Water-based composite resin composition, water-based plastic paint and preparation method of water-based plastic paint

A composite resin and composition technology, used in coatings, anti-corrosion coatings, polyurea/polyurethane coatings, etc., can solve problems such as poor scratch resistance, too slippery, and poor adhesion

Active Publication Date: 2018-06-22
WANHUA CHEMICAL (NINGBO) CO LTD +2
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, organic or inorganic matting powder has a rough or too slippery feel, poor compatibility with the main film-forming resin, poor wear resistance, poor scratch resistance, and poor chemical resistance.
[0004] Pure water-based large particle size self-dulling polyurethane resin has extremely low matteness and excellent black haze. It does not need to add any matting agent in the system, and the products obtained by using it have a good suede and soft touch, and have great application prospects in plastic products. , however, it also has certain defects, such as poor adhesion, poor scratch resistance, poor wear resistance, which limits its application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based composite resin composition, water-based plastic paint and preparation method of water-based plastic paint
  • Water-based composite resin composition, water-based plastic paint and preparation method of water-based plastic paint
  • Water-based composite resin composition, water-based plastic paint and preparation method of water-based plastic paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0090]Water-based plastic paint consists of component A and component B. Wherein, the formulation weight parts of component A and component B are composed as follows:

[0091] Component A

[0092]

[0093] Component B

[0094] 5;

[0095] in, It is a water-based large particle size polyurethane resin, and its main raw materials include hexamethylene diisocyanate, 4,4'-dicyclohexylmethane diisocyanate, polytetrahydrofuran ether diol, polycaprolactone diol, MPEG1200, N-( 2-Aminoethyl)-2-aminoethanesulfonate, N-(2-hydroxyethyl)ethylenediamine and isophoronediamine.

[0096] It is a water-based acrylic resin, and its main raw materials include styrene, methyl methacrylate, and tetrahydrofuran acrylate.

[0097] The manufacturing method of water-based plastic paint is:

[0098] The preparation method of component A: In the dispersing barrel, start the dispersing machine, adjust the speed at 300-500 rpm, and add it according to the formula Water-based wetting agent,...

Embodiment 2

[0101] Water-based plastic paint consists of component A and component B. Wherein, the formulation weight parts of component A and component B are composed as follows:

[0102] Component A

[0103]

[0104] Component B

[0105] 6;

[0106] in, It is a water-based large particle size self-dulling polyurethane resin, and its main raw materials include hexamethylene diisocyanate, isophorone diisocyanate, polytetrahydrofuran ether diol, polycarbonate diol, N120, N-(2-aminoethyl base)-2-aminoethanesulfonate, N-(2-hydroxyethyl)ethylenediamine and isophoronediamine.

[0107] Among them, the main raw materials of the water-based acrylic resin 1 include styrene, methyl methacrylate, tetrahydrofuran acrylate, and tetrahydrofuryl acrylate. The preparation method is as follows:

[0108] Under the protection of nitrogen, mix 2 parts of sodium dodecylsulfonate, 2 parts of nonylphenyl polyoxyethyl ether, 0.5 parts of ammonium persulfate and 60 parts of water, stir to make it full...

Embodiment 3

[0112] Water-based plastic paint consists of component A and component B. Wherein, the formulation weight parts of component A and component B are composed as follows:

[0113] Component A

[0114]

[0115] Component B

[0116] 4;

[0117] Among them, the main raw materials of water-based large particle size polyurethane resin 1 include hexamethylene diisocyanate, isophorone diisocyanate, polytetrahydrofuran ether diol, polycarbonate diol, polycaprolactone diol, MPEG1200, diol Methylolpropionic acid, sodium N-(2-aminoethyl)-2-aminoethanesulfonate, N-(2-hydroxyethyl)ethylenediamine, and ethylenediamine. Add the dehydrated polyol, aliphatic diisocyanate, hydrophilic compound and acetone into a reaction vessel filled with nitrogen for contact, and stir the mixture at 80°C for reaction; until the NCO value in the system reaches 1.8wt%, The obtained prepolymer was dissolved in acetone and cooled, and the aqueous solution in which the chain extender was dissolved was broug...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of water-based plastic paints, and provides a water-based composite resin composition, a water-based plastic paint and a preparation method of the water-based plastic paint. The water-based composite resin composition is prepared by adopting the following components in percentages by weight: 70-90wt% of water-based large-particle-size polyurethane resinwith the particle size of 800-2000nm, 6-25wt% of water-based acrylic resin, and 2-8wt% of an auxiliary agent; and the water-based plastic paint is prepared by adopting the following raw materials inparts by weight: A, 100 parts of the above water-based composite resin composition, and B, 2-6 parts of a water-based isocyanate curing agent. According to the method provided by the invention, compounding of the water-based large-particle-size polyurethane resin and the water-based acrylic resin is adopted, so that the plastic paint has excellent adhesion, scratch resistance, abrasion resistance,chemical resistance and the like.

Description

technical field [0001] The invention belongs to the technical field of water-based plastic paint, and in particular relates to a water-based composite resin composition, water-based plastic paint and a preparation method thereof. Background technique [0002] Water-based environmentally friendly polyurethane paint does not contain organic solvents, is non-toxic, easy to use, and its physical and chemical properties can achieve the effect of solvent-based coatings. Therefore, water-based environmentally friendly polyurethane paints are increasingly used in textile coatings, leather finishing, and industrial coatings. Being valued is the trend of future industry development. [0003] In addition, products with matte surface materials are more and more popular. At present, in the formulation of matte materials, directly adding matting powder is still the most widely used method. However, organic or inorganic matting powders have a rough or slippery feel, poor compatibility wi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D175/08C09D133/12C09D125/14C09D5/08C08G18/66C08G18/48C08G18/44C08G18/42C08G18/34C08G18/32
CPCC08G18/348C08G18/3855C08G18/4018C08G18/4277C08G18/44C08G18/4804C08G18/4854C08G18/6625C09D5/08C09D175/08C08L33/12C08L25/14C08L33/14
Inventor 赵炳炎邓俊英张洁耿丹丹孙家宽
Owner WANHUA CHEMICAL (NINGBO) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap