Preparation method of automobile filter paper emulsion
A technology of emulsion and filter paper, which is applied in the field of preparation of automobile filter paper emulsion, can solve the problems that cannot meet the requirements of filter element production, processing and use, and low strength, and achieve excellent emulsification performance, high cross-linking degree, and good chemical and mechanical properties. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0016] Example 1
[0017] To 80g of isopropanol solution, at a stirring speed of 300r / min, add 8g of a mixture of ethyl acrylate, n-butyl acrylate and isooctyl acrylate, 8g of a mixture of AMPS and sodium allyl sulfonate, acrylic acid 4g of a mixture of hydroxyethyl and hydroxypropyl methacrylate, adjust the temperature to 80°C, add 0.1% azobisisoheptonitrile by mass to the total monomer content, keep the temperature for 120 minutes, and complete the preparation under high temperature and high vacuum conditions. The solvent was distilled off from the bottom to prepare a 10% aqueous solution; in the first step, 20g of a polymer emulsifier aqueous solution was prepared, heated to 90°C, and 98.03g of a mixture of styrene, acrylic acid, n-butyl acrylate and methyl methacrylate was added dropwise ; The mixture of silane coupling agent KH-570 and SG-SI171 1.87g and ammonium persulfate initiator accounting for 0.05% of the total monomer content, drip the reaction for 180 min, drip to co...
Example Embodiment
[0018] Example 2
[0019] To 80g isopropanol solution, at a stirring speed of 200r / min, add 6g of a mixture of isooctyl acrylate, n-butyl acrylate and lauryl acrylate, AMPS, sodium styrene sulfonate and sodium allyl sulfonate 12g of mixed material of hydroxyethyl acrylate and 2g of hydroxyethyl methacrylate, adjust the temperature to 70°C, add 0.3% azobiscyclohexylcarbonitrile by mass to the total monomer content, keep the temperature for 300min and complete the preparation , Distill off the solvent under high temperature and high vacuum conditions, and prepare a 10% aqueous solution; use the first step to prepare 100g of the polymer emulsifier aqueous solution, raise the temperature to 80℃, and add methyl methacrylate, ethyl methacrylate and propylene dropwise Mixture of nitrile, lauryl acrylate, 2-ethylhexyl acrylate, lauryl methacrylate and n-octyl methacrylate 46.3g; mixture of methylol acrylamide and silane coupling agent KH-570 3.7 g and 0.3% of the total monomer content o...
Example Embodiment
[0020] Example 3
[0021] To 80g isopropanol solution, at a stirring speed of 100r / min, add 6g of ethyl acrylate and n-butyl acrylate mixture, 8g of AMPS and sodium allyl sulfonate mixture, 6g of hydroxyethyl acrylate, Adjust the temperature to 90°C, add 0.5% dimethyl azobisisobutyrate with a mass of the total monomer content, keep the reaction for 240 minutes, and complete the preparation. The solvent is evaporated under high temperature and high vacuum conditions to prepare a 10% aqueous solution; The first step is to prepare 150g of a polymer emulsifier aqueous solution, heat to 80°C, and add dropwise a mixture of styrene, methyl methacrylate, acrylonitrile, butyl acrylate, lauryl acrylate and 2-ethylhexyl acrylate 45.5 g, 4.5g of a mixture of methylol acrylamide and silane coupling agent SG-SI151 and a potassium persulfate initiator accounting for 0.1% of the total monomer content, drip the reaction for 180 minutes, and complete the insulation reaction for 120 minutes, and th...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap