Preparation method for differentiated EG

A differentiated and fossilized technology, applied in the direction of single-component polyester rayon, can solve the problems of single and invariable EG varieties, achieve improved dispersion and compatibility, durable anti-aging effects, and ensure deep integration and The effect of stability

Inactive Publication Date: 2018-08-28
ZHEJIANG MODERN TEXTILE IND RES INST
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the EG variety has always been single and almost unchanged

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] A preparation method of differential EG, comprising the steps of:

[0046] (1) the concentration of 75 parts by weight is the oxalic acid solution of 10wt%, the concentration of 18 parts is the hypochlorous acid solution of 3wt% and the bismuth vanadate of 7 parts, the graphene oxide of 7 parts, the zinc oxide of 1.5 parts , 1.5 parts of rutile-type titanium oxide, and 0.9 parts of hydrotalcite are mixed, moved to a hydrothermal reactor, and continuously stirred and reacted for 4 hours at a temperature of 135 ° C and a pressure of 0.15 MPa, then cooled naturally under stirring, and used at 47 ° C Grind in a high-energy ball mill with liquid for 2.5 hours, filter, then calcinate at 510°C for 3.5 hours, fully wash with deionized water, dry in a vacuum at 90°C, grind for 2.5 hours with a ball mill, and pass through a 250-mesh sieve to obtain EG special anti-aging agent;

[0047] (2) Add 10% propylene glycol, 2.5% glycerin, 0.65% lactic acid and 7% EG special anti-aging ag...

Embodiment 2

[0051] A preparation method of differential EG, comprising the steps of:

[0052] (1) the concentration of 73.2 parts by weight is the oxalic acid solution of 15wt%, the concentration of 12 parts is the hypochlorous acid solution of 5wt%, and the bismuth vanadate of 6 parts, the graphene oxide of 6 parts, the zinc oxide of 1 part , 1 part of rutile titanium oxide and 0.8 parts of hydrotalcite are mixed, moved to a hydrothermal reactor, continuously stirred and reacted for 5 hours at a temperature of 150°C and a pressure of 0.1MPa, and then cooled naturally under stirring, and used at 55°C Grind with liquid in a high-energy ball mill for 2 hours, filter, and then calcined at 520°C for 3 hours, fully washed with deionized water, vacuum-dried at 95°C, and then ground for 2 hours with a ball mill, and sieved through a 300-mesh EG special anti-aging agent;

[0053] (2) Under continuous stirring, add 8% propylene glycol, 2% glycerin, 0.8% lactic acid and 10% EG special anti-aging ag...

Embodiment 3

[0058] A preparation method of differential EG, comprising the steps of:

[0059] (1) the concentration of 60 parts by weight is the oxalic acid solution of 5wt%, the concentration of 20 parts is the hypochlorous acid solution of 2wt%, and the bismuth vanadate of 5 parts, the graphene oxide of 8 parts, the zinc oxide of 3 parts , 3 parts of rutile titanium oxide and 1 part of hydrotalcite are mixed, moved to a hydrothermal reactor, and continuously stirred and reacted for 3 hours at a temperature of 120°C and a pressure of 0.2MPa, then cooled naturally under stirring, and used at 40°C Grind with liquid in a high-energy ball mill for 3 hours, filter, and then calcined at 500°C for 4 hours, fully washed with deionized water, vacuum-dried at 80°C, and then ground for 3 hours with a ball mill, and sieved through a 200-mesh EG special anti-aging agent;

[0060] (2) Under continuous stirring, 12% propylene glycol, 3% glycerin, 0.5% lactic acid and 4% EG special anti-aging agent prep...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

Provided is a preparation method for differentiated EG. The method comprises the following steps that oxalic acid solution, hypochloric acid solution, pucherite, graphene oxide, zinc oxide, titanium dioxide top grade and hydrotalcite are mixed to be grinded after hydrothermal reaction is carried out, and filtration, calcination, washing and drying are carried out to prepare a special age resisterfor EG; ethylene glycol, propylene glycol, glycerinum, lactic acid, the obtained special age resister for EG, silicon dioxide, mica powder and potassium hydrogen phosphate dispersion liquid are mixedand grinded, then dispersion and filtration are carried out to prepare differentiated EG mother liquor with a function of ageing resistance; the obtained differentiated EG mother liquor is sprayed into the EG to prepare the differentiated EG fused deeply with the function of ageing resistance. The preparation method for the differentiated EG has the advantage that the differentiated EG prepared bythe above method has the good function of ageing resistance.

Description

technical field [0001] The invention belongs to the technical field of EG variety development, and in particular relates to a preparation method of differentiated EG. Background technique [0002] The Chinese name of EG is ethylene glycol, and the English name is ethylene glycol, referred to as EG. Its chemical formula is (CH2OH) 2 , is the simplest diol. As a basic chemical raw material, EG is active in nature and can undergo reactions such as esterification, etherification, alcoholization, oxidation, acetalization, and dehydration. EG molecules have two hydroxyl functional groups, so they are mainly used to prepare synthetic materials such as polymers, such as engineering plastics, building materials, mechanical parts, beverage bottles, packaging films, films, clothing, films and other products, and there are more and more More and more products are used in the outdoor environment, and they are constantly eroded by factors such as wind and rain, sunlight and ultraviolet...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G63/60C08G63/20C08G63/183C08K3/04C08K3/22C08K3/26C08K3/36C08K3/32D01F6/92D01F1/10
CPCC08G63/183C08G63/20C08G63/60C08K3/04C08K3/22C08K3/26C08K3/32C08K3/36C08K2003/2241C08K2003/2296C08K2003/324D01F1/10D01F6/92
Inventor 范艳苹凌荣根李琪陶仁中张芳胡超
Owner ZHEJIANG MODERN TEXTILE IND RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products