Preparation method of modified sericite powder
A technology of sericite powder and modification, which is applied in the field of preparation of sericite powder, can solve the problems of affecting the characteristics of sericite powder, agglomerate into agglomerates, poor dispersibility, etc., and achieves good wetting and dispersing effect, small particle size, and improved moisturizing effect. wet effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0016] Example one
[0017] The method for preparing modified sericite powder proposed by the present invention includes the following steps:
[0018] S1. Preparation of organic modification liquid: add lauryl alcohol polyoxyethylene ether, ethoxylated fatty acid methyl ester and sodium dodecyl benzene sulfonate into water, stir to dissolve, after all dissolved, ultrasonic defoaming, and then add in order The silane coupling agent is stirred and dissolved to obtain the organic modification solution for use;
[0019] S2. Take sericite powder and add 8 times the amount of the organic modification solution prepared in step S1, stir at 55°C for 30 minutes, and the stirring speed is 150r / min, after heating and stirring, transfer to a rocking shaker, shake for 30 minutes, and The amplitude is 20mm, the rotation speed is 300r / min, and then transferred to an ultrasonic instrument for ultrasonic 10min, and cooled to room temperature to obtain the sericite powder mixture;
[0020] S3. Centrifu...
Example Embodiment
[0023] Example two
[0024] The method for preparing modified sericite powder proposed by the present invention includes the following steps:
[0025] S1. Preparation of organic modification liquid: add lauryl alcohol polyoxyethylene ether, ethoxylated fatty acid methyl ester and sodium dodecyl benzene sulfonate into water, stir to dissolve, after all dissolved, ultrasonic defoaming, and then add in order The silane coupling agent is stirred and dissolved to obtain the organic modification solution for use;
[0026] S2. Take sericite powder and add 9 times the amount of the organic modification solution prepared in step S1, stir at 45°C for 30 minutes, and the stirring speed is 100r / min, after heating and stirring, transfer to a rocking shaker, shake for 30 minutes, and The amplitude is 20mm, the rotation speed is 200r / min, and then transferred to an ultrasonic instrument for ultrasonic 15min, and cooled to room temperature to obtain the sericite powder mixture;
[0027] S3. Centrifu...
Example Embodiment
[0030] Example three
[0031] The method for preparing modified sericite powder proposed by the present invention includes the following steps:
[0032] S1. Preparation of organic modification liquid: add lauryl alcohol polyoxyethylene ether, ethoxylated fatty acid methyl ester and sodium dodecyl benzene sulfonate into water, stir to dissolve, after all dissolved, ultrasonic defoaming, and then add in order The silane coupling agent is stirred and dissolved to obtain the organic modification solution for use;
[0033] S2. Take sericite powder and add 10 times the amount of the organic modification solution prepared in step S1, stir at 40°C for 30 minutes, and the stirring speed is 50r / min, after heating and stirring, transfer to a rocking shaker, shake for 40 minutes, and The amplitude is 20mm, the rotation speed is 100r / min, and then transferred to an ultrasonic instrument for 20 minutes of sonication, and cooled to room temperature to obtain the sericite powder mixture;
[0034] S3...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap