Chlorine-free low-melting-point thermoplastic gas generating agent and preparation method thereof

A gas generating agent, low melting point technology, applied in the production of compressed gas, attack equipment, explosives, etc., can solve the problems of low energy level, high burning rate and pressure index, achieve zero waste rate, improve the effect of intrinsic safety

Active Publication Date: 2018-01-30
HUBEI INST OF AEROSPACE CHEMOTECH
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, the disadvantages of chlorine-free low melting point thermoplastic g

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0040] Example 1

[0041] (1) Composition of non-chlorine low melting point thermoplastic fuel gas generator

[0042] Oxidizing agent (modified ammonium nitrate): 70%; cooling agent (ammonium oxalate): 10%; combustion regulator (chromium trioxide): 1%; binder (EVA420): 10%; plasticizer (decane Dioctyl acid): 7%; auxiliary (tris[1,-(2-methylaziridine)] phosphine oxide): 0.3%; auxiliary (silane coupling agent): 0.2%; auxiliary (N ,N-diphenyl-p-phenylenediamine): 1.2%; auxiliary (carbon black): 0.3%

[0043] (2) Performance of non-chlorine low melting point thermoplastic fuel gas generator

[0044] Specific impulse: 1848.06 N*s / kg; combustion temperature: 938.47 o C; characteristic speed: 1067.14 m / s; average molecular weight of fuel gas: 21.8 g / mol; melting point: 81.3 o C; Air volume: 1184.9 L / Kg; Residue content: 2.4%; Pressure index (3MPa~9MPa): 0.48

Example Embodiment

[0045] Example 2

[0046] (1) Composition of non-chlorine low melting point thermoplastic fuel gas generator

[0047] Oxidizer (modified ammonium nitrate): 72%; cooling agent (dihydroxyglyoxime): 10%; combustion regulator (chromium trioxide): 0.5%; combustion regulator (vanadium pentoxide): 1.5%; Adhesive (EVA420): 8%; plasticizer (acetyl triethyl citrate): 6%; auxiliary (alcoholamine complex): 0.2%; auxiliary (aluminate coupling agent): 0.6 %; additives (N,N-diphenyl-p-phenylenediamine): 0.5%; additives (carbon black): 0.7%

[0048] (2) Performance of non-chlorine low melting point thermoplastic fuel gas generator

[0049] Specific impulse: 1951.14 N*s / kg; combustion temperature: 1122.5 o C; characteristic velocity: 1213.18 m / s; average molecular weight of fuel gas: 22.3 g / mol; melting point: 82.1 o C; Air volume: 1152.0 L / Kg; Residue content: 2.5%; Pressure index (3MPa~9MPa): 0.51

Example Embodiment

[0050] Example 3

[0051] (1) Composition of non-chlorine low melting point thermoplastic fuel gas generator

[0052] Oxidizer (modified ammonium nitrate): 65%; cooling agent (dihydroxyglyoxime): 8%; cooling agent (calcium carbonate): 5%; combustion regulator (vanadium pentoxide): 0.4%; combustion regulator (Ferric oxide): 0.6%; adhesive (EVA420): 9%; plasticizer (acetyl triethyl citrate): 6%; plasticizer (mineral oil): 2%; additives (three [1,-(2-methylaziridine)] phosphine oxide): 0.4%; auxiliary (aluminate coupling agent): 1.2%; auxiliary (N,N-diphenyl-p-phenylenediamine) :1.8%; additives (carbon black): 0.6%

[0053] (2) Performance of non-chlorine low melting point thermoplastic fuel gas generator

[0054] Specific impulse: 1746.92 N*s / kg; combustion temperature: 915.49 o C; characteristic speed: 1008.94 m / s; average molecular weight of fuel gas: 23.1 g / mol; melting point: 82.5 o C; Air volume: 1072.5 L / Kg; Residue content: 2.61%; Pressure index (3MPa~9MPa): 0.54

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Melting pointaaaaaaaaaa
Gas outputaaaaaaaaaa
Melting pointaaaaaaaaaa
Login to view more

Abstract

The invention provides a chlorine-free low-melting-point thermoplastic gas generating agent and a preparation method thereof. The chlorine-free low-melting-point thermoplastic gas generating agent comprises the following components in percentages by mass: 60 to 80% of an oxidant, 1 to 20% of a cooling agent, 1 to 3% of a combustion regulator, 5 to 10% of a low-melting-point thermoplastic resin adhesive, 1 to 5% of an auxiliary agent and 1 to 10% of a plasticizer. The thermoplastic gas generating agent prepared by using the method provided by the invention is free of metal powder, has a low combustion temperature, has clean gas, and overcomes the disadvantage that a large amount of hydrogen chloride generated in combustion products causes air pollution due to application of ammonium perchlorate in a conventional gas generating agent. The thermoplastic gas generating agent provided by the invention can realize melt-mixing at a low temperature (less than 90 DEG C), greatly improves the preparation safety of a thermoplastic propellant, can realize continuous production and repeated processing of waste products, and reduces production cost.

Description

technical field [0001] The invention relates to a chlorine-free low-melting thermoplastic gas generating agent for gas generators and other gas generators, belonging to the field of composite solid propellants. Background technique [0002] Ammonium perchlorate (AP) has the advantages of high oxygen balance, wide range of sources and low price. As a cost-effective oxidant, it has been widely used in the field of gas generating agents. Usually, the mass fraction in gas generating agents can be It reaches about 70%, but the gas generating agent containing AP will produce a large amount of hydrogen chloride (HCl) gas during the combustion process, which will cause air pollution and damage the ozone layer when discharged into the atmosphere, and combine with moisture in the air to produce acid mist Or acid rain, which causes serious damage to human beings and nature. With the gradual enhancement of people's awareness of environmental protection, chlorine-free gas generators have...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C06B31/28C06D5/00
Inventor 刘轩鲁国林乔应克李志勇
Owner HUBEI INST OF AEROSPACE CHEMOTECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap