 20 hours;

[0022] (4) Washing and drying the reactant to obtain iron oxide magnetic nanoparticles.

[0023] The characterization results show that iron oxide nanoparticles are uniformly dispersed on the graphene layer, which effectively avoids the agglomeration of graphene, and the prepared graphene / iron oxide composite exhibits excellent photocatalytic degradation activity under ultraviolet light irrad...

Embodiment 2

[0025] Preparation method of graphene / iron oxide composite material

[0026] (1), adding graphene oxide into a mixed solution of deionized water and ethanolamine, and ultrasonically dispersing at 20° C. for 2 hours, wherein the volume ratio of deionized water and ethanolamine is 4:1;

[0027] (2), PEG-10000, ferrous ammonium sulfate and hexamethylenetetramine are dissolved in mixed solution, wherein, graphene oxide: PEG-10000: ferrous ammonium sulfate: hexamethylenetetramine=100: 2:4:3;

[0028] (3), the mixed solution is placed in a sealed environment, and kept at 200°C for 15 hours;

[0029] (4) Washing and drying the reactant to obtain iron oxide magnetic nanoparticles.

Embodiment 3

[0031] Preparation method of graphene / iron oxide composite material

[0032] (1), adding graphene oxide into a mixed solution of deionized water and ethanolamine, and ultrasonically dispersing at 25° C. for 2.5 hours, wherein the volume ratio of deionized water and ethanolamine is 3:1;

[0033] (2), PEG-10000, ferrous ammonium sulfate and hexamethylenetetramine are dissolved in mixed solution, wherein, graphene oxide: PEG-10000: ferrous ammonium sulfate: hexamethylenetetramine=100: 2:4:3;

[0034] (3), the mixed solution is placed in a sealed environment, and kept at 180°C for 20 hours;

[0035] (4) Washing and drying the reactant to obtain iron oxide magnetic nanoparticles.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing a graphene / ferric oxide composite material. The method comprises the following steps: (1) putting a mixed solution of deionized water and ethanol amine into graphene oxide, and performing ultrasonic dispersion; (2) dissolving PEG-10000, ammonium ferrous sulfate and hexamethylenetetramine into the mixed solution; (3) placing the mixed solution in a sealed environment, and keeping the temperature of 180-200 DEG C for 15-20 hours; and (4) washing and drying a reactant, thereby obtaining ferric oxide magnetic nano particles. The ferric oxide nano particles prepared by using the method are uniformly dispersed on a graphene layer, so that agglomeration of graphene is effectively avoided, and the prepared graphene / ferric oxide composite material is excellent in photocatalytic degradation activity under radiation of ultraviolet radiation, is good in stability, has ferromagnetic behaviors, and can be effectively separated from dyes under the action of external magnetic fields.

Description

technical field [0001] The application belongs to the technical field of wastewater treatment, and in particular relates to a preparation method of a graphene / iron oxide composite material. Background technique [0002] Organic dyes cause water pollution, so the remediation of the water environment has become an important issue in recent years. Organic dyes are widely used because of their wide range of uses, but most organic dyes are harmful to the human body. Therefore, it is urgent to develop an effective, Simple and environmentally friendly technology to purify water resources. [0003] Iron oxide is an important magnetic material, which has broad application prospects in adsorption, catalysis, lithium-ion batteries, sensors, and biomedicine. Contents of the invention [0004] The object of the present invention is to provide a kind of preparation method of graphene / iron oxide composite material, to overcome the deficiencies in the prior art. [0005] To achieve the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J20/30B01J20/20B01J20/28C02F1/28C02F1/30C02F1/48C02F101/30
CPCB01J20/06B01J20/20B01J20/28009B01J2220/4806B01J2220/4812C02F1/281C02F1/30C02F1/48C02F2101/308
Inventor 范佳晨
Owner 张家港市思杰五金工具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com