Zeolite interior wall material, and processing method and application thereof

A processing method and zeolite technology are applied to the zeolite inner wall material and the processing field thereof, which can solve the problems such as easy generation of harmful substances, and achieve the effects of simple construction, good decorative performance and simple production.

Inactive Publication Date: 2018-08-03
欧亚绿邦(北京)科技有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because the raw materials of zeolite interior wall materials are healthy, environmentally friendly and have good decorative properties, they are a new generation of interior decoration materials that can replace diatom mud, wallpaper and latex paint, and a large number of artificially synthesized interior decoration materials are added to the market. Preparations, prone to harmful substances

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Embodiment 1 proposes a kind of zeolite interior wall material, comprises the raw material of following parts by weight: 20 parts of zeolite, 8 parts of attapulgite, 10 parts of diatomite, 20 parts of heavy calcium, 5 parts of talcum powder, 40 parts of quartz powder, 1 part of diatomite composite nano-silica, 0.5 part of cellulose, 3 parts of VAE, 0.2 part of sodium polyacrylic acid, 0.1 part of a mixture of polyethylene glycol and amorphous silica, 0.8 part of benzimidazole methyl carbamate and starch 0.05 parts of ether.

[0027] The processing method of the zeolite interior wall material of embodiment 1, comprises the steps:

[0028] (1) Put the raw materials except the quartz powder into the mixer according to the above parts by weight and stir for 15 minutes.

[0029] (2) The weight ratio of the product obtained in step (1) to water is 2:1 and water is weighed.

[0030] (3) The product obtained in the step (1) was mixed with 14 / 15 of the water and stirred for 3 ...

Embodiment 2

[0036] Embodiment 2 proposes a zeolite inner wall material, including the following raw materials in parts by weight: 40 parts of zeolite, 5 parts of attapulgite, 15 parts of diatomaceous earth, 10 parts of heavy calcium, 10 parts of talcum powder, 20 parts of quartz powder, 1.5 parts of diatomite composite nano-silica, 0.3 parts of cellulose, 5 parts of VAE, 0.1 part of sodium polyacrylic acid, 0.2 parts of a mixture of polyethylene glycol and amorphous silica, 0.5 parts of benzimidazole methyl carbamate and starch 0.1 parts of ether.

[0037] The processing method of the zeolite interior wall material of embodiment 2, comprises the steps:

[0038] (1) Put the raw materials except the quartz powder into the mixer according to the above parts by weight and stir for 20 minutes.

[0039] (2) The weight ratio of the product obtained in step (1) to water is 1:1 and water is weighed.

[0040] (3) The product obtained in the step (1) was mixed with 14 / 15 of the water and stirred f...

Embodiment 3

[0046] Embodiment 3 proposes a kind of zeolite interior wall material, comprises the raw material of following parts by weight: 30 parts of zeolite, 6 parts of attapulgite, 13 parts of diatomite, 15 parts of heavy calcium, 7 parts of talcum powder, 30 parts of quartz powder, 1.3 parts of diatomite composite nano-silica, 0.4 parts of cellulose, 4 parts of VAE, 0.15 parts of sodium polyacrylic acid, 0.15 parts of a mixture of polyethylene glycol and amorphous silica, 0.6 parts of benzimidazole methyl carbamate and starch 0.07 parts of ether.

[0047] The processing method of the zeolite inner wall material of embodiment 3 comprises the steps:

[0048] (1) Put the raw materials except the quartz powder into the mixer according to the above parts by weight and stir for 17 minutes.

[0049](2) The weight ratio of the product obtained in step (1) to water is 1.5:1 and water is weighed.

[0050] (3) The product obtained in the step (1) was mixed with 14 / 15 of the water and stirred ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a zeolite interior wall material and a preparation method thereof. The zeolite interior wall material comprises the following raw materials: zeolite, attapulgite, diatomite, heavy calcium carbonate, talcum powder, quartz powder, an aldehyde-removing molecular sieve, cellulose, dispersible adhesive powder, a dispersant, an antifoaming agent, a mildewproof agent and starch ether. The zeolite interior wall material provided by the invention adopts the zeolite as a main material, and the zeolite has a unique porous structure, so the zeolite interior wall material has ion-exchange properties, adsorption and separation properties, high catalytic activity, reversible dehydration properties, thermal stability and acid resistance. The zeolite interior wall material prepared by using the zeolite as the main material provided by the invention has the functions of pure nature, breathability, deodorization capability, strong purification capability, fire prevention, flame retardancy, etc. In addition, the zeolite interior wall material provided by the invention has the advantages of simple production, convenience in storage, simple and easy construction and good decorative performance.

Description

technical field [0001] The invention relates to a zeolite inner wall material and its processing method and application. Background technique [0002] At present, the rapid development of my country's real estate industry has brought vigorous development to the building decoration industry. The indoor air pollution caused by decoration materials directly brings health hazards to the occupants, especially children, the elderly, pregnant women and occupational contacts. [0003] In my country, the annual loss caused by indoor air pollution is about tens of billions of dollars. Health problems caused by indoor pollution have become prominent public health problems. With continuous improvement, the pursuit of a more elegant and comfortable home environment has become the mainstream of modern life. As a result, decoration projects in the home improvement market, especially interior decoration, continue to heat up, and the environmental pollution in the decoration process and the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/28C04B38/08C04B14/04E04F13/14
CPCC04B14/047C04B26/285C04B38/08C04B2111/00017C04B2111/00025C04B2111/00482E04F13/14C04B14/102C04B14/08C04B14/28C04B14/042C04B14/06C04B20/0008C04B24/2641C04B24/32C04B24/123C04B24/38
Inventor 赵广全
Owner 欧亚绿邦(北京)科技有限公司