A technology of water-based alkyd resin and wood products, applied in the field of coatings, can solve problems such as water resistance, poor toughness, health hazards, and many harmful substances, and achieve good toughness, good compatibility, and excellent mechanical properties.

Inactive Publication Date: 2018-04-24
合肥林邦门业有限公司
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are many harmful substances in the construction process of the product, which will cause certain harm to people's health. With the in-depth reform of environmental protection regulations, the requirements for surface coatings of wood products are becoming more and more stringent. Water-based wood coatings do not contain solvent-based organic volatiles. Advantages, the share in the coatings industry is gradually increasing
At present, the biggest problem of water-based alkyd resin coatings is the shortcomings of water resistance and poor toughness, which need to be improved urgently

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A water-based alkyd resin coating for the surface of wood products, its raw materials include: 80g of film-forming substance, 2g of tetraethylenepentamine, 0.2g of pyrenediamine, 5g of microcrystalline cellulose compound, 2g of calcined kaolin, vermiculite powder 5g, glass fiber 1g, pigment 10g, magnesium oxide 1g, antibacterial agent 2g, antifungal agent 1g, defoamer 2g, wetting agent 1g, oxidized polyethylene wax 22g, water 80g.

[0017] The film-forming substances include: 80 g of water-based alkyd resin and 15 g of water-based acrylic resin. The pigments include: 4g of ferric oxide, 1g of iron oxide yellow, and 4g of lithopone.

[0018] The microcrystalline cellulose composite is prepared by the following process: mix 10g of microcrystalline cellulose, 0.8g of maleic anhydride, and 60g of water evenly, add 6g of sulfuric acid solution with a concentration of 2wt%, heat up to 115°C and reflux for 20min, add 0.8g of disproportionated Rosin, 10g of polyethylene glycol...

Embodiment 2

[0020] A kind of waterborne alkyd resin coating that is used on the surface of wooden products, its raw material comprises: 90g of film-forming substance, 1g of tetraethylenepentamine, 0.6g of pyrene diamine, 1g of microcrystalline cellulose compound, 8g of calcined kaolin, vermiculite powder 1g, glass fiber 5g, pigment 4g, magnesium oxide 2g, antibacterial agent 1g, antifungal agent 2g, defoamer 1g, wetting agent 2g, oxidized polyethylene wax 15g, water 160g.

[0021] The film-forming substances include: 40 g of water-based alkyd resin and 35 g of water-based acrylic resin. The pigments include: 2g of ferric oxide, 2g of iron oxide yellow, and 1g of lithopone.

[0022] The microcrystalline cellulose composite is prepared by the following process: mix 20g of microcrystalline cellulose, 0.2g of maleic anhydride, and 100g of water evenly, add 2g of sulfuric acid solution with a concentration of 3.5wt%, heat up to 105°C and reflux for 40min, add 0.2g Disproportionated rosin, 20g...

Embodiment 3

[0024] A kind of water-based alkyd resin coating that is used on the surface of wooden products, its raw material comprises: 82g of film-forming substance, 1.8g of tetraethylenepentamine, 0.3g of pyrene diamine, 4g of microcrystalline cellulose compound, 4g of calcined kaolin, leech Stone powder 4g, glass fiber 2g, pigment 8g, magnesium oxide 1.2g, antibacterial agent 1.7g, antifungal agent 1.4g, defoamer 1.8g, wetting agent 1.3g, oxidized polyethylene wax 20g, water 100g.

[0025] The film-forming substances include: 70g of water-based alkyd resin and 20g of water-based acrylic resin. The pigments include: 3.5g of ferric oxide, 1.2g of iron oxide yellow, and 3g of lithopone.

[0026] The microcrystalline cellulose composite is prepared by the following process: mix 12g microcrystalline cellulose, 0.6g maleic anhydride, and 70g water evenly, add 5g sulfuric acid solution with a concentration of 2.5wt%, heat up to 112°C and reflux for 25min, add 0.6g Disproportionated rosin, 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a waterborne alkyd resin coating for a wooden product surface, which is prepared from, by weight, 80-90 parts of film forming substance, 1-2 parts of tetraethylenepentamine, 0.2-0.6 part of phenylenediamine, 1-5 parts of microcrystalline cellulose composite, 2-8 parts of calcined kaolin, 1-5 parts of vermiculite powder, 1-5 parts of glass fiber, 4-10 parts of pigment, 1-2 parts of magnesium oxide, 1-2 parts of antibacterial agent, 1-2 parts of mildew preventive, 1-2 parts of antifoaming agent, 1-2 parts of wetting agent, 15-22 parts of oxidized polyethlene wax, and 80-160 parts of water. The waterborne alkyd resin coating for the wooden product surface has good coating fullness, high hardness, good flexibility, and good waterproof and anti-scratching performance; moreover, the coating is featured by low VOC value and sticky resistance; meanwhile, the cost is low.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a water-based alkyd resin coating used on the surface of wood products. Background technique [0002] In the product composition of wood coatings in my country, solvent-based products still occupy an important position. However, there are many harmful substances in the construction process of the product, which will cause certain harm to people's health. With the in-depth reform of environmental protection regulations, the requirements for surface coatings of wood products are becoming more and more stringent. Water-based wood coatings do not contain solvent-based organic volatiles. Advantages, the share in the coatings industry is gradually increasing. At present, the biggest problem of waterborne alkyd resin coatings is the shortcomings of water resistance and poor toughness, which need to be improved urgently. Contents of the invention [0003] Based on the technical prob...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/08C09D133/00C09D7/61C09D7/63C09D7/65
CPCC09D167/08C08K2003/222C08L2205/035C08L1/04C08L23/30C08L71/02C08L5/08C08L93/04C08K13/04C08K7/14C08K3/22C08K3/34C08K3/346
Inventor 袁中领
Owner 合肥林邦门业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap