Hydroxyl compound type composite foaming agent and preparation method thereof

A technology of compound foaming agent and hydroxyl compound, applied in the field of foaming agent, can solve the problems of poor foam uniformity, single foaming agent, poor foaming power, etc., achieve uniform foaming diameter, improve stability, and reduce repulsion force effect

Active Publication Date: 2018-04-24
GUANGDONG SHENGRUI TECH CO LTD
View PDF6 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The first three generations of foaming agents have problems such as poor foaming power, poor stability, and poor foam uniformity. In order to solve the shortcomings of a single foaming agent, it is necessary to conduct compound foaming agent research by compounding multiple components.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydroxyl compound type composite foaming agent and preparation method thereof
  • Hydroxyl compound type composite foaming agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0057] As a preferred technical solution of the present invention, the preparation method of the polyether polyol at least comprises the following steps:

[0058] (1) Raw material pretreatment: slowly pour propylene oxide into a 500mL glass bottle, cover the lid immediately, place the molecular sieve in a muffle furnace at 500°C for 5 hours, and take it out after natural cooling in the furnace; put 30 Molecular sieves are put into propylene oxide to remove trace moisture contained therein; the remaining molecular sieves are stored in sealed bags, and the sealed bags are placed in a vacuum desiccator for subsequent use; three (2-hydroxyethyl) isocyanide Urate ester (THERIC) and double metal cyanide coordination catalyst (DMC) were placed in an oven at 60°C for 60 minutes to remove moisture;

[0059] (2) At 25°C, put 1.0-5.0g THERIC and 0.001-0.01g DMC in a 250mL small steel bottle equipped with a rotor, and vacuum dry at 60°C for 2 hours;

[0060] (3) After the small steel cyl...

Embodiment 1

[0104] Embodiment 1 provides a kind of hydroxyl compound type composite blowing agent, and its preparation raw material comprises by weight:

[0105] Nonionic surfactant: 15 parts,

[0106] Anionic surfactant: 3 parts,

[0107] Foam stabilizer: 1.5 parts,

[0108] Thickener: 0.8 parts,

[0109] Water: 79.7 parts;

[0110] The nonionic surfactant is a mixture of polyether polyol and lignin polyether polyol, the mass ratio of polyether polyol and lignin polyether polyol is 1:2; the anionic surfactant is dodecane The mixture of base anionic surfactant and N-lauroyl sarcosinate, the mass ratio of dodecyl anionic surfactant and N-lauroyl sarcosinate is 1.5:1; the lauryl Anionic surfactants are sodium dodecyl alcohol polyoxyethylene ether sulfate, ammonium lauryl sulfate, potassium salt of dodecyl phosphate, triethanolamine dodecyl phosphate, and the dodecyl Alcohol polyoxyethylene ether sodium sulfate, ammonium lauryl sulfate, potassium dodecyl phosphate, and triethanolamine d...

Embodiment 2

[0129] Embodiment 2 provides a kind of hydroxyl compound type composite blowing agent, and its preparation raw material comprises by weight:

[0130] Nonionic surfactant: 15 parts,

[0131] Anionic surfactant: 3 parts,

[0132] Foam stabilizer: 1.5 parts,

[0133] Thickener: 0.8 parts,

[0134] Water: 79.7 parts;

[0135] The nonionic surfactant is a mixture of polyether polyol and lignin polyether polyol, the mass ratio of polyether polyol and lignin polyether polyol is 1:2; the anionic surfactant is dodecane The mixture of base anionic surfactant and N-lauroyl sarcosinate, the mass ratio of dodecyl anionic surfactant and N-lauroyl sarcosinate is 1.5:1; the lauryl Anionic surfactants are sodium dodecyl alcohol polyoxyethylene ether sulfate, ammonium lauryl sulfate, potassium salt of dodecyl phosphate, triethanolamine dodecyl phosphate, and the dodecyl Alcohol polyoxyethylene ether sodium sulfate, ammonium lauryl sulfate, potassium dodecyl phosphate, and triethanolamine d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a foaming agent, specifically to a hydroxyl compound type composite foaming agent and a preparation method thereof. The hydroxyl compound type composite foaming agent at leastcomprises the following preparation raw materials in parts by weight: 2 to 20 parts of a nonionic surfactant, 1 to 5 parts of an anionic surfactant, 0.1 to 5 parts of a foam stabilizer, 0.5 to 1 partof a thickening agent and 69 to 96.4 parts of water, wherein the nonionic surfactant is one ore more selected from the group consisting of polyether polyol and lignin polyether polyol; and the anionic surfactant is one or more selected from the group consisting of a dodecyl anionic surfactant, lauryl sulfate triethanolamine, secondary alkyl sodium sulfonate, fatty alcohol sodium hydroxyethyl sulfonate, N-sodium lauroyl sarcosine, amide polyoxyethylene ether magnesium sulfate, dodecanol polyoxyethylene ether disodium sulfosuccinate, sodium alpha-olefin sulfonate, sodium fatty alcohol ether sulfate, sulfonates of ethoxylated fatty acid methyl ester, alcohol ether carboxylate, methyl stearate polyoxyethylene ether sodium sulfonate and isooctyl phosphate.

Description

technical field [0001] The invention relates to a foaming agent, in particular to a hydroxyl compound compound foaming agent and a preparation method thereof. Background technique [0002] With the reform of wall materials and the implementation of building energy-saving policies in my country, the development and application of energy-saving building materials have received extensive attention. The country has vigorously developed new materials such as energy-saving, waste utilization, heat preservation, light weight, and heat insulation. Among them, foam concrete blocks occupy an important position in non-load-bearing wall materials. Foamed concrete has many advantages such as light weight, heat insulation, sound insulation and fire resistance, and good seismic performance. It has been widely used abroad, and it has developed rapidly in China in recent years. Foam concrete is usually made by mechanically preparing foaming agent aqueous solution into foam, and then adding ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B24/32C04B103/42
CPCC04B40/0039C04B2103/42C04B24/32C04B24/161C04B24/16C04B24/003C04B24/123C04B2103/48C04B2103/44C04B22/002
Inventor 陈忠平汪建斌马元锦陈俊霖詹云霞张凯李希贤
Owner GUANGDONG SHENGRUI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More