Antifouling light fireproof door
A technology for fire doors and fire door core panels, applied to fire doors, anti-fouling/underwater coatings, paints containing biocides, etc., can solve the problems of high fire stability and safety, personnel safety and property loss and other problems, to achieve excellent thermal and chemical stability, improve observation, and improve the effect of adhesion
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0018] An antifouling lightweight fireproof door, the core component of which is a fireproof door core plate, made of the following components in parts by weight: 40 parts of perlite, 20 parts of silicon carbide, 15 parts of diatomaceous earth, and 14 parts of butyl titanate , 10 parts of glass enamel powder, 10 parts of polypropylene resin, 13 parts of dichloromethane, 5 parts of methyl acrylate, 4 parts of N-methylol acrylamide, 2 parts of OP series emulsifier, 4 parts of copper iodide double salt, 1 part of sodium silicate, 25 parts of water, its preparation method comprises the following steps:
[0019] (1) Crush the perlite in the weight portion into 2mm particles, mix it with diatomaceous earth evenly, put it into a high temperature resistant expander, heat it to 1350°C at a heating rate of 30°C per minute, and maintain it for 20 minutes , slowly cooling down to obtain a hollow honeycomb-shaped particle sphere;
[0020] (2) Pass the silicon carbide powder into the hot i...
Embodiment 2
[0026] An antifouling lightweight fireproof door, the core component of which is a fireproof door core plate, which is made of the following components in parts by weight: 42 parts of perlite, 23 parts of silicon carbide, 17 parts of diatomaceous earth, and 15 parts of butyl titanate , 12 parts of glass enamel powder, 11 parts of polypropylene resin, 14 parts of dichloromethane, 6 parts of methyl acrylate, 5 parts of N-methylol acrylamide, 3 parts of OP series emulsifier, 5 parts of copper iodide double salt, 1.5 parts of sodium silicate, 28 parts of water, its preparation method comprises the following steps:
[0027] (1) Crush the perlite in the weight portion into 3mm particles, mix it with diatomaceous earth evenly, put it into a high temperature resistant expander, heat it to 1400°C at a heating rate of 40°C per minute, and maintain it for 23 minutes , slowly cooling down to obtain a hollow honeycomb-shaped particle sphere;
[0028] (2) Pass the silicon carbide powder in...
Embodiment 3
[0034] An antifouling lightweight fireproof door, the core component of which is a fireproof door core plate, made of the following components in parts by weight: 45 parts of perlite, 15 parts of silicon carbide, 20 parts of diatomaceous earth, and 16 parts of butyl titanate , 15 parts of glass enamel powder, 12 parts of polypropylene resin, 16 parts of dichloromethane, 8 parts of methyl acrylate, 6 parts of N-methylol acrylamide, 4 parts of OP series emulsifier, 6 parts of copper iodide double salt, 2 parts of sodium silicate, 30 parts of water, its preparation method comprises the following steps:
[0035] (1) Crush the perlite in the weight portion into 4mm particles, mix it with diatomaceous earth evenly, put it into a high temperature resistant expander, heat it to 1450°C at a heating rate of 50°C per minute, and maintain it for 25 minutes , slowly cooling down to obtain a hollow honeycomb-shaped particle sphere;
[0036] (2) Pass the silicon carbide powder into the hot is...
PUM
Property | Measurement | Unit |
---|---|---|
Compressive strength | aaaaa | aaaaa |
Flexural strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com