A nanofiber and electrode technology, which is applied in the field of synthetic self-supporting flexible electrodes, can solve problems such as nanofiber cracking and composite electrodes not showing flexibility, and achieve the effects of reducing production costs, improving area specific capacitance, and reducing reduction

Active Publication Date: 2020-06-23
NANYANG TECH UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the produced composite electrodes did not exhibit flexibility and suffered from cracking of the nanofibers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nanofiber electrodes and supercapacitors
  • Nanofiber electrodes and supercapacitors
  • Nanofiber electrodes and supercapacitors

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0126] Example 1: V 0.07 Mo 0.93 o 3 nH 2 O Polymerization of nanofiber paper

[0127] Polypyrrole-V 0.07 Mo 0.93 o 3 nH 2 The fabrication process of O nanofiber mixed paper (Ppy-VM NHP) electrode is as follows: figure 1 shown.

[0128] First, after using as reaction solvent H 2 o 2 In solution, V was synthesized under hydrothermal conditions 0.07 Mo 0.93 o 3 nH 2 O nanofibers. The resulting solution was then subjected to vacuum filtration (Whatman filter paper) to obtain V 0.07 Mo 0.93 o 3 nH 2 O nanofiber paper (VM NP). The filtration process or system is a vertical filtration flow system in which filter bottles with barbed side arms are used. A filter membrane is placed on top of the bottle. A vacuum pump is then attached to the side arm, and the solution is filtered through the membrane to obtain nanofiber paper. Soak the produced VMNP electrode in HNO 3 medium (to completely oxidize the nanofibers) and dry at room temperature. Although the as-prepa...

Embodiment 2

[0130] Example 2: MoO doped with 10 wt% vanadium 3 Nanofiber paper (V 0.07 Mo 0.93 o 3 nH 2 O nanofiber paper)

[0131] Before and after providing polypyrrole, V 0.07 Mo 0.93 o 3 nH 2 The transverse and cross-sectional views of field emission scanning electron microscopy (FESEM) micrographs of O nanofibrous paper are shown in Figures 3A to 3D middle. Figure 3A The wrinkling and bending features associated with nanofiber paper are shown. This is similar to the curved surface obtained by conventional reduced graphene oxide self-supporting paper. To facilitate the interaction of electrolyte ions with the electrode material surface, the presence of wrinkled or wavy features is required. Even after the polymerization of the pyrrole monomer, it was found that the surface of the nanofiber paper did not change, as Figure 3B shown. Cross-sectional FESEM analysis showed that by V 0.07 Mo 0.93 o 3 nH 2 Self-supporting flexible paper electrodes made of O nanofibers com...

Embodiment 3

[0133] Example 3: Mechanical flexibility of Ppy-VM NHPs

[0134] To examine the mechanical properties of Ppy-VM NHP electrodes, their Young's modulus and tensile strength were analyzed by dynamic mechanical analysis (DMA), as Figure 4 shown. Examining the behavior of the Ppy-VM NHP electrode under tensile stress by stress / strain curves (see also Figure 4 ). In the stress / strain curves, the mechanical response (stress / strain) of VM NP and Ppy-VM NHP electrodes can be divided into three parts, namely the initial loading state (E I - volumetric deformation region, represented by points at / close to the beginning of the curve), straightening state (E s - rearrangement region, without any points) and linear elastic state (E E – Regions of bond breakage and deformation, represented by points near / towards the end of the curve).

[0135] In the initial loading state, the Young's modulus of Ppy-VM NHP was found to be lower than that of VM NP, which indicated that the ease of defo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

According to the present invention, a method for synthesizing a self-supporting flexible electrode is provided. The method includes mixing a solution containing molybdenum powder, vanadium powder and hydrogen peroxide to form a solution of formula V 0.07 Mo 0.93 O 3 nH 2 a mixture comprising nanofibers represented by O, filtering the mixture to form an electrode comprising nanofibers; treating the electrode with an acidic solution; contacting the acid-treated electrode with a solution comprising a monomer of a conductive polymer; and The monomers are polymerized in a medium containing an oxidizing agent to form the conductive polymer. According to the present invention, a self-supporting flexible electrode is also provided, which includes nanofibers composed of molybdenum, vanadium and conductive polymers, wherein the electrode is composed of formula X-V 0.07 Mo 0.93 O 3 nH 2 O means. In this formula, X is a conductive polymer, and n is independently 1 or 2. According to the invention there is also provided a memory device comprising an electrode as defined above.

Description

[0001] Cross References to Related Applications [0002] This application claims priority from Singapore Patent Application No. 10201504975T filed on 23 June 2015, the entire contents of which are hereby incorporated by reference for all purposes. technical field [0003] The present invention relates to a method for synthesizing self-supporting flexible electrodes. The invention also relates to electrodes produced according to the methods described herein. Background technique [0004] In recent years, great efforts have been made to fabricate flexible planar electrodes for supercapacitors to meet the emerging modern electronics industry and its demands. [0005] The feasibility of carbon-based materials and their derivatives as flexible and self-supporting electrode materials has been extensively investigated. For example, carbon nanotubes (CNTs) have been introduced to form self-supporting and flexible electrode materials. However, these carbon nanotubes tend to disper...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01G9/042C01G31/02C01G39/02
CPCC01G39/02H01G9/042C01P2002/50C01P2002/54C01P2002/72C01P2002/82C01P2004/16H01G11/30H01G11/24H01G11/86Y02E60/13C01G31/02C08L45/00C08L79/02C08L2203/20H01G11/36
Inventor 威坪·库马尔李佩诗
Owner NANYANG TECH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com